A steel casting and orange peel technology is applied in the casting field to prevent orange peel defects on the surface of large steel castings. It can solve the problems of increasing production costs and restricting production efficiency, so as to reduce workload, improve post-order cleaning efficiency, The effect of improving surface quality

Active Publication Date: 2017-12-22
KOCEL STEEL
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this mode of operation seriously restricts the production efficiency of the subsequent order and increases the production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The embodiment of the present invention provides a casting method for preventing orange peel defects on the surface of large steel castings, comprising the following steps:

[0015] Modeling: Put the steel casting mold into the sand box, run the sand, and release the mold after the sand mold is compacted to form the steel casting sand mold;

[0016] Spray coating: use a spraying machine to spray paint on the surface of the cavity of the steel casting sand mold. The spray coating includes spraying the first coating layer and spraying the second coating layer. The coating used for the first coating layer is corundum powder coating The coating used for the second coating layer is zircon powder coating. The method of spraying the first coating layer is to use a spraying machine to spray the corundum powder coating on the surface of the steel casting cavity, and the spray thickness is 0.2 ~ 0.3mm , the method of spraying the second coating layer is to use a spraying machine ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a casting method for preventing a large-scale steel casting surface from generating orange peel defects. The casting method includes the steps of modeling, coating spraying and mould assembling pouring. The step of coating spraying includes spraying of a first coating layer and spraying of a second coating layer, coating adopted in the first coating layer is emery powder coating, coating adopted in the second coating layer is zircon powder coating, the method for spraying the first coating layer is that the emery powder coating is sprayed to the surface of a steel casting cavity through a spraying machine, the spraying thickness is 0.2 mm to 0.3 mm, the method for spraying the second coating layer is that the zircon powder coating is sprayed to the first coating layer through the spraying machine, and the spraying thickness if 0.2 mm to 0.3 mm. The zircon powder coating layer and sand mould chromite sand are isolated through the emery powder coating layer, the zircon powder coating layer is not in direct contact with the chromite sand, and therefore the aim that the emery powder coating and molten steel are not in direct contact is achieved, and the problem of reactive sintering of the zircon powder coating and the chromite sand is avoided.

Description

technical field [0001] The invention relates to the technical field of sand casting paint brushing, in particular to a casting method for preventing orange peel defects on the surface of large steel castings. Background technique [0002] The traditional large-scale steel castings are made of resin sand, and the surface sand is all made of chromite sand, and the main component is Cr 2 O 3 ·Fe 2 O 3 , The back sand is all silicon, and the corundum powder coating is brushed or sprayed twice after the steel casting sand mold is demolded, with a total thickness of 0.4~0.6mm, and then poured after 24 hours in the oven. Among them, cylinder steel castings are high-alloy or low-alloy products. The pouring temperature reaches 1560~1570℃, the wall thickness of the castings is 60~500mm, and the gross weight of the castings is 12~80t. With the pouring system, the actual tonnage of the castings will reach Its gross weight is about 2 times. After this type of casting is shot blasted...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22C23/02B22C3/00
Inventor 赵健东冯周荣马瑞杨磊
Owner KOCEL STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap