Fireproof and transparent building paint and preparation method thereof

A kind of architectural coating and transparent technology, applied in the direction of fireproof coating, etc., can solve the problems of unavoidable fire of wooden building materials, easy melting of coating, etc., and achieve the effect of maintaining aesthetics, high melting point and low cost

Inactive Publication Date: 2018-02-02
FOSHAN CITY SANSHUI DISTRICT MANYA ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This new type of paint made with this composition will be resistant against fires even at very hot temperatures without covering up any wood structures or other things like windows on top.

Problems solved by technology

Technological Problem: Current architectural coatings used to enhance durable properties such as water resistance often result in unsatisfactory results due to their lack of transparency during exposure time under high temperatures (such as fires). Additionally, current methods require expensive equipment that may damage wood surfaces overtime causing them to lose strength quickly after being exposed to these conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The fireproof transparent architectural paint of the present invention consists of the following components in parts by weight:

[0043] 5 parts of mica powder;

[0044] Y 2 o 3 - 1 part of ZrO2 nanoparticles;

[0045] 1 part sodium silicate;

[0046] 5 parts of pentaerythritol;

[0047] 7 parts of film-forming agent;

[0048] Sodium fluoroaluminate 1 part;

[0049] 30 parts of water;

[0050] 3 parts adhesive;

[0051] 3 parts of thickener;

[0052] 2 parts of flame retardant.

[0053] The preparation method of fireproof transparent architectural coating of the present invention is: when preparing, the mica powder of above-mentioned parts by weight, Y 2 o 3 -ZrO2 nanoparticles, sodium silicate, pentaerythritol, film-forming agent, sodium fluoroaluminate were added to water and stirred for 2 minutes, cooled to 8°C, then added adhesive, thickener, flame retardant and stirred for 1 minute, heated to room temperature to prepare become.

Embodiment 2

[0055] The fireproof transparent architectural paint of the present invention consists of the following components in parts by weight:

[0056] 5 parts of mica powder;

[0057] Y 2 o 3 - 1 part of ZrO2 nanoparticles;

[0058] 1 part sodium silicate;

[0059] 5 parts of pentaerythritol;

[0060] 7 parts of film-forming agent;

[0061] Sodium fluoroaluminate 1 part;

[0062] 30 parts of water;

[0063] 3 parts adhesive;

[0064] 3 parts of thickener;

[0065] 2 parts of flame retardant.

[0066] The preparation method of fireproof transparent architectural coating of the present invention is: when preparing, the mica powder of above-mentioned parts by weight, Y 2 o 3 -ZrO2 nanoparticles, sodium silicate, pentaerythritol, film-forming agent, sodium fluoroaluminate were added to water and stirred for 5 minutes, cooled to 6°C, then added adhesive, thickener, flame retardant and stirred for 1 minute, heated to room temperature to prepare become.

Embodiment 3

[0068] The fireproof transparent architectural paint of the present invention consists of the following components in parts by weight:

[0069] 5 parts of mica powder;

[0070] Y 2 o 3 - 1 part of ZrO2 nanoparticles;

[0071] 1 part sodium silicate;

[0072] 5 parts of pentaerythritol;

[0073] 7 parts of film-forming agent;

[0074] Sodium fluoroaluminate 1 part;

[0075] 30 parts of water;

[0076] 3 parts adhesive;

[0077] 3 parts of thickener;

[0078] 2 parts of flame retardant.

[0079] The preparation method of fireproof transparent architectural coating of the present invention is: when preparing, the mica powder of above-mentioned parts by weight, Y 2 o 3 -ZrO2 nanoparticles, sodium silicate, pentaerythritol, film-forming agent, sodium fluoroaluminate were added to water and stirred for 8 minutes, cooled to 4°C, then added adhesive, thickener, flame retardant and stirred for 1 minute, heated to room temperature to prepare become.

[0080] According to the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fireproof transparent architectural coating and a preparation method thereof, which is composed of the following components in parts by weight: 5-8 parts of mica powder, 1-3 parts of Y2O3-ZrO2 nanoparticles, 1-2 parts of sodium silicate, 5-8 parts of pentaerythritol, 7-12 parts of film-forming agent, 1-2 parts of sodium fluoroaluminate, 30-90 parts of water, 3-5 parts of adhesive, 3-5 parts of thickener, 2 parts of flame retardant -5 servings. The paint prepared by the above formula in the present invention has the characteristics of high melting point and transparency. It can not only form a layer of fire-proof coating that is not easy to melt under high temperature and isolate the air on the surface of wooden building materials, but also does not cover the texture of wooden building materials. , to maintain the aesthetics of building materials. The invention solves the problem that the existing paints do not have fireproofing and aesthetics, and provides a fireproofing transparent building paint with low cost and simple preparation.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Owner FOSHAN CITY SANSHUI DISTRICT MANYA ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com