Water feeding pipe and preparation method thereof

A water supply pipe, linear low-density technology, applied in the field of water supply pipes and their preparation, can solve the problems of insufficient mechanical strength, flame retardancy, toughness and aging resistance, and achieve good insulation, corrosion resistance, anti-corrosion, and anti-aging properties. good corrosive effect

Inactive Publication Date: 2017-10-24
HEFEI ANLI ELECTRIC POWER ENG CO LTD
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the existing problems of insufficient mechanical strength, flame retardancy, toughness and aging resistance of existing water supply pipes, the purpose of the present invention is to provide a water supply pipe and its preparation method, and the obtained water supply pipe has mechanical strength High, good flame retardancy, good toughness and good aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water feeding pipe and preparation method thereof
  • Water feeding pipe and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A water supply pipe, comprising the following raw materials in parts by weight: 95 parts of metallocene linear low density polyethylene, 2.5 parts of chromium carbonate, 4.5 parts of fumed white carbon black, 2.5 parts of nano-active calcium carbonate, metallocene linear low density polyethylene wax 1.5 parts, 1.5 parts of phthalates, 0.3 parts of γ-aminopropyl triethoxysilane, 0.2 parts of rose essential oil, 0.4 parts of dibutyltin dilaurate, 2.5 parts of modification additives, hydroxy distearate 1.5 parts of aluminum, 30 parts of hollow glass microspheres, 9 parts of aluminum hydroxide, 3 parts of nano-zirconium carbide, 2 parts of aluminum silicate, 3 parts of glass fiber, 0.3 parts of heat stabilizer, 0.2 parts of light stabilizer, and 0.4 parts of antioxidant part, 0.6 part of compatibilizer and 0.5 part of plasticizer;

[0041] The modification aid is composed of the following raw materials in parts by weight: 35 parts of metallocene linear low-density polyethylen...

Embodiment 2

[0058] A water supply pipe, comprising the following raw materials in parts by weight: 90 parts of metallocene linear low-density polyethylene, 2 parts of chromium carbonate, 4 parts of fumed white carbon black, 2 parts of nano-active calcium carbonate, metallocene linear low-density polyethylene wax 1 part, 1 part of phthalate, 0.2 part of γ-aminopropyltriethoxysilane, 0.1 part of rose essential oil, 0.3 part of dibutyltin dilaurate, 2 parts of modifying additives, hydroxy distearate 1 part of aluminum, 20 parts of hollow glass microspheres, 6 parts of aluminum hydroxide, 2 parts of nano-zirconium carbide, 1 part of aluminum silicate, 1 part of glass fiber, 0.2 parts of heat stabilizer, 0.1 part of light stabilizer, 0.2 parts of antioxidant part, 0.3 part of compatibilizer and 0.2 part of plasticizer;

[0059] The modification aid is composed of the following raw materials in parts by weight: 30 parts of metallocene linear low density polyethylene, 15 parts of polyphthalamide...

Embodiment 3

[0076] A water supply pipe, comprising the following raw materials in parts by weight: 100 parts of metallocene linear low density polyethylene, 3 parts of chromium carbonate, 5 parts of fumed white carbon black, 3 parts of nano-active calcium carbonate, metallocene linear low density polyethylene wax 2 parts, 2 parts of phthalates, 0.4 parts of γ-aminopropyltriethoxysilane, 0.3 parts of rose essential oil, 0.5 parts of dibutyltin dilaurate, 3 parts of modifying additives, hydroxy distearate 2 parts of aluminum, 40 parts of hollow glass microspheres, 12 parts of aluminum hydroxide, 4 parts of nano-zirconium carbide, 3 parts of aluminum silicate, 5 parts of glass fiber, 0.4 parts of heat stabilizer, 0.3 parts of light stabilizer, and 0.6 parts of antioxidant part, 0.9 part of compatibilizer and 0.8 part of plasticizer;

[0077] The modification aid is composed of the following raw materials in parts by weight: 40 parts of metallocene linear low-density polyethylene, 20 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a water feeding pipe and a preparation method thereof and relates to the technical field of plastic pipes. The water feeding pipe comprises, by weight, metallocene linear low density polyethylene, chromium carbonate, fumed silica, nano-active calcium carbonate, metallocene linear low density polyethylene wax, phthalate, gamma-aminopropyltriethoxysilane, rose essential oil, dibutyltin dilaurate, a modifying aid, aluminum hydroxy distearate, hollow glass microbeads, aluminum hydroxide, nano zirconium carbide, aluminum silicate, glass fibers, a thermal stabilizer, a photo-stabilizer, an antioxidant, a compatilizer, and a plasticizer. The preparation method includes the steps of: 1) weighing raw materials; 2) performing granulation; 3) performing mixing, kneading, cooling, extrusion and shaping. The water feeding pipe has high mechanical strength, good flame retarding property, good toughness and good anti-aging performance.

Description

technical field [0001] The invention belongs to the technical field of plastic pipes, and in particular relates to a water supply pipe and a preparation method thereof. Background technique [0002] PE material is widely used in the field of water supply pipe manufacturing due to its high strength, high temperature resistance, corrosion resistance, and non-toxicity. Because it will not rust, it is an ideal pipe to replace ordinary iron water supply pipes. With the gradual expansion of urban construction, water supply pipes will also be used in harsher environments, such as continuous high and low temperature, acid and alkali and other chemical corrosion, and continuous high pressure. In addition, the existing water supply pipes have poor flame retardancy, which seriously affects the safe use of the water supply system. [0003] Therefore, it is necessary to further improve the mechanical strength, flame retardancy, toughness and aging resistance of the water supply pipe to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L77/06C08L33/08C08K13/04C08K7/28C08K3/22C08K3/14C08K3/34C08K7/14C08K5/098C08K7/08C08K3/38C08K5/134C08K5/18C08K5/524C08K5/3435C08K5/526
CPCC08L23/08C08K2003/2227C08K2003/387C08K2201/011C08K2201/014C08L2201/02C08L2201/08C08L2203/18C08L2205/025C08L2205/035C08L77/06C08L33/08C08L51/00C08K13/04C08K7/28C08K3/22C08K3/14C08K3/34C08K7/14C08K5/098C08K7/08C08K3/38C08K5/1345C08K5/18C08K5/524C08K5/3435C08K5/526
Inventor 殷世尧
Owner HEFEI ANLI ELECTRIC POWER ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap