Heat treatment process of drill rod pipe body

A technology of drill pipe and process, which is applied in the field of heat treatment process of pipe body, can solve the problems that the tensile properties of drill pipe body cannot meet the requirements, and it is difficult to meet the technical requirements of V150 steel grade drill pipe, etc., and achieve simple heat treatment steps, Good impact performance and reasonable process parameters

Inactive Publication Date: 2018-06-12
QINGDAO XIAOMIXING ELECTRONICS TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the heat treatment process disclosed in China is difficult to meet the technical requirements of V150 steel grade drill pipe, especially the tens

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat treatment process of drill rod pipe body

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] The invention will be further described in detail below through specific embodiments.

[0020] Using a company's drill pipe body, its chemical composition is, C: 0.26, Cr: 0.98, Mo: 0.64, V: 0.005, Si: 0.22, Mn: 0.75, Cu: 0.03, S: 0.001, P: 0.008, The remainder is Fe, and the unit is mass percent. Heat treatment as follows:

[0021] ①Quenching

[0022] a. The drill pipe body is transported to a step-by-step quenching furnace heated to 910°C, and kept for 60 minutes;

[0023] b. After the drill pipe body is released from the furnace, enter the quenching liquid at 23°C within 15 seconds. The quenching liquid is tap water, and rotates at a speed of 88 rpm. The quenching time is 40 seconds, and the temperature of the quenching liquid is adjusted by the cooling tower. , The drill pipe body rotates at a certain rate for rapid and uniform quenching to form a fine and uniform grain structure.

[0024] ②Tempering

[0025] Within 1 hour of quenching, the drill pipe body is t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat treatment process of a drill rod pipe body. The heat treatment process of the drill rod pipe body comprises quenching and tempering heat treatment according to the following steps and process parameters: (1) quenching: (a) the drill rod pipe body is conveyed into a stepper quenching furnace which is heated to 880-930 DEG C, and is insulated by 40-60 minutes; and (b)after the drill rod pipe body is discharged from the furnace, the drill rod pipe body enters quenching liquid of 10-30 DEG C within 15 seconds, and the quenching time is not shorter than 30 seconds; and (2) tempering: the drill rod pipe body is conveyed into a stepper tempering furnace which is heated to 560-590 DEG C, is insulated by 60-85 seconds, is discharged from the furnace, and is naturallycooled to the room temperature. As the heat treatment process of the drill rod pipe body is adopted, the impact performance of a drill rod is excellent, and exceeds a standard value of a V150 steel stage by above 30%; the mechanical indexes, such as strength and ductility of the heated drill rod pipe body meet the requirements of the V150 steel stage, and the pass percent is above 98%; and the heat treatment process of the drill rod pipe body is reasonable in heat treatment operation step and process parameter.

Description

technical field [0001] The invention relates to a heat treatment process for a pipe body, in particular to a quenching and tempering process for manufacturing a drill pipe body with relatively high mechanical properties, so that it can reach the standard of V150 steel grade. Background technique [0002] Petroleum drill pipe is the main tool for oil field drilling, and its structure includes the drill pipe body and the drill pipe joints at both ends of the drill pipe body. In the process of oil and gas extraction and refining, the drill pipe body must be able to withstand huge internal and external pressure, twisting, bending and vibration. [0003] With the continuous development of the petroleum industry, more and more deep wells and ultra-deep wells have been developed, which puts forward higher and higher requirements for drill pipes. At present, the highest strength of API series drill pipes is S135 steel grade, but with the increase of drilling depth, the strength req...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D9/08C21D1/18C22C38/22C22C38/24C22C38/02C22C38/04C22C38/20
CPCC21D9/085C21D1/18C22C38/02C22C38/04C22C38/20C22C38/22C22C38/24
Inventor 曲立辉
Owner QINGDAO XIAOMIXING ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap