A kind of preparation method of terrazzo polishing powder

A polishing powder and terrazzo technology, applied in polishing compositions containing abrasives, polishing compositions, chemical instruments and methods, etc., can solve problems such as changes, affecting polishing efficiency and polishing brightness, and achieve easy control of conditions and good polishing effect. , the effect of less dosage

Inactive Publication Date: 2020-11-17
UNIV OF JINAN
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in the polishing powder, the change of the chemical composition will lead to the change of the adhesion between the polishing film and the terrazzo, and the change of the concentration of the polishing powder, which will eventually affect the polishing efficiency and the brightness of the polishing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1)Al 2 o 3 -SiO 2 –Fe 2 o 3 Preparation of the complex: In the reactor, add water: 540 mL, ferric chloride: 60 g, stir and dissolve, aluminum oxide: 250 g, silicon dioxide: 120 g, add ammonia water: 30 mL, and stir at room temperature 30min, solid-liquid separation, dried at 105±2°C, then roasted at 500±10°C for 2h, cooled, and crushed by air flow to obtain Al 2 o 3 -SiO 2 –Fe 2 o 3 Composite, the fineness of which is between 3500 and 4000 mesh;

[0019] (2) Preparation of terrazzo polishing powder: In the grinder, add Al 2 o 3 -SiO 2 –Fe 2 o 3 Compound: 180g, oxalic acid dihydrate: 420g, sodium oxalate: 140g, grind, mix evenly, add phenolic resin: 100g, arachidic acid: 140g, grind, mix evenly, betaine: 20g, grind, mix evenly, terrazzo Polishing powder.

Embodiment 2

[0021] (1)Al 2 o 3 -SiO 2 –Fe 2 o 3 Preparation of the complex: In the reactor, add water: 290mL, ferric chloride: 25g, stir and dissolve, aluminum oxide: 110g, silicon dioxide: 50g, add ammonia water: 25mL, and stir at room temperature for 30min , solid-liquid separation, dried at 105±2°C, then roasted at 500±10°C for 2 hours, cooled, and crushed by air flow to obtain Al 2 o 3 -SiO 2 –Fe 2 o 3 Composite, the fineness of which is between 3500 and 4000 mesh;

[0022] (2) Preparation of terrazzo polishing powder: In the grinder, add Al 2 o 3 -SiO 2 –Fe 2 o 3 Compound: 80g, oxalic acid dihydrate: 225g, sodium oxalate: 80g, grind, mix evenly, add phenolic resin: 40g, arachidic acid: 60g, grind, mix evenly, betaine: 15g, grind, mix evenly, terrazzo Polishing powder.

Embodiment 3

[0024] (1)Al 2 o 3 -SiO 2 –Fe 2 o 3 Preparation of the complex: In the reactor, add water: 54 mL, ferric chloride: 6 g, stir and dissolve, aluminum oxide: 25 g, silicon dioxide: 12 g, add ammonia water: 3 mL, and stir at room temperature 30min, solid-liquid separation, dried at 105±2°C, then roasted at 500±10°C for 2h, cooled, and crushed by air flow to obtain Al 2 o 3 -SiO 2 –Fe 2 o 3 Composite, the fineness of which is between 3500 and 4000 mesh;

[0025] (2) Preparation of terrazzo polishing powder: In the grinder, add Al 2 o 3 -SiO 2 –Fe 2 o3 Compound: 18g, oxalic acid dihydrate: 42g, sodium oxalate: 14g, grind, mix evenly, add phenolic resin: 10g, arachidic acid: 14g, grind, mix evenly, betaine: 2g, grind, mix evenly, terrazzo Polishing powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a terrazzo polishing powder. The preparation method is characterized in that the Al2O3 (aluminum oxide)-SiO2 (silicon dioxide)-Fe2O3 (ferric oxide) compound is used as a grinding material, oxalic acid is used as an acid polishing agent, and a dispersant, a surfactant and the like are used as additives, so as to prepare the polishing powder. The preparation method specifically comprises the following steps of adding the following components into a reactor, such as 50 to 58% of water, and 4 to 8% of ferric trichloride; after stirring and dissolving, adding 22 to 28% of aluminum oxide, and 10 to 15% of silicon dioxide, and adding 3 to 6% of ammonia water, wherein the sum of the components is 100%; stirring to react for 30min at room temperature, separating solid and liquid, drying at the temperature of 105+ / -2 DEG C, roasting for 2h at the temperature of 500+ / -10 DEG C, cooling, and crushing by air flow, so as to obtain the Al2O3-SiO2-Fe2O3 compound. The polishing powder has the advantages that the polishing effect is good, the glossiness is high, the number of scratches is fewer, the flatness is high, and the usage amount is small.

Description

technical field [0001] The invention relates to the field of fine chemicals, in particular to a preparation method of terrazzo polishing powder. Background technique [0002] Terrazzo (also known as terrazzo) is a product made by mixing gravel, glass, quartz stone and other aggregates into cement binder to make a concrete product, and then grinding and polishing the surface. The terrazzo made of cement binder is called inorganic terrazzo, and the terrazzo made of epoxy binder is also called epoxy terrazzo or organic terrazzo. According to the construction process, terrazzo is divided into on-site pouring terrazzo and prefabricated plate terrazzo floor . Traditional terrazzo has a huge market in China due to its unique advantages such as low cost, optional color mosaic, and convenient construction. There are as many as one billion square meters of terrazzo floors used in various buildings in urban and rural areas across the country. Abrasion-resistant terrazzo, the surface ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K3/14
CPCC09G1/02C09G1/18
Inventor 李冬梅李慧芝赵淑英
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com