Enhanced type adsorbable ligation clip and preparation method thereof

An enhanced ligation clip technology, which is applied in medical formula, medical science, surgery, etc., can solve the problems of MRI and CT artifacts and deflection, weak closure force of ligation clips, and hidden dangers of patient rehabilitation, and achieve good biodegradability Sexuality, strong closure force, and good biocompatibility

Active Publication Date: 2018-03-20
SHANDONG ACADEMY OF PHARMACEUTICAL SCIENCES
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Metal clips are easy to operate, have excellent mechanical properties, and are widely used in clinical practice. However, due to their metal properties, they have the following disadvantages: Interfering with imaging examinations, MRI and CT have artifacts and deflection; when using a coagulator during surgery, there is a risk of conductive damage to tissue ; Rigid structure, narrow ligation range
Polydioxanone (PPDO) has excellent flexibility and processability, and has become the preferred raw material for absorbable ligation clips, such as Johnson & Johnson Anshu Suppository TM, etc., but due to the influence of its mechanical strength and modulus, The closure force of the ligation clip is weak, and the FDA adverse event report shows that different types of Johnson & Johnson absorbable ligation clip products have over-closure failures
In addition, the healing time of the luminal tissue is only 2 weeks, while all marketed absorbable ligation clips, such as Johnson & Johnson Anshu SuppositoryTM, Tyco Lapro-ClipTM and Hangzhou Shengshi Sufeng, need more than 180 days to completely degrade. There is a long postoperative risk period, such as inflammation, adhesion, etc., which brings hidden dangers to the recovery of patients

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Enhanced type adsorbable ligation clip and preparation method thereof
  • Enhanced type adsorbable ligation clip and preparation method thereof
  • Enhanced type adsorbable ligation clip and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The invention also discloses a method for preparing an enhanced absorbable ligature clip, comprising the following steps:

[0035] ① Vacuum-dry the polyester material at 100°C for 24 hours. Under the protection of nitrogen, put it in the screw of the spinning device to melt it. Under the voltage of 8~30KV, extrude and spin the filament at a constant speed. After receiving it in the vortex cooling liquid tank, the diameter 1-10 μm polyester fiber bundle; the polyester material is polyglycolide or polylactide;

[0036] ②Under the protection of nitrogen, heat-stretch the polyester fiber bundle obtained in step ① twice, each stretching ratio is 5-8 times, to obtain nanofibers with a diameter of 300-500nm;

[0037] When the material of the polyester fiber bundle obtained in step 1 is polyglycolide, the temperatures of the two thermal stretches are respectively 180°C and 160°C; The stretching temperatures are 150°C and 130°C respectively;

[0038] ③ The nanofibers obtained ...

Embodiment 1

[0053] A reinforced absorbable ligature clip, the material used in the ligature clip is composed of base material and nano-short fibers, the nano-short fibers maintain a crystalline form and are uniformly dispersed in the base material, and the mass percentage of nano-short fibers in the composite material is 5% ; The base material is polydioxanone; the nano-short fiber is a polyester material, and the polyester material is polyglycolide; the diameter of the nano-short fiber is 300nm, and the length is 20 μm.

Embodiment 2

[0055] A reinforced absorbable ligature clip, the material used in the ligature clip is composed of base material and nano-short fibers, the nano-short fibers maintain a crystalline form and are uniformly dispersed in the base material, and the mass percentage of nano-short fibers in the composite material is 50% ; The base material is polytrimethylene carbonate; the nano-short fiber is a polyester material, and the polyester material is polylactide; the diameter of the nano-short fiber is 500nm, and the length is 50 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an enhanced type adsorbable ligation clip and a preparation method thereof. The ligation clip is prepared from a base material and nano staple fibers, the nano staple fibers are uniformly dispersed in the base material in a manner of keeping a crystalline form, and the mass percent of the nano staple fibers in a composite material is 5% to 50%. The enhanced type adsorbableligation clip disclosed by the invention has good biocompatibility and biodegradability; after the ligation clip is used, phenomena such as tissue adhesion, infarction and sepsis cannot be caused; during degradation, polyester materials of the nano staple fibers such as polyglycollide or polylactide are relatively high in hydrolysis speed, and a regional acidic environment can be generally formedinside the ligation clip in 30 days, so that the degradation of the base material is accelerated, and the absorption time of the base material is greatly shortened to 90 days from original 180 days; the generation of foreign-matter adverse reaction is absent, so that the clinical requirements of medical materials can be met.

Description

technical field [0001] The invention relates to the technical field, in particular to an enhanced absorbable ligation clip and a preparation method thereof. Background technique [0002] Compared with the traditional silk ligation, the disposable ligation clip suitable for laparoscopic surgery is more convenient, accurate and efficient in operation, and its clinical effectiveness has been recognized. Because of its wide application range, large dosage and high added value, it has been favored by domestic and foreign enterprises and research institutes. People are widely concerned. At present, ligation clips are mainly divided into metal clips, non-absorbable plastic clips and absorbable ligation clips according to their materials. [0003] Metal clips are easy to operate, have excellent mechanical properties, and are widely used in clinical practice. However, due to their metal properties, they have the following disadvantages: Interfering with imaging examinations, MRI and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L17/12
CPCA61L17/12A61L2400/04
Inventor 刘阳朱爱臣马丽霞王宪朋董浩吴倩倩李俊起王传栋王勤
Owner SHANDONG ACADEMY OF PHARMACEUTICAL SCIENCES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com