Ultra-low temperature anti-penetration PVB interlayer film

An intermediate film and anti-penetration technology, which is applied in the direction of protective equipment, clothing, protective clothing, etc., to achieve good anti-penetration performance and improve international competitiveness

Inactive Publication Date: 2018-09-28
JIANGSU AOTIANLI NEW MATERIAL CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current market positioning pattern is very obvious. Foreign high-end PVB interlayers firmly occupy the high-end market, and domestic PVB interlayers can only rely on low prices to compete with each other in the middle and low-end markets.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-low temperature anti-penetration PVB interlayer film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0017] see figure 1 , in the embodiment of the present invention, a kind of ultra-low temperature anti-penetration PVB intermediate film, comprises intermediate film main body 1, the thickness of described intermediate film main body 1 is 0.6mm, adopts high-viscosity PVB resin, number average molecular weight exceeds 100000Da, acetalization rate The content is between 78% and 85%. The upper and lower surfaces of the intermediate film main body 1 have been fros...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
number average molecular weightaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a ultra-low temperature anti-penetration PVB interlayer film. The interlayer film comprises an interlayer film body, wherein the interlayer film body is made from high-viscosity PVB resin, a fiber reinforced layer is compounded in the interlayer film body, and a plurality of bulges are formed on the upper surface and lower surface of the fiber reinforced layer; and a compound plasticizer which is triethylene glycol diisooctanoate is compounded in the interlayer film body. Compared with a conventional product, the interlayer film has the characteristic of better anti-penetration performance, can be applied to manufacture of interlayer safety glass and meet high-level safety requirements for strong penetration resistance, and can be widely applied to the fields of front and rear windshields of an automobile, bulletproof glass and the like, so that technological progress of a domestic PVB interlayer film is facilitated, the international competitiveness of the domestic PVB interlayer film is improved, and a positive promoting effect on the competitiveness and brand building of enterprises is achieved.

Description

technical field [0001] The invention relates to an ultra-low temperature anti-penetration PVB intermediate film. Background technique [0002] Polyvinyl butyral (PVB) film is the most widely used material in architectural laminated glass and automobile laminated windshield glass. It has good light transmission, adhesion, toughness and optical properties. The PVB interlayer film can firmly bond the two outer layers of glass together, making the laminated glass have strong impact resistance and energy-absorbing buffering functions, providing protection for the personal safety of users. [0003] The total production capacity of PVB interlayer film in the world is insufficient, mainly because the production technology requirements of PVB interlayer film are relatively high, only a few countries can produce independently, and the major manufacturers with advanced PVB interlayer film production technology strictly keep their technology secret, which is even more serious The unbal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/02B32B15/082B32B27/22B32B27/30B32B3/30
CPCB32B3/30B32B15/02B32B27/12B32B27/22B32B27/304B32B2262/103B32B2571/02B32B2605/08
Inventor 潘日坚
Owner JIANGSU AOTIANLI NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap