Preparation method of ag@agcl/tio2-graphene oxide composite material

A composite material, graphene technology, applied in chemical instruments and methods, special compound water treatment, physical/chemical process catalysts, etc., can solve problems such as low photocatalytic quantum efficiency, achieve good adsorption of pollutants, large specific surface area, The effect of broadening the spectral absorption range

Active Publication Date: 2019-05-17
WUHAN UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to TiO 2 Has a large band gap (3.0-3.2eV), pure TiO 2 The photocatalytic quantum efficiency of the photocatalyst is low, and the effective photocatalytic reaction can only occur under the drive of ultraviolet light.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ag@agcl/tio2-graphene oxide composite material
  • Preparation method of ag@agcl/tio2-graphene oxide composite material
  • Preparation method of ag@agcl/tio2-graphene oxide composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) First, 0.068g AgNO 3 and 0.5g PDDA were dissolved in 20ml deionized water, and then AgNO 3 Add the solution dropwise to the PDDA solution, and stir for 15 minutes to obtain the Ag+ dispersion;

[0034] (2) Dissolve 0.0234g NaCl and 0.1g glucose in 20mL and 60mL deionized water respectively to prepare a solution, and add the prepared NaCl solution and glucose solution dropwise to the above Ag + In the dispersion liquid, after stirring for one hour, the mixed solution was transferred to a reaction kettle, heated to 180°C and kept for hydrothermal reaction for 24 hours, and centrifuged after the reaction was completed. The centrifuged product was washed three times with ethanol and deionized water respectively, and the washed product was dissolved in deionized water to obtain Ag@AgCl sol. When preparing the Ag@AgCl sol, the product was dissolved in 20ml of deionized water per 120ml of the reaction solution. From figure 1 -a and figure 1In -b, it can be seen that t...

Embodiment 2

[0042] The other steps and parameters of Examples 2-4 are the same as in Example 1, except that the dosage of Ag@AgCl sol in step (4) is 60mL (Example 2), 80mL (Example 3) and 100ml (Example 3) respectively. Example 4).

Embodiment 5

[0046] Other parameter steps of embodiment 5-7 are identical with embodiment 3, difference is: in step (5) TiO 2 The powders were used in amounts of 0.2 g (Example 5), 0.6 g (Example 6) and 1 g (Example 7), respectively.

[0047] Compared Figure 4 and Figure 5 , when TiO 2 When the dosage is 0.2g, graphite oxide almost replaces TiO 2 The coating of nanotubes greatly affects its absorption of light; and when TiO 2 When the dosage is 1g, TiO 2 Excess, some TiO 2 Not formed into tubes and not composited with graphite oxide.

[0048] Then compare its photocatalytic performance, when TiO 2 When the dosage is 0.4g, the photocatalytic performance is the best. Within 20 minutes, the photocatalytic efficiency reaches over 80%, and the methylene blue is basically degraded in about 40 minutes. When TiO 2 When the dosage was 0.6g, the photocatalytic performance decreased. And when TiO 2 When the dosage is 0.2g and 1g, the photocatalytic performance drops sharply. The former i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
catalytic efficiencyaaaaaaaaaa
catalytic efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of inorganic functional materials, and specifically discloses an Ag@AgCl / TiO 2 -Preparation method of graphene oxide composite materials. In this method, after mixing Ag@AgCl nanoparticles with GO, they are directly mixed with TiO 2 Hydrothermal reaction under alkaline conditions yields Ag@AgCl / TiO 2 -Graphene oxide composites. Compared with ordinary photocatalytic materials, Ag@AgCl / TiO 2 -Graphene oxide composite materials can undergo effective photocatalytic reactions in both the visible and ultraviolet light regions, making full use of the light source; the composite material has a large specific surface area and strong adsorption capacity, which can better absorb pollutants; The presence of reduced graphene oxide can effectively inhibit the recombination of photogenerated electron pairs, thereby greatly improving the photocatalytic performance. Ag@AgCl / TiO 2 -The raw materials used in graphene oxide composite materials are cheap and easy to obtain, and the preparation and composite processes are simple and easy. It is a promising photocatalytic material.

Description

technical field [0001] The invention belongs to the technical field of inorganic functional materials, in particular to an Ag@AgCl / TiO 2 -Preparation method of graphene oxide composite material. Background technique [0002] Nano-TiO 2 With the advantages of stable chemical properties, light corrosion resistance and strong photocatalytic oxidation ability, it is widely used in photocatalytic degradation of various pollutants. Titanium dioxide nanotubes (TiO 2 NTs) is TiO 2 One of the existing forms, has the advantage of high specific surface area, and other forms of TiO 2 Compared to TiO 2 Nanotubes exhibit higher photocatalytic ability. However, due to TiO 2 Has a large band gap (3.0-3.2eV), pure TiO 2 The photocatalytic quantum efficiency of the photocatalyst is low, and the effective photocatalytic reaction can only occur under the driving of ultraviolet light. Based on this, many scholars modified TiO 2 or compound it with metals or photocatalytic materials in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/135B01J20/20C02F1/28C02F1/30C02F1/32
CPCB01J20/0233B01J20/0288B01J20/06B01J20/20C02F1/288C02F1/30C02F1/32B01J27/135C02F2305/10B01J35/39
Inventor 涂文懋潘红飞
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com