Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of chitin fiber and cupro fiber, which is applied in the directions of yarn, textile and paper making, can solve the problems of insufficient performance and insufficient distribution of fibers.
Inactive Publication Date: 2017-09-26
NANTONG DOUBLE GREAT TEXTILE
View PDF6 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The performance of the existing blended yarn products is not good enough, the fiber distribution is not uniform enough, and it cannot meet people's needs
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0014] The chitin fiber / cupro ammonia fiber / PET antibacterial blended yarn of the present embodiment is made by the following process:
[0015] 1) Take 25 parts by weight of chitin fiber, 25 parts by weight of cupro ammonia fiber, and 55 parts by weight of PET fiber. The PET fiber is an antibacterial PET fiber modified by zeolite. After mixing the above fibers, go through a cotton blender. blended cotton;
[0016] 2) After being processed by an opener, a carding machine, a drawing frame, a roving frame, a spinning frame and a winder in sequence, the chitin fiber / cupro fiber / PET antibacterial blended yarn is obtained.
Embodiment 2
[0018] The chitin fiber / cupro ammonia fiber / PET antibacterial blended yarn of the present embodiment is made by the following process:
[0019] 1) Take 35 parts by weight of chitin fiber, 15 parts by weight of cupro ammonia fiber, and 65 parts by weight of PET fiber. The PET fiber is an antibacterial PET fiber modified by zeolite. blended cotton;
[0020] 2) After being processed by an opener, a carding machine, a drawing frame, a roving frame, a spinning frame and a winder in sequence, the chitin fiber / cupro fiber / PET antibacterial blended yarn is obtained.
Embodiment 3
[0022] The chitin fiber / cupro ammonia fiber / PET antibacterial blended yarn of the present embodiment is made by the following process:
[0023] 1) Take 30 parts by weight of chitin fiber, 20 parts by weight of cupro ammonia fiber, and 60 parts by weight of PET fiber. The PET fiber is an antibacterial PET fiber modified by zeolite. After mixing the above fibers, go through a cotton blender. blended cotton;
[0024] 2) After being processed by an opener, a carding machine, a drawing frame, a roving frame, a spinning frame and a winder in sequence, the chitin fiber / cupro fiber / PET antibacterial blended yarn is obtained.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention provides a chitinfiber / copperammoniafiber / PET antibacterial blended yarn which is made by using the following processes: 1) mixing 25-35 parts by weight of chitinfiber, 15-25 parts by weight of copperammonia fiber and 55-65 parts by weight of PET fiber, and performing cotton mixing by using a cotton mixing machine, wherein the PET fiber is antibacterial PET fiber modified with zeolite; 2) treating by using a cotton opener, a cardingmachine, a drawing frame, a crude yarnmachine, a fine yarn machine and a winding machine in sequence, so as to obtain the chitin fiber / copperammonia fiber / PET antibacterial blended yarn. The chitin fiber / copper ammonia fiber / PET antibacterial blended yarn provided by the invention has the technical effect of antibacterial properties.
Description
technical field [0001] The invention relates to a chitin fiber / cupro ammonia fiber / PET antibacterial blended yarn, which belongs to the technical field of functional chemical fibers. Background technique [0002] Blended yarn refers to the yarn that is mixed and spun by two or more different fibers in a certain proportion, such as polyester-cotton blended yarn, polyester-viscose blended yarn, etc. There are also a variety of fibers that are distributed and adjusted in different proportions to become blended yarns. Blended yarn can be composed of different fibers with excellent appearance and hand feeling, and the choice of fiber raw materials, blending ratio and combination method can be changed according to the application. Therefore, blended yarns can be used in knitted and woven garments, decorative fabrics, as well as industrial materials and sewing threads. [0003] Chitin and its derivative chitosan have certain ductility and filamentation properties, and are good fi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).