Preparation process of electronic ceramic flow-casting sizing agent
A technology of casting slurry and electronic ceramics, which is applied in the field of electronic ceramics production, can solve the problems of poor powder dispersion, poor mechanical properties, and poor mixing uniformity of ball milling, so as to achieve good mixing uniformity of ball milling, improve smoothness and Elasticity, the effect of improving the plasticizing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] An electronic ceramic casting slurry configuration process, comprising the following process steps:
[0024] a. Weigh powder, main solvent, dispersant, binder and plasticizer according to the designed ratio;
[0025] The powder material includes alumina, kaolin, talc, calcium carbonate and yttrium oxide, and the weight percentage of alumina in the casting slurry is 60%. The weight percentage in the casting slurry is 25%, and the described binder is polyvinyl butyral, and the weight percentage in the casting slurry is 5%, and the dispersant is nonyl Base phenol polyoxyethylene ether, its weight percentage in the casting slurry is 1%, and the plasticizer is dibutyl phthalate, and its weight percentage in the casting slurry is It is 3%, and the balance is the mixture of kaolin, talc, calcium carbonate and yttrium oxide in the powder.
[0026] b. Add the weighed powder to the ball mill, then add the dispersant to the ball mill, then add half of the main solvent to the bal...
Embodiment 2
[0030] An electronic ceramic casting slurry configuration process, comprising the following process steps:
[0031] a. Weigh powder, main solvent, dispersant, binder and plasticizer according to the designed ratio;
[0032] The powder material includes alumina, kaolin, talc, calcium carbonate and lanthanum oxide, the weight percentage of alumina in the casting slurry is 75%, and the main solvent is absolute ethanol, which is The weight percentage in the casting slurry is 15%, and the described binder is polyvinyl butyral, and the weight percentage in the casting slurry is 2%, and the dispersant is nonyl Base phenol polyoxyethylene ether, its weight percentage in the casting slurry is 1%, and the plasticizer is dibutyl phthalate, and its weight percentage in the casting slurry is It is 4%, and the balance is the mixture of kaolin, talc, calcium carbonate and lanthanum oxide in the powder.
[0033] b. Add the weighed powder to the ball mill, then add the dispersant to the ball...
Embodiment 3
[0037] An electronic ceramic casting slurry configuration process, comprising the following process steps:
[0038] a. Weigh powder, main solvent, dispersant, binder and plasticizer according to the designed ratio;
[0039] The powder material includes alumina, kaolin, talc, chromium oxide, molybdenum oxide, calcium carbonate and yttrium oxide, and the weight percentage of alumina in the casting slurry is 65%. It is absolute ethanol, and its weight percentage in the casting slurry is 20%, and the binder is polyvinyl butyral, and its weight percentage in the casting slurry is 4% , the dispersant is nonylphenol polyoxyethylene ether, and its weight percentage in the casting slurry is 0.5%, and the plasticizer is dibutyl phthalate, which is used in the casting slurry. The weight percentage of the slurry is 2%, and the balance is a mixture of kaolin, talc, chromium trioxide, molybdenum oxide, calcium carbonate and yttrium oxide in the powder.
[0040] b. Add the weighed powder t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction