Preparation of an antibacterial and immunomodulatory surface-functionalized electrospun membrane for bone regeneration

A technology of surface functionalization and immunoregulation, which is applied in the field of antibacterial and immunoregulatory implant materials, can solve problems such as low bioavailability, and achieve the effect of solving clinical challenges

Active Publication Date: 2021-03-05
WUXI ZHONGKE GUANGYUAN BIOMATERIALS
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the clinical application of azithromycin is limited by its low water solubility, low bioavailability (37%), and its systemic side effects (such as diarrhea, abdominal pain, and other gastrointestinal symptoms)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for preparing an antibacterial and immunomodulatory surface-functionalized electrospun membrane for bone regeneration, including the preparation of a medical-grade polycaprolactone membrane, the preparation of a medical-grade polycaprolactone membrane containing a calcium phosphate coating, Preparation of medical-grade polycaprolactone film loaded with azithromycin calcium phosphate coating, wherein the preparation of the medical-grade polycaprolactone film of calcium phosphate coating mainly includes three steps of surface activation, biomimetic mineralization and post-treatment

[0028] The preparation of described medical grade polycaprolactone film is as follows:

[0029] Dissolve 5g of polycaprolactone (Mw=80,000) in a mixture of chloroform and dimethylformamide (the volume ratio of chloroform and dimethylformamide is 9 / 1), stir at room temperature for 4 hours, and prepare the concentration As a 25% (w / v) solution. Put the polymer solution into a 5mL syri...

Embodiment 2

[0037] A method for preparing an antibacterial and immunomodulatory surface-functionalized electrospun membrane for bone regeneration, including the preparation of a medical-grade polycaprolactone membrane, the preparation of a medical-grade polycaprolactone membrane containing a calcium phosphate coating, Preparation of medical-grade polycaprolactone film loaded with azithromycin calcium phosphate coating, wherein the preparation of the medical-grade polycaprolactone film of calcium phosphate coating mainly includes three steps of surface activation, biomimetic mineralization and post-treatment

[0038] The preparation of described medical grade polycaprolactone film is as follows:

[0039] Dissolve 10g of polycaprolactone (Mw=150,000) in a mixture of acetone and dimethylformamide (the volume ratio of acetone and dimethylformamide is 9 / 1), stir at room temperature for 5 hours, and prepare the concentration As a 20% (w / v) solution. Put the polymer solution into a 5mL syringe....

Embodiment 3

[0047] A method for preparing an antibacterial and immunomodulatory surface-functionalized electrospun membrane for bone regeneration, including the preparation of a medical-grade polycaprolactone membrane, the preparation of a medical-grade polycaprolactone membrane containing a calcium phosphate coating, Preparation of medical-grade polycaprolactone film loaded with azithromycin calcium phosphate coating, wherein the preparation of the medical-grade polycaprolactone film of calcium phosphate coating mainly includes three steps of surface activation, biomimetic mineralization and post-treatment

[0048] The preparation of described medical grade polycaprolactone film is as follows:

[0049] Dissolve 10g of polycaprolactone (Mw=50,000) in a mixture of acetone and dimethylformamide (the volume ratio of acetone and dimethylformamide is 9 / 1), stir at room temperature for 5 hours, and prepare the concentration As a 20% (w / v) solution. Put the polymer solution into a 5mL syringe. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to the technical field of antibacterial and immunoregulatory implant materials, in particular to a method for preparing a surface-functionalized electrospinning membrane for antibacterial and immunoregulatory bone regeneration, including the preparation of medical-grade polycaprolactone by electrospinning The film is coated with a calcium phosphate coating, and the antibiotic azithromycin is fixed in the film by solvent evaporation technology to obtain a medical grade polycaprolactone film loaded with azithromycin calcium phosphate coating. The membrane prepared by this method can be used for local and controlled drug delivery, which solves the clinical problem of infection during guided bone regeneration, and circumvents the limitations associated with systemic administration of azithromycin, and has broad application prospects in the field of biomedicine, especially orthopedics.

Description

technical field [0001] The invention relates to the technical field of antibacterial and immunoregulatory implant materials, in particular to a method for preparing an antibacterial and immunoregulatory surface functionalized electrospun membrane for bone regeneration. Background technique [0002] Guided bone regeneration (GBR) is a technique widely used to restore bone defects. The GBR technique involves the surgical application of a barrier membrane that must fulfill several criteria such as biocompatibility, steric maintenance capacity, and not only for the time period of tissue regeneration but also for the entire duration of the wound maturation and remodeling process. Retention of internal barrier properties. In addition to these physical criteria, bioactivity is considered a desirable feature of GBR membranes to initiate and enhance bone formation. GBR technology is a surgical operation that uses a barrier membrane to provide space maintenance and selective repopul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L31/06A61L31/08A61L31/16D04H1/728
Inventor 黄建祥许杉杉孟庆怡
Owner WUXI ZHONGKE GUANGYUAN BIOMATERIALS