A kind of silicone button and preparation method thereof
A silicone and button technology, applied to buttons, fasteners, clothing, etc., can solve the problems of time-consuming and labor-intensive processing, obvious yellowing, color migration, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0057] The present invention also provides a method for preparing a silicone button, comprising the following steps:
[0058] A) After mixing solid silica gel, vulcanizing agent, antistatic agent and color masterbatch, obtain the mixture of solid silica gel;
[0059] B) After the mixture obtained in the above steps is vulcanized and molded in a mold, a silicone button is obtained.
[0060] In the above-mentioned preparation method of the present invention, the optimal principle and the added amount of the raw materials used are the same as those in the aforementioned silicone button, and will not be repeated here.
[0061] In the present invention, firstly, the solid silica gel, vulcanizing agent, antistatic agent and color masterbatch are mixed to obtain a mixture of solid silica gel.
[0062] The present invention has no special restrictions on the model and parameters of the color masterbatch, the model and parameters of the color masterbatch used for silica gel well known...
Embodiment 1
[0094] Weigh 1kg of solid silica gel with a hardness of 70 degrees, mix evenly, add 30g of solid silica gel vulcanizing agent and mix evenly, add 10g of antistatic agent, and then add a certain quality of solid silica gel color masterbatch, mix evenly, and pack it for later use.
[0095] Put the mixed solid silica gel into the mold, put it into the air pressure mold for pre-pressing, and then put it into the hot-press vulcanizing machine, the hot-press vulcanization temperature is 220°C, the hot-press vulcanization time is 1 minute, and the hot-press vulcanization pressure is 120Mpa. After the time, you can take out the product and get the silicone button.
[0096] The appearance inspection was carried out on the silicone buttons prepared in Example 1 of the present invention.
[0097] see figure 1 , figure 1 Appearance photo of the silicone button prepared in Example 1 of the present invention.
[0098] The silicone button prepared in Example 1 of the present invention was...
Embodiment 2
[0110] Weigh 1 kg of solid silica gel with a hardness of 75 degrees, and after mixing evenly, add 30 g of solid silica gel vulcanizing agent and 20 g of antistatic agent and mix evenly, then add a certain quality of solid silica gel masterbatch, mix evenly, and pack it for later use.
[0111] Weigh 1kg of liquid silica gel, add a certain mass of diluent and liquid color paste and mix evenly, add 10g of liquid silica gel vulcanizing agent, stir evenly, and store for later use.
[0112] Add the liquid silicone into the mold with a dispenser, and then put the mold on a heating plate at 200°C for baking. When the liquid silicone is semi-cured, take it off, put the mixed solid silicone into the mold, and put it into the mold. The air pressure mold is pre-pressed, and then placed in a hot-press vulcanizer. The hot-press vulcanization temperature is 220°C, the hot-press vulcanization time is 60 seconds, and the hot-press vulcanization pressure is 80Mpa. After the predetermined time is...
PUM
| Property | Measurement | Unit |
|---|---|---|
| hardness | aaaaa | aaaaa |