Continuous casting alloy steel bloom convex combined roller and heavy pressing process

A technology for alloy steel and bloom, which is applied in the field of continuous casting alloy steel bloom convex combined rolls and heavy reduction technology, can solve the problems of inability to improve segregation defects and high reduction efficiency, and solve the problem of matching reduction traces, The effect of improving the quality of the heart and stable quality

Inactive Publication Date: 2018-01-05
DONGBEI SPECIAL STEEL GRP DALIAN SPECIAL STEEL CO LTD
View PDF12 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Due to the high reduction efficiency, the current gradual curvature convex roll reduction process can only improve shrinkage defects at the end of solidification, but cannot improve segregation defects at the two-phase region.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous casting alloy steel bloom convex combined roller and heavy pressing process
  • Continuous casting alloy steel bloom convex combined roller and heavy pressing process
  • Continuous casting alloy steel bloom convex combined roller and heavy pressing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] In Embodiment 1 and Embodiment 2, the same convex combination roller is used to carry out the pressing process in the pouring link, and the specification of the continuous casting slab: 380mm×490mm.

[0038] Example 1

[0039] Brand: 2Cr13, Sample: 3439-303

[0040] Convex combined roll reduction: 5mm+12mm;

[0041] Comparison of the reduction effect by the transverse low-magnification structure level of the continuous casting slab:

[0042] Unpressed: if Figure 4 As shown, medium pine 1.0, shrinkage cavity 2.0

[0043] Convex combined roller pressing: such as Figure 5 As shown, medium pine 0.5, shrinkage cavity 0

Embodiment 2

[0045] Brand: GCr15, Sample: 0120-101, 0120-301

[0046] Convex combined roll reduction: 6mm+15mm;

[0047] Comparison of the reduction effect by the transverse low-magnification structure level of the continuous casting slab:

[0048] Unpressed: if Image 6 As shown, medium pine 2.0, center crack 1.0

[0049] Convex combined roller pressing: such as Figure 7 As shown, medium pine 0.5, shrinkage cavity 0

[0050] Test for carbon segregation:

[0051] Carbon segregation detection is centered on the geometric center of the slab, using a 5mm drill bit to drill steel shavings every 20mm for chemical analysis. The sampling points are as follows: Figure 8 shown. Among them, 23 points are taken in the width direction, and the center point is the 12th point; 17 points are taken in the inner and outer arc directions (the center point is still the 12th point); the midpoint of the line connecting the geometric center to the four corners (4 1 / 4 places points), a total of 43 point...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a continuous casting alloy steel bloom convex combined roller and a heavy pressing process. The core quality problem of a continuous cast bloom is solved. The technical schemecomprises the convex combined roller and the heavy pressing process; the convex combined roller is characterized in that a pulling-straightening roller is designed to be a constant-curvature boss-freeconvex roller body capable of improving the segregation in the flowing direction of enriched molten steel before the continuous cast bloom is solidified and a gradually-changed-curvature boss convexroller body capable of compensating severe looseness and cavity shrinkage defects formed by volume shrinkage; the constant-curvature boss-free convex roller body is located at the position where the central solid phase ratio is 0.2; the gradually-changed-curvature boss convex roller body is located at the position of the solidification ending point; the accurate pressing parameters of the convex roller bodies are determined; and pressing under large deflection is conducted in sequence at the two positions. The continuous casting alloy steel bloom convex combined roller and the heavy pressing process have the beneficial effects that by adoption of the convex combined roller equipment and the heavy pressing process, the quality defects of the segregation of chemical components, solidification center cavity shrinkage and severe looseness of the continuous cast bloom are overcome, and the macroscopic examination shows that the core quality of the continuous cast bloom is remarkably improved and quality is stable.

Description

technical field [0001] The invention relates to a continuous casting alloy steel bloom convex combination roll and a heavy reduction process, belonging to the field of continuous casting of steel production. Background technique [0002] In order to eliminate quality problems such as center porosity, center segregation, and shrinkage cavity of the continuous casting slab, domestic alloy steel bloom continuous casting machines have basically introduced foreign straight roll multi-stand and dynamic soft reduction equipment technology. Due to the larger cross-section of the bloom, the temperature of the shells on both sides is about 20°C lower than that of the center, and the tensile strength is higher, so the deformation resistance is greater, and the shells on both sides have a greater lateral tensile force on the liquid core, which easily leads to the formation of solid-liquid interface For tearing, only the technology of multi-pass and small reduction can be used, but for a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/12
Inventor 周伟基路辉王震宙吴鹏马玉民毕胜姜盛鑫蒲洪波金鑫毕建良杜飞虎杨毓水何德永候雪宇丁玉亮
Owner DONGBEI SPECIAL STEEL GRP DALIAN SPECIAL STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products