Wear-resistant blended yarn weaved fabric

A technology of blended fabrics and wear-resistant coatings, applied in the field of clothing fabrics, can solve problems such as excessive hairiness, hard hand feeling, rough jute cloth, etc., and achieve the effect of solving poor wear resistance and excellent wear resistance

Inactive Publication Date: 2018-04-20
大连率为环保科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Jute cloth is rough, hard to the touch, and has a lot of hairiness, so it is not suitable for clothing materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant blended yarn weaved fabric
  • Wear-resistant blended yarn weaved fabric
  • Wear-resistant blended yarn weaved fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A preparation method of a wear-resistant blended fabric, the preparation method comprising the steps of:

[0028] By weight, get 7 parts of polyester fiber, 5 parts of polypropylene fiber;

[0029] Blending polyester fibers and polypropylene fibers to obtain a base fabric layer;

[0030] In parts by weight, take 50 parts of polyester resin, 10 parts of diphenylmethane diisocyanate, 6 parts of polyamide polyamine epichlorohydrin, 2 parts of benzoyl peroxide, and 1 part of N,N-dimethylaniline;

[0031] Heat polyester resin, diphenylmethane diisocyanate, polyamide polyamine epichlorohydrin, benzoyl peroxide and N,N-dimethylaniline until dissolved to obtain a wear-resistant coating solution;

[0032] The wear-resistant coating liquid is evenly coated on the outer surface of the base cloth layer, the thickness of the wear-resistant coating is 0.2 mm, and the wear-resistant coating is dried at 15° C. to obtain a wear-resistant blended fabric.

Embodiment 2

[0034] A preparation method of a wear-resistant blended fabric, the preparation method comprising the steps of:

[0035] By weight, get 8 parts of polyester fiber, 3 parts of polypropylene fiber;

[0036] Blending polyester fibers and polypropylene fibers to obtain a base fabric layer;

[0037] By weight, get 40 parts of polyester resin, 20 parts of diphenylmethane diisocyanate, 12 parts of polyamide polyamine epichlorohydrin, 2.5 parts of benzoyl peroxide, 2 parts of N,N-dimethylaniline;

[0038] Heat polyester resin, diphenylmethane diisocyanate, polyamide polyamine epichlorohydrin, benzoyl peroxide and N,N-dimethylaniline until dissolved to obtain a wear-resistant coating solution;

[0039] The wear-resistant coating liquid is evenly coated on the outer surface of the base fabric layer, the thickness of the wear-resistant coating is 0.15 mm, and the wear-resistant coating is dried at 15° C. to obtain a wear-resistant blended fabric.

Embodiment 3

[0041] A preparation method of a wear-resistant blended fabric, the preparation method comprising the steps of:

[0042] By weight, get 10 parts of polyester fiber, 2 parts of polypropylene fiber;

[0043] Blending polyester fibers and polypropylene fibers to obtain a base fabric layer;

[0044] By weight, get 30 parts of polyester resin, 25 parts of diphenylmethane diisocyanate, 15 parts of polyamide polyamine epichlorohydrin, 1.5 parts of benzoyl peroxide, 2.5 parts of N,N-dimethylaniline;

[0045] Heat polyester resin, diphenylmethane diisocyanate, polyamide polyamine epichlorohydrin, benzoyl peroxide and N,N-dimethylaniline until dissolved to obtain a wear-resistant coating solution;

[0046] The wear-resistant coating liquid is evenly coated on the outer surface of the base fabric layer, the thickness of the wear-resistant coating is 0.25 mm, and the wear-resistant coating is dried at 15° C. to obtain a wear-resistant blended fabric.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wear-resistant blended yarn weaved fabric belonging to the field of garment materials. The wear-resistant blended yarn weaved fabric comprises a base cloth layer and a wear-resistant coating, wherein the wear-resistant coating comprises polyester resin, methylene diphenyl diisocyanate, polyamide-polyamsne-epichlorohydrin, an initiator and an accelerant. The formula of the conventional wear-resistant coating is improved, so that the wear resistance of the prepared wear-resistant blended yarn weaved fabric is better than that of the conventional like product.

Description

technical field [0001] The invention relates to a wear-resistant blended fabric, which belongs to the field of clothing fabrics. Background technique [0002] Twill is divided into two types: coarse twill and fine twill. Denim uses cotton yarns above No. 32 (below 18 British counts) as warp and weft yarns; fine denim uses cotton yarns below No. 18 (above 32 British counts) as warp and weft yarns. There are white, bleached and variegated twill fabrics, which are often used as linings of uniforms, sportswear, sports shoes, emery cloth base fabrics and padding materials. The wide-loom bleached twill can be used as a quilt, and it can also be used as a bed sheet after printing. After electro-optical or calendering finishing, the plain and variegated fine twill fabric has a bright surface, which can be used as an umbrella cover and clothing folder. [0003] Nylon can be blended or pure spun into various medical and knitwear. Nylon filament is mostly used in knitting and silk ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/12D06N3/14D06N3/00
Inventor 苏文珊
Owner 大连率为环保科技有限公司