Nano-emulsion for fracturing water control and preparation method of nano-emulsion
A technology for nanoemulsions and water, applied in chemical instruments and methods, drilling compositions, etc., can solve the problems of large particle size, high viscosity, poor physical properties, etc., and achieve low surface tension, low viscosity, and low permeability Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0057] Example 1
[0058] At room temperature, take 20.0g dihydroxy polydimethylsiloxane, hydroxyl content: 8.0%, molecular weight 16000, 5.0g alkylphenol polyoxyethylene ether NP-10, 2.0g fatty acid polyoxyethylene ester OEO- 103,5.0g of n-propanol was added to the dihydroxy polydimethylsiloxane, stirred at 100r / min for 30min, and then at 50℃, 400r / min stirring, 33.0g of deionized water was dropped uniformly within 15min Into the oil phase, a transparent and uniform liquid is obtained, which is a nanoemulsion for fracturing water control.
Example Embodiment
[0059] Example 2
[0060] At room temperature, take 20.0g dihydroxy polydimethylsiloxane, the hydroxyl content is 12.0%, the molecular weight is 50000, 6.2g alkylphenol polyoxyethylene ether NP-10, 3.0g fatty acid polyoxyethylene ester OEO- 103,6.0g of n-butanol was added to the dihydroxy polydimethylsiloxane, stirred at 100r / min for 30min, and then at 80℃, 800r / min stirring, 40.0g of deionized water was dropped uniformly within 15min Into the oil phase, a transparent and uniform liquid is obtained, which is a nanoemulsion for fracturing water control.
Example Embodiment
[0061] Example 3
[0062] At room temperature, take 20.0g dihydroxy polydimethylsiloxane, the hydroxyl content is: 8.0%, the molecular weight is 50000, 4.0g alkylphenol polyoxyethylene ether NP-12, 4.0g fatty acid polyoxyethylene ester OEO- 103,3.0g of n-propylamine was added to the dihydroxy polydimethylsiloxane, stirred at 100r / min for 25min, and then at 40℃, 500r / min stirring, 35.0g of deionized water was dropped uniformly in 20min In the oil phase, a transparent and uniform liquid is obtained, which is a nanoemulsion for fracturing and water control.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap