A kind of crystal material, its preparation method and application

A crystal material and crystal technology, applied in the field of inorganic crystal materials, can solve the problems of high repetition frequency, complex structure, large beam divergence angle, etc., and achieve the effect of high power output

Active Publication Date: 2019-10-29
FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantage of this method is that the wavelength is adjustable and the repetition frequency is high, but the structure is complex and the beam divergence angle is large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of crystal material, its preparation method and application
  • A kind of crystal material, its preparation method and application
  • A kind of crystal material, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Example 1Er 6 B 4 o 15 Preparation of small single crystal samples

[0051] Er 2 o 3 and H 3 BO 3 And prepare raw materials according to the following chemical reaction formula:

[0052] 3Er 2 o 3 +4H 3 BO 3 →Er 6 B 4 o 15 +6H 2 O↑

[0053] 99.99% pure Er 2 o 3 with analytically pure H 3 BO 3 Mix evenly, put it into a corundum crucible, put it into a muffle furnace, raise it to the high-temperature solid-phase sintering temperature at a heating rate of 150°C / h, keep it at this temperature for a period of time, and then lower it to room temperature at a certain cooling rate to obtain rod-shaped single crystal sample.

[0054] Table 1 shows the relationship between the number of the obtained samples and the high-temperature solid-state sintering temperature, sintering time, and cooling rate.

[0055] Table 1

[0056] Sample serial number High temperature solid phase sintering temperature High temperature solid state sintering time coo...

Embodiment 2

[0057] Example 2Er 6 B 4 o 15 Preparation of Large Size Single Crystal Samples

[0058] The flux system used was Li 2 O-ZnF 2 -B 2 o 3 , the molar ratio of the three is 1:3:5. Er 2 o 3 and H 3 BO 3 And prepare raw materials according to the following chemical reaction formula:

[0059] 3Er 2 o 3 +4H 3 BO 3 →Er 6 B 4 o 15 +6H 2 O↑

[0060] Flux system and Er 6 B 4 o 15 The mass ratio of the melt is a certain value between 2.9:7 and 3.1:7.

[0061] Weigh Er according to the above ratio 2 o 3 、H 3 BO 3 , Li 2 O and ZnF 2 , after mixing evenly, put it into a Ф60mm×60mm platinum crucible, put it into a self-made crystal growth furnace, slowly raise the temperature to 1050°C at a speed of 150°C / h, keep it for 1h, and then raise the temperature at the same speed until the raw materials are melted, and keep the temperature constant After half an hour, the raw material is completely melted, and then the platinum wire twisted at the bottom is used as the se...

Embodiment 3

[0065] The crystal structure characterization of embodiment 3 sample

[0066] Take sample S1-1 # Medium size is 0.6×0.45×0.1mm 3 Rod-shaped small single crystal, X-ray single crystal diffraction analysis.

[0067] The results showed that Er 6 B 4 o 15 The crystal belongs to the monoclinic system, space group P2 1 / n(No.14), unit cell parameters β=9 1.899(4)°, Z=4, the density is 7.429g cm -3 . Er 6 B 4 o 15 The crystal structure is as figure 1 Shown by ErO 6 Polyhedra and BO 3 group composition, each ErO 6 with the other two ErO 6 and two BOs 3 The units are connected to form a sandwich layer structure, and the layers are filled with BO formed by B atoms and three O atoms. 3 Triangular group, B-O bond length is The O-B-O bond angle is 120.000(1)°.

[0068] Sample S1-1 was analyzed by powder X-ray diffraction method # ~S1-3 # , S2 # ~S5 # structure was determined. Sample S1-1 # The theoretical XRD diffraction pattern obtained from the crystal structur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The application discloses a crystal material, a preparation method and an application thereof. The chemical formula of the crystal material is Er6B4O15 and the crystal material is a monoclinic system and has P21 / n space groups. The cell parameters are as shown in a formula, wherein beta is equal to 91.8-91.9 degrees and Z is equal to 4. The crystal material can be used for outputting near-infrared laser, the wave length of which is 1560nm, under a 980nm pump.

Description

technical field [0001] This application relates to a 1.56 μm human eye-safe near-infrared laser crystal, its preparation method and application, and belongs to the field of inorganic crystal materials Background technique [0002] The ~1.56μm near-infrared band laser has received great attention due to its unique advantages. These characteristics are: (1) Located in a good atmospheric transmission window, it has strong penetration ability to smoke and fog, especially in the smoky battlefield (2) Located in the detection sensitive area of ​​detectors such as Ge and InGaAs working at room temperature, signal detection can be realized without low temperature control; (3) Located in the wavelength band that is safe for human eyes, the allowable exposure to human eyes The amount is 400,000 times that of the 1.06μm Nd:YAG laser, which is 10.6μm CO 2 100 times that of the laser; (4) The light attenuation rate is the lowest when it is transmitted in the silica fiber, only 0.2 decib...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B29/10C30B9/12C30B1/10H01S3/16
CPCC30B1/10C30B9/12C30B29/10H01S3/1666
Inventor 王燕李坚富朱昭捷游振宇涂朝阳
Owner FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com