Formula of millable polyurethane rubber

A mixing-type polyurethane and rubber technology, which is applied in the formulation field of mixing-type polyurethane rubber, can solve problems such as low labor productivity, unreasonable design, and high energy consumption, and achieve high labor productivity, reasonable design, and high energy consumption. The effect of low consumption

Inactive Publication Date: 2018-03-09
李舜林
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing mix-type polyurethane rubber mix ratio design is unreasonable and cannot be applied to the needs of existing production and life. The cost is high, the labor productivity is low, the energy consumption is high in the process of processing and manufacturing, and high production cannot be achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A formula for mixing type polyurethane rubber, calculated in parts by weight, comprising 95 parts of raw material mixing type polyurethane rubber, 17 parts of coumarone resin, 7 parts of accelerator, 2 parts of anti-aging agent, 4 parts of sulfur, high wear-resistant 5 parts of carbon black, 3.5 parts of stearate, 7 parts of sodium stearate, 15 parts of sulfur, and 5 parts of pine tar.

Embodiment 2

[0017] A formula for mixing type polyurethane rubber, calculated in parts by weight, comprising 87 parts of raw material mixing type polyurethane rubber, 12 parts of coumarone resin, 6 parts of accelerator, 1 part of anti-aging agent, 2 parts of sulfur, high wear-resistant 4 parts of carbon black, 2.5 parts of stearate, 6 parts of sodium stearate, 11 parts of sulfur, and 2 parts of pine tar.

Embodiment 3

[0019] A formula for mixing type polyurethane rubber, calculated in parts by weight, comprising 104 parts of raw material mixing type polyurethane rubber, 29 parts of coumarone resin, 9 parts of accelerator, 3 parts of anti-aging agent, 5 parts of sulfur, high wear-resistant 6 parts of carbon black, 4 parts of stearate, 9 parts of sodium stearate, 19 parts of sulfur, 6 parts of pine tar.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a formula of mixing type polyurethane rubber, which comprises 87-104 parts of raw material mixing type polyurethane rubber, 12-29 parts of coumarone resin, 6-9 parts of accelerator, and anti-aging agent, calculated according to parts by weight 1‑3 parts, 2‑5 parts of sulfur, 4‑6 parts of high wear-resistant carbon black, 2.5‑4 parts of stearic acid, 6‑9 parts of sodium stearate, 11‑19 parts of sulfur, 2‑6 parts of pine tar , the present invention has an extremely reasonable mix design, is suitable for the needs of existing production and life, has low cost, high labor productivity, low energy consumption in the manufacturing process, and can achieve high-yield rubber formula.

Description

technical field [0001] The invention relates to the field of rubber preparation, in particular to a formula of mixing type polyurethane rubber. Background technique [0002] Early rubber was latex taken from plants such as rubber trees and rubber grasses, which were processed into materials with elasticity, insulation, impermeability to water and air. High elastic polymer compound. Divided into two kinds of natural rubber and synthetic rubber. Natural rubber is processed by extracting gum from rubber trees, rubber grass and other plants; synthetic rubber is obtained by polymerization of various monomers. Rubber products are widely used in all aspects of industry or life. The existing mix-type polyurethane rubber has an unreasonable design of mixing ratio, cannot meet the needs of existing production and life, has high cost, low labor productivity, high energy consumption in the process of processing and manufacturing, and cannot achieve high yield. Contents of the inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/04C08L45/02C08K13/02C08K3/06C08K3/04C08K5/098
CPCC08L75/04C08K2201/014C08L2205/03C08L45/02C08K13/02C08K3/06C08K3/04C08K5/098
Inventor 李舜林
Owner 李舜林
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap