Embossed hollow-out dazzling gold lace sheet and preparation technology thereof

A relief and dazzling technology, applied in the field of lace relief hollow dazzling gold sheet and its preparation, can solve the problems of small ornamental, poor mechanical and physical properties, etc., achieve good chemical stability, low production cost, Stable quality effect

Inactive Publication Date: 2018-04-03
DONGGUAN IUIU HOUSEHOLD PROD
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing patterns are generally flat patterns, which are less ornamen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Embossed hollow-out dazzling gold lace sheet and preparation technology thereof
  • Embossed hollow-out dazzling gold lace sheet and preparation technology thereof
  • Embossed hollow-out dazzling gold lace sheet and preparation technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] A lace embossed hollowed-out colorful gold sheet, said lace embossed hollowed-out colorful gold sheet comprises the following raw materials in parts by weight:

[0053]

[0054]

[0055] The PVC resin is an ethylene-based PVC resin with an average degree of polymerization of 1000.

[0056] The filler is composed of light calcium carbonate with a particle size of 10 μm and modified by high-grade fatty acid salts and heavy calcium carbonate with a particle size of 100 μm and modified with high-grade fatty acid esters. A mixture of 0.5:1 composition.

[0057] The heat stabilizer is a mixture of calcium stearate, barium stearate, zinc stearate and hydrotalcite in a weight ratio of 1:0.8:0.8:0.4.

[0058] The toner material is a mixture of phthalocyanine blue and ultramarine blue toner in a weight ratio of 0.8:1.

[0059] The titanium dioxide is surface-treated, and its preparation method is: stir the rutile-type titanium dioxide at a high speed at 100°C for 15 minut...

Embodiment 2

[0071] A lace embossed hollowed-out colorful gold sheet, said lace embossed hollowed-out colorful gold sheet comprises the following raw materials in parts by weight:

[0072]

[0073] The PVC resin is an ethylene-based PVC resin with an average degree of polymerization of 1200.

[0074] The filler is composed of light calcium carbonate with a particle size of 2 μm and modified by high-grade fatty acid salts and heavy calcium carbonate with a particle size of 200 μm and modified with high-grade fatty acid esters. 0.8:1 composition mixture.

[0075] The heat stabilizer is a mixture of calcium stearate, barium stearate, zinc stearate and hydrotalcite in a weight ratio of 1:0.9:0.9:0.5.

[0076] The toner material is a mixture of phthalocyanine blue and ultramarine blue toner in a weight ratio of 0.9:1.

[0077] The titanium dioxide is surface-treated, and its preparation method is: stir the rutile-type titanium dioxide at a high speed of 105°C for 18 minutes to remove the a...

Embodiment 3

[0089] A lace embossed hollowed-out colorful gold sheet, said lace embossed hollowed-out colorful gold sheet comprises the following raw materials in parts by weight:

[0090]

[0091] The PVC resin is an ethylene-based PVC resin with an average degree of polymerization of 1500.

[0092] The filler is composed of light calcium carbonate with a particle size of 30 μm and modified by high-grade fatty acid salts and heavy calcium carbonate with a particle size of 300 μm and modified with high-grade fatty acid esters. 1:1 composition mixture.

[0093] The heat stabilizer is a mixture of calcium stearate, barium stearate, zinc stearate and hydrotalcite in a weight ratio of 1:1:1:0.6.

[0094] The toner material is a mixture of phthalocyanine blue and ultramarine blue toner in a weight ratio of 1:1.

[0095] The titanium dioxide is surface-treated, and its preparation method is: stir the rutile-type titanium dioxide at a high speed of 110°C for 20 minutes to remove the absorbed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of sheets, in particular to an embossed hollow-out dazzling gold lace sheet and a preparation technology thereof. The embossed hollow-out dazzling gold lace sheet is prepared from raw materials in parts by weight as follows: 40-50 parts of PVC resin, 60-65 parts of a filling agent, 30-38 parts of diisononyl phthalate, 2.0-2.5 parts of a heat stabilizer,0.2-0.25 parts of a toner material, 0.15-0.20 parts of titanium dioxide and 0.03-0.04 parts of other auxiliaries. The embossed hollow-out dazzling gold lace sheet has better three-dimensional effect,touches soft and comfortable, further has the advantages of being good in chemical stability, flame-retardant, insulated, acid-resistant, alkali-resistant, waterproof, dampproof, corrosion-resistant,tension-resistant, anti-aging, anti-static and the like and is excellent in comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of sheets, in particular to a lace embossed hollowed-out colorful gold sheet and a preparation process thereof. Background technique [0002] With the development of society, the improvement of human living standards and the constant pursuit of material, it is now more and more convenient, fashionable and beautiful to use in the field of household daily products. Soft polyvinyl chloride sheet is transparent and beautiful, soft in texture, and has been widely used in the field of daily products, such as tablecloths, table mats and place mats, some home decorations for floor mats, etc. This type of product is generally attached with a transparent film on the other side of the printed pattern. When it is covered on furniture, especially glass furniture, it can not only display the printed pattern on the transparent film, but also observe the shape of the furniture through the transparent film. Play a very good...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08K13/06C08K9/04C08K3/26C08K5/098C08K5/12B29C69/00B29C47/00B29L7/00
CPCB29L2007/002B29C48/001B29C48/0023C08K3/26C08K5/098C08K5/12C08K9/04C08K13/06C08K2003/265C08K2201/003C08K2201/014C08L27/06C08L2201/02C08L2201/04C08L2205/035C08L2205/16C08L67/00
Inventor 刘承发
Owner DONGGUAN IUIU HOUSEHOLD PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap