Method for recycling beech waste wood chips

A technology for wood chips and beech wood, applied in the field of wood chip recycling, can solve the problems of unsatisfactory combustion heat, low utilization rate, waste of resources, etc., and achieve the effect of improving the value of recycling and utilization, reducing the amount of consumption, and reducing the waste of resources.

Inactive Publication Date: 2018-08-14
贵港市万升木业有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the increase in the use of beech, a lot of beech leftovers, shavings, waste wood chips, etc. are produced in the process of processing. Because the value of beech is relatively high, these wastes are also very valuable resources. The beech waste is directly discarded...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for recycling beech waste wood chips

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A method for recycling beech waste sawdust, said method is to collect sawdust, shavings, and leftovers produced during beech processing, and then make sawdust, use a sieve to screen out even fineness, length 5-10mm sawdust, Obtain beech waste sawdust, and then use the beech waste sawdust as raw material to make decorative boards; the production process includes the following steps:

[0040] (1) Take the following raw materials by weight: 95 parts of beech waste sawdust, 7 parts of epoxy resin, 21 parts of 2000 mesh quartz powder, 18 parts of 800 mesh quartz powder, 11 parts of 40 mesh quartz sand, 0.7 parts of salicylate part, 0.8 part of nano-zinc oxide, 0.09 part of coupling agent, and 0.08 part of curing agent;

[0041] The epoxy resin is composed of brominated diphenol-based propane epoxy resin and o-cresol type novolac epoxy resin of the same quality.

[0042] The salicylate is composed of phenyl salicylate and p-octylphenyl salicylate in a mass ratio of 1:2.5.

...

Embodiment 2

[0050] A method for recycling beech waste sawdust, said method is to collect sawdust, wood shavings and leftovers produced during beech processing, then make sawdust, use a sieve to screen the sawdust with uniform fineness and a length of 15-20mm, Obtain beech waste sawdust, and then use the beech waste sawdust as raw material to make decorative boards; the production process includes the following steps:

[0051] (1) Take the following raw materials by weight: 90 parts of beech waste sawdust, 5 parts of epoxy resin, 18 parts of 2000 mesh quartz powder, 15 parts of 800 mesh quartz powder, 9 parts of 40 mesh quartz sand, 0.5 parts of salicylate part, 0.5 part of nano-zinc oxide, 0.07 part of coupling agent, and 0.05 part of curing agent;

[0052] The epoxy resin is brominated diphenolic propane epoxy resin; the salicylate is composed of phenyl salicylate and p-octylphenyl salicylate in a mass ratio of 1:2; the coupling The agent is γ-aminopropyltrimethoxysilane; the curing age...

Embodiment 3

[0058] A method for recycling beech waste sawdust, said method is to collect sawdust, shavings, and leftovers produced during beech processing, and then make sawdust, use a sieve to screen out even fineness, length 5-10mm sawdust, Obtain beech waste sawdust, and then use the beech waste sawdust as raw material to make decorative boards; the production process includes the following steps:

[0059] (1) Take the following raw materials by weight: 100 parts of beech waste sawdust, 8 parts of epoxy resin, 25 parts of 2000 mesh quartz powder, 22 parts of 800 mesh quartz powder, 15 parts of 40 mesh quartz sand, 1 part of salicylate 1 part, 1 part of nano zinc oxide, 0.12 part of coupling agent, 0.1 part of curing agent;

[0060] The epoxy resin is o-cresol novolac epoxy resin; the salicylate is composed of phenyl salicylate and p-octylphenyl salicylate with a mass ratio of 1:3; the coupling agent It is diethylamino-substituted methyl triethoxysilane; the curing agent is tert-butyl ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for recycling beech waste wood chips. The method comprises the following steps that the beech waste wood chips are produced into a decorative board after being collected; (1), the following raw materials of the beech waste wood chips, epoxy resin, 2,000-mesh quartz powder, 800-mesh quartz powder, 40-mesh quartz sand, salicylate, nano zinc oxide, a coupling agent and a curing agent are weighed; (2), the raw materials are evenly mixed; (3), the mixture is loaded into a mold, and vibrating and pressing forming are carried out; (4), curing is carried out; and (5),grinding and polishing are carried out. By the adoption of the method, the beech waste wood chips can be recycled, resources are fully used, and the produced decorative board has the beneficial effects of being high in practicability, durable in use, high in anti-aging capability, good in toughness, good in sound insulation effect and the like and has the natural feeling of logs and good appearance.

Description

technical field [0001] The invention relates to a method for recycling wood chips, in particular to a method for recycling waste beech wood chips. Background technique [0002] Beech, also written as "椐木" or "椇木", is produced in the south of my country. The north does not know this name, but calls this wood South Elm. Although it is not a luxurious wood, it is widely used in traditional Ming and Qing furniture, especially in folk. This kind of beech furniture is mostly Ming style, and its shape and production techniques are basically the same as those of hardwood furniture such as huanghuali. It has considerable artistic and historical value. Beech wood is heavy, strong, impact-resistant, easy to bend under steam, clear texture, uniform wood texture, soft and smooth tones, can be made into shapes, and has good nail holding performance. The hardness of beech wood is strong, comparable to mahogany. The reason why beech wood is called "declining nobleman" is that after beech ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27G3/00
CPCB27G3/00
Inventor 杨静
Owner 贵港市万升木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap