Preparation method of pressure-resistant coal ash autoclaved bricks
An autoclaved brick and coal ash technology, applied in the field of autoclaved bricks, can solve problems such as poor quality, low strength, and easy cracking, and achieve the effects of increasing dosage, improving quality, and improving freeze-thaw resistance and drying shrinkage performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0014] A preparation method of pressure-resistant coal ash autoclaved brick, comprising the steps of:
[0015] S1. Mix fly ash, slag, and stone powder evenly, add urea, sodium lauryl sulfate, and water to mix evenly, add polyethylene glycol to stir, add phenolic resin to stir, add phosphoric acid to mix evenly, and obtain a prefabricated material;
[0016] S2. statically press the prefabricated material, and perform autoclave treatment to obtain pressure-resistant coal ash autoclaved bricks.
Embodiment 2
[0018] A preparation method of pressure-resistant coal ash autoclaved brick, comprising the steps of:
[0019] S1. Mix 25 parts of fly ash, 30 parts of slag, and 2 parts of stone powder in parts by weight, add 4 parts of urea, 1 part of sodium lauryl sulfate, and 80 parts of water, mix evenly, add 5 parts of polyethylene glycol and stir 50min, the stirring speed is 600r / min, add 18 parts of phenolic resin and stir for 3min, the stirring speed is 2400r / min, add 1 part of phosphoric acid and mix evenly to obtain the prefabricated material;
[0020] S2. The prefabricated material is statically pressed into shape, the pressing pressure is 26MPa, the pressing time is 1min, the autoclaving treatment is 30h, the autoclaving temperature is 185°C, and the autoclaving pressure is 0.6MPa to obtain a pressure-resistant coal ash autoclaved brick.
Embodiment 3
[0022] A preparation method of pressure-resistant coal ash autoclaved brick, comprising the steps of:
[0023] S1. Mix 35 parts of fly ash, 10 parts of slag, and 12 parts of stone powder in parts by weight, add 2 parts of urea, 2 parts of sodium lauryl sulfate, and 40 parts of water, mix well, add 18 parts of polyethylene glycol and stir 30min, the stirring speed is 800r / min, add 4 parts of phenolic resin and stir for 8min, the stirring speed is 2000r / min, add 2 parts of phosphoric acid and mix evenly to obtain the prefabricated material;
[0024] S2. The prefabricated material is statically pressed into shape, the pressing pressure is 22MPa, the pressing time is 2min, the autoclaving treatment is 20h, the autoclaving temperature is 195°C, and the autoclaving pressure is 0.4MPa to obtain the pressure-resistant coal ash autoclaved brick.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap