A kind of lithium-ion battery cathode precursor material with low lattice stress and preparation method thereof

A lithium-ion battery, lattice stress technology, applied in battery electrodes, secondary batteries, circuits, etc., can solve the problem of high lattice stress of ternary cathode materials, affecting the cycle stability and rate performance of electrode materials, and generating lattice stress. and other problems, to achieve the effect of low material cost, low stress, and reduced lattice stress

Active Publication Date: 2019-12-10
HARBIN INST OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the problem of lattice stress caused by the change of transition metal element ratio in the ternary gradient precursor material currently used to prepare lithium-ion battery positive electrode materials, so that the lattice stress of the prepared ternary positive electrode material is higher, and then Problems that affect the cycle stability and rate performance of electrode materials, and provide a lithium-ion battery cathode precursor material with low lattice stress and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lithium-ion battery cathode precursor material with low lattice stress and preparation method thereof
  • A kind of lithium-ion battery cathode precursor material with low lattice stress and preparation method thereof
  • A kind of lithium-ion battery cathode precursor material with low lattice stress and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0034] Specific embodiment one: the chemical formula of a kind of lithium-ion battery anode precursor material with low lattice stress of this embodiment is Ni x co y mn z m 1-x-y-z (OH) 2-n f n or Ni x co y mn z m 1-x-y-z (CO 3 ) 1-0.5n f n ; Wherein the Ni content x decreases from the inside to the outside, and the F content n increases from the inside to the outside, 0

specific Embodiment approach 2

[0035] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is that the change gradient of the content x of Ni and the change gradient of the content n of F satisfy 5≤Δ x / Δ n ≤7; where Δ x is the difference of Ni content x at different distances from the center of the sphere, Δ n is the difference of the content n of F at the position corresponding to the content x of Ni. Other steps and parameters are the same as those in the first embodiment.

specific Embodiment approach 3

[0036] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is: said M is Li, Zr, Fe, Sm, Pr, Nb, Ga, Zn, Y, Mg, Al, Cr, Ca, Na , Ti, Cu, K, Sr, Mo, Ba, Ce, Sn, Sb, La and Bi or a mixture of several. Other steps and parameters are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a lithium ion battery positive electrode precursor material with low crystal lattice stress and a preparation method thereof. The invention belongs to the field of lithium ion batteries and in particular relates to a lithium ion battery positive electrode precursor material with low crystal lattice stress and the preparation method thereof. The invention aims to solve the problems that the prepared ternary cathode material is high in crystal lattice stress and further the cycling stability and rate capability of the electrode material are influenced because the crystal lattice stress is produced by the change of a ratio of transition metal elements in a conventional ternary gradient precursor material used for preparing the lithium ion battery positive electrode material. The method comprises the following steps: 1, preparing an aqueous solution of a mixed metal salt; 2, preparing an aqueous solution of a precipitator; 3, preparing an aqueous solution of a complexing agent; 4, preparing an aqueous solution of fluorides; 5, preparing a precursor material; and 6, cooling. According to the precursor material and the preparation method thereof disclosed by the invention, the content of Ni and F in the lithium ion battery positive electrode precursor material has a reverse gradient change, the crystal lattice stress is effectively decreased, and the cycling stability and the rate capability are improved.

Description

technical field [0001] The invention belongs to the field of lithium ion batteries, and in particular relates to a lithium ion battery cathode precursor material with low lattice stress and a preparation method thereof. Background technique [0002] Since the commercialization of lithium-ion batteries in the 1990s, they have rapidly become the most important and widely used secondary batteries. After years of development, today's lithium-ion batteries have been widely used in various small portable electronic products and power tools, and as countries around the world pay more attention to energy in recent years, they are gradually being widely used in the new energy vehicle market. Cathode material is one of the key materials for manufacturing lithium-ion batteries. Since the specific capacity of general positive electrode materials is significantly lower than that of negative electrode materials, the performance of positive electrode materials directly affects the indicato...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/505H01M4/525H01M10/0525
CPCH01M4/505H01M4/525H01M10/0525Y02E60/10
Inventor 杜春雨徐晟徐星尹鸽平左朋建程新群马玉林
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com