Wear-resistant environment-friendly glass powder used in paint and preparation method of glass powder

A kind of glass powder, environmental protection technology, applied in the direction of fireproof coatings, etc., can solve the problems such as not very environmental protection, paint wear resistance enhancement effect is not very good, human health hazards, etc., to achieve simple process, good application prospects, and environmentally friendly materials Effect

Inactive Publication Date: 2018-09-14
合肥市晨雷思建筑材料科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing glass powder is not very effective in enhancing the wear resistance of paint, and it is not very environmentally friendly, and will cause certain harm to human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The wear-resistant and environment-friendly glass powder used in a kind of paint of the present embodiment comprises the raw material of following percentage by weight:

[0031] SiO 2 26%, Al 2 o 3 12%, PbF 2 16%, CaO14%, Fe 2 o 3 6%, CuO2%, Ni2%, Cu2%, B1%, Re1%, NaN1%.

[0032] The glass frit of present embodiment also contains Sb 2 o 3 , and its weight percentage is 4%.

[0033] The glass frit of this embodiment also contains Sr, which is 2% by weight.

[0034] The glass frit of this embodiment also contains fillers, and the percentage by weight of the fillers is 23%.

[0035] The filler in this embodiment is a mixture of mica powder and carbide slag powder in a ratio of 3:2 by weight.

[0036] The preparation method of the wear-resistant and environment-friendly glass powder used in a kind of paint of the present embodiment comprises the following steps:

[0037] Step 1, weighing each component raw material as required;

[0038] Step two, the SiO 2 、Al ...

Embodiment 2

[0041] The wear-resistant and environment-friendly glass powder used in a kind of paint of the present embodiment comprises the raw material of following percentage by weight:

[0042] SiO 2 30%, Al 2 o 3 16%, PbF 2 20%, CaO18%, Fe2 o 3 10%, CuO6%, Ni6%, Cu4%, B2%, Re3%, NaN3%.

[0043] The glass frit of present embodiment also contains Sb 2 o 3 , and its weight percentage is 8%.

[0044] The glass frit of this embodiment also contains Sr, which is 6% by weight.

[0045] The glass frit of this embodiment also contains fillers, and the percentage by weight of the fillers is 31%.

[0046] The filler in this embodiment is a mixture of mica powder and carbide slag powder in a ratio of 3:2 by weight.

[0047] The preparation method of the wear-resistant and environment-friendly glass powder used in a kind of paint of the present embodiment comprises the following steps:

[0048] Step 1, weighing each component raw material as required;

[0049] Step two, the SiO 2 、Al ...

Embodiment 3

[0052] The wear-resistant and environment-friendly glass powder used in a kind of paint of the present embodiment comprises the raw material of following percentage by weight:

[0053] SiO 2 28%, Al 2 o 3 14%, PbF 2 18%, CaO16%, Fe 2 o 3 8%, CuO4%, Ni4%, Cu3%, B1.5%, Re2%, NaN2%.

[0054] The glass frit of present embodiment also contains Sb 2 o 3 , and its weight percentage is 6%.

[0055] The glass frit of this embodiment also contains Sr, which is 4% by weight.

[0056] The glass frit of this embodiment also contains fillers, and the percentage by weight of the fillers is 23-31%.

[0057] The filler in this embodiment is a mixture of mica powder and carbide slag powder in a ratio of 3:2 by weight.

[0058] The preparation method of the wear-resistant and environment-friendly glass powder used in a kind of paint of the present embodiment comprises the following steps:

[0059] Step 1, weighing each component raw material as required;

[0060] Step two, the SiO 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses wear-resistant environment-friendly glass powder used in paint. The glass powder comprises the following raw materials in percentage by weight: 26-30% of SiO2, 12-16% of Al2O3,16-20% of PbF2, 14-18% of CaO, 6-10% of Fe2O3, 2-6% of CuO, 2-6 % of Ni, 2-4% of Cu, 1-2% of B, 1-3% of Re, and 1-3% of NaN. The invention aims to provide the wear-resistant environment-friendly glass powder used in the paint, and the glass powder improves the wear resistance of the paint, is an environment-friendly material, is pollution free, does not harm human health, and has a high use valueand a good application prospect.

Description

technical field [0001] The invention relates to the technical field of glass powder, in particular to a wear-resistant and environment-friendly glass powder used in paints and a preparation method thereof. Background technique [0002] Glass powder is a kind of inorganic cubic hard ultra-fine particle powder of Anmi Micro-Nano. The appearance is white powder. Raw materials such as high-temperature high-purity silica and alumina are used in the production, and then go through an ultra-clean production process to form a non-toxic Glass transparent powder with sequence structure, stable chemical properties, super weather-resistant powder material with acid and alkali resistance, chemical inertness and low expansion coefficient; it is a scratch-resistant and highly transparent powder material with small particle size, good dispersion and transparency High, good anti-settling effect; after surface improvement, it has good affinity and strong steric resistance, and can be easily d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More