A self-adhesive waterproof membrane, non-bitumen-based technology, applied in the direction of non-polymer adhesive additives, adhesives, adhesive types, etc., can solve the problem of poor waterproof quality, heavy waterproof membrane weight, and asphalt weather resistance In order to solve the problems of limited durability, it can achieve the effect of durable and excellent bonding performance, good low-temperature bending performance, convenient transportation and construction

Inactive Publication Date: 2018-02-09
湖北蓝盾之星科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As the price of asphalt continues to rise; the technology of self-adhesive membranes is becoming more and more mature. Due to the increasingly mature technology, some small factories flood the market with a large number of defective products, so many asphalt self-adhesive waterproofing membranes on the market are mixed with good and bad people, resulting in poor waterproof quality. There is no guarantee; at this stage, people's requirements for environmental protection are becoming more and more stringent, and asphalt is a very complex substance, which contains many substances that are not friendly to the environment. Due to the existence of asphalt, it will affect environmental protection; The requirement for waterproofing life is getting higher and higher, and the weather resistance of asphalt is very limited; in addition, due to the heavy weight of the traditional waterproof membrane, it brings great difficulty to storage and construction. Stirring needs to be heated to about 200°C, which increases energy consumption and causes great environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Extraction oil 30%, waste oil (recovered cooking oil) 10%, hot melt adhesive grade elastomer (EVA) 4%, SBS 411 (LG company star-shaped benzene blended ethylene-butadiene-styrene block copolymer , the grade is 411) 6.8%, SIS 2%, high softening point coumarone resin 5%, C9 petroleum resin 15%, devulcanized rubber powder 12%, floating beads 15%, ultraviolet agent (UV531) 0.1%, interface agent ( Water-soluble epoxy-modified acrylate) 0.1%.

[0024] The non-bitumen-based waterproof membrane prepared according to the above production process has the following product properties: peel strength 3.7N / mm, bond strength with concrete 5.0N / mm, low temperature -30°C without breaking, high temperature resistance 70°C No flow, peel strength 2.0N / mm after UV aging resistance, no break at low temperature -25°C, no flow at high temperature 70°C, peel strength 2.5N / mm after heat aging resistance, no break at low temperature -25°C, High temperature resistance 70 ℃ does not flow. Fully me...

Embodiment 2

[0026] Heavy oil 32%, waste oil (recovered edible oil) 7%, hot melt adhesive grade elastomer (EVA) 6%, styrene-butadiene-styrene block copolymer (Yueyang Petrochemical linear styrene-butadiene Styrene-styrene block copolymer (SBS) grade is 1301) 8.8%, SIS 1%, high softening point coumarone resin 7%, C9 petroleum resin 15%, devulcanized rubber powder 13%, floating beads 10%, anti Ultraviolet agent (UV327) 0.1%, interface agent (water-soluble epoxy-modified acrylate) 0.1%.

[0027] The non-bitumen-based waterproof membrane prepared according to the above production process has the following product properties: peel strength 4.3N / mm, bond strength with concrete 4.5N / mm, low temperature -30°C without breaking, high temperature resistance 70°C No flow, peel strength after UV aging resistance is 2.2N / mm, low temperature temperature -25°C does not break, high temperature resistance does not flow at 70°C, peel strength after heat aging resistance is 2.3N / mm, low temperature temperatur...

Embodiment 3

[0029] Light oil 30%, waste oil (recycled cooking oil), hot melt adhesive grade elastomer (EVA) 2%, styrene-butadiene-styrene block copolymer (SBS 411) 2%, SBR 1%, High softening point coumarone resin 7%, C9 petroleum resin 10%, sole rubber 16%, floating beads 19.8%, ultraviolet agent (UV1164) 0.1%, interface agent (water-soluble epoxy-modified acrylate) 0.1%.

[0030] The non-bitumen-based waterproof membrane prepared according to the above production process has the following product properties: peel strength 3.3N / mm, bond strength with concrete 4.0N / mm, low temperature -30°C without breaking, high temperature resistance 70°C No flow, peel strength 1.8N / mm after UV aging resistance, no breakage at low temperature -25°C, no flow at high temperature 70°C, peel strength 2.0N / mm after heat aging resistance, no breakage at low temperature temperature -25°C, High temperature resistance 70 ℃ does not flow. Fully meet the national standard GB / T 23441 type II and GB / T 23457 wet layi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a modified non-asphalt-base self-adhesion waterproof coiled material with floating beads. The modified non-asphalt-base self-adhesion waterproof coiled material is characterizedby comprising, by weight, 15-48% of electron-rich system softening oil (which is a mixture, contains large pi bonds and accordingly is an electron-rich system), 0.5-6% of hot melt adhesive grade elastomers, 2-10% of styrene-butadiene-styrene block copolymers, 1-5% of tackifying rubber, 5-20% of waste rubber elastomers, 0.1-0.5% of anti-ultraviolet agents, 3-8% of high-temperature resin, 8-20% oftackifying resin, 0.1-0.2% of interfacial agents, 5-30% of floating beads and 5-15% of waste edible oil. The electron-rich system softening oil, the hot melt adhesive grade elastomers, the styrene-butadiene-styrene block copolymers, the tackifying rubber, the waste rubber elastomers, the anti-ultraviolet agents, the high-temperature resin, the tackifying resin, the interfacial agents, the floatingbeads and the waste edible oil are prepared to obtain the modified non-asphalt-base self-adhesion waterproof coiled material.

Description

technical field [0001] The invention relates to the technical field of chemical waterproof materials, in particular to a self-adhesive waterproof material which is different from traditional asphalt-based materials. Background technique [0002] As the price of asphalt continues to rise; the technology of self-adhesive membranes is becoming more and more mature. Due to the increasingly mature technology, some small factories flood the market with a large number of defective products, so many asphalt self-adhesive waterproof membranes on the market are mixed with good and bad people, resulting in poor waterproof quality. There is no guarantee; at this stage, people's requirements for environmental protection are becoming more and more stringent, and asphalt is a very complex substance, which contains many substances that are not friendly to the environment. Due to the existence of asphalt, it will affect environmental protection; The requirement for waterproofing life is gett...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J157/02C09J123/08C09J153/02C09J145/02C09J11/08C09J11/04
CPCC09J157/02C08L2201/08C08L2205/025C08L2205/035C09J11/04C09J11/08C08L21/00C08L53/02C08L23/0853C08L91/00C08L45/02C08K7/26C08K7/24
Inventor 鲁小龙童祖元童未峰陈有智张祖华胡胜平
Owner 湖北蓝盾之星科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap