Anhydrous tubular metal hypophosphite and preparation method thereof

A technology of hypophosphite and hypophosphorous acid, which is applied in the direction of hypophosphorous acid and phosphorus oxyacid, can solve the problems of containing crystal water, irregular and uniform shape, etc., achieve good thermal stability, improve mechanical properties, and simple preparation method Effect

Active Publication Date: 2018-05-01
HEFEI UNIV
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved in the present invention is to overcome the defects of existing metal hypophosphite, such as crystal water, irregular and uniform appearance, etc., to provide an anhydrous tubular metal hypophosphite and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anhydrous tubular metal hypophosphite and preparation method thereof
  • Anhydrous tubular metal hypophosphite and preparation method thereof
  • Anhydrous tubular metal hypophosphite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 0.80 gram of manganese chloride, 0.53 gram of hypophosphorous acid and 0.15 gram of cetyltrimethylammonium bromide were dissolved in 60 milliliters of N,N-dimethylformamide and 5 milliliters of ethanol in the mixed solvent, then added In a 100 ml polytetrafluoroethylene reactor, heat up to 180°C, react for 24 hours, and finally filter and wash the obtained product, and the obtained solid powder is the anhydrous tubular manganese hypophosphite of the present invention.

[0020] figure 1 Infrared spectrum (FTIR) of the anhydrous tubular manganese hypophosphite prepared for Example 1. In the FTIR spectrum, 2921cm -1 and 2848cm -1 The absorption peak at corresponds to the C–H stretching vibration, 1626cm -1 The absorption peak at corresponds to the stretching vibration of C=O, indicating that the resulting product contains a small amount of N,N-dimethylformamide; 1382cm -1 and 1056cm -1 The absorption peaks at correspond to the stretching vibrations of P=O and P–O resp...

Embodiment 2

[0024] 0.47 gram of sodium chloride, 0.53 gram of hypophosphorous acid and 0.58 gram of hexadecyltrimethylammonium bromide were dissolved in a mixed solvent of 50 milliliters of methylene chloride and 10 milliliters of ethanol, and then added to 100 milliliters of polytetrafluoroethylene In the reaction kettle, the temperature is raised to 200°C, and the reaction is carried out for 48 hours. Finally, the obtained product is filtered and washed, and the obtained solid powder is the anhydrous tubular sodium hypophosphite of the present invention.

Embodiment 3

[0026] 0.97 gram of aluminum chloride, 0.80 gram of hypophosphorous acid and 0.68 gram of dodecyl dimethyl benzyl ammonium chloride were dissolved in a mixed solvent of 55 milliliters of tetrahydrofuran and 15 milliliters of ethanol, and then added to 100 milliliters of polytetrafluoroethylene In the reaction kettle, the temperature is raised to 140° C., and the reaction is carried out for 12 hours. Finally, the obtained product is filtered and washed, and the obtained solid powder is the anhydrous tubular aluminum hypophosphite of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses anhydrous tubular metal hypophosphite and a preparation method thereof, and belongs to the technical fields of halogen-free flame retardants and preparation thereof. A molecular formula of the anhydrous tubular metal hypophosphite is M(H2PO2)n, wherein M is any one of Na, K, Ca, Mg, Al, Zn, Mn, Fe, La or Ce; n is 1, 2 or 3. The preparation method comprises the following steps of firstly dissolving a metal chloride, hypophosphorous acid and a surfactant into an organic solvent, then adding into a polytetrafluoroethylene reaction kettle, raising a temperature, reacting, and finally filtering and washing an obtained product. The anhydrous tubular metal hypophosphite provided by the invention has good heat stability, further, does not contain water, cannot cause the degradation of a macromolecular material in a processing process of modifying the macromolecular material, is of a tubular structure, and not only can be used for improving the flame retarding performance of the macromolecular material, but also can be used for ameliorating the mechanical performance of the macromolecular material; the preparation method is simple, and the anhydrous tubular metal hypophosphite is applicable to most macromolecular material, and has a wide market application prospect.

Description

technical field [0001] The invention relates to an anhydrous tubular metal hypophosphite and a preparation method thereof, belonging to the technical field of halogen-free flame retardants and preparation thereof. Background technique [0002] Polymer materials include plastics, rubber, fibers, films, adhesives, and coatings. Among them, plastics, synthetic fibers and synthetic rubber, known as the three major synthetic materials of modern polymers, have become important materials that are indispensable for national economic construction and people's daily life. [0003] However, most polymer materials are flammable, and polymer materials will generate a lot of smoke and toxic gases during heating or combustion, which greatly restricts their application fields. At present, the flame retardants used for polymer materials are mainly halogen-containing systems. Although the flame retardant efficiency of halogen-containing flame retardants is very high, due to the large amount ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B25/165C08K7/00
CPCC01B25/165C01P2002/72C01P2002/82C01P2004/03C01P2004/10C08K7/00C08K2201/003C08K2201/004
Inventor 杨伟陈浩杨雯杰王黎丽鲁红典
Owner HEFEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap