958 alloy for die casting and red silver jewelry and processing technology thereof

A processing technology and alloy technology, applied in the field of alloys, can solve problems such as vulcanization blackening, acceleration, and lack of corrosion resistance, and achieve the effects of small gas absorption, small shrinkage cavity formation tendency, and excellent filling performance

Inactive Publication Date: 2018-11-13
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of alloy does not have sufficient corrosion resistance to discolor after use, or the vulcanization and blackening are accelerated due to wear and tear out of the base alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A 958 alloy for die-casting red silver jewelry and its processing technology. In terms of weight percentage, the composition of the alloy is C:0.2wt.%, B:0.5wt.%, Ba:1.2wt.%, Ti:0.4wt.%, Mo:0.8wt.%, Sb:0.3wt.%. , Ag: 95.0wt.%, the balance is copper. The above-mentioned 958 alloy for red silver jewellery, which is used for die-casting, and its processing technology include the following steps: adding the above proportioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; Minutes, stir evenly by high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1200 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. Roll the obtained ingot at room temperature, and the amount of rolling in each pass is 20-30%; after every two rollings, the intermediate annealing temperature is 520 degrees, and the temperat...

Embodiment 2

[0021] A 958 alloy for die-casting red silver jewelry and its processing technology. In terms of weight percentage, the composition of the alloy is C:0.3wt.%, B:0.6wt.%, Ba:1.4wt.%, Ti:0.8wt.%, Mo:1.2wt.%, Sb:0.5wt.%. , Ag: 96.0wt.%, the balance is copper. The above-mentioned 958 alloy for red silver jewellery, which is used for die-casting, and its processing technology include the following steps: adding the above proportioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; Minutes, stir evenly by high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1200 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. Roll the obtained ingot at room temperature, and the amount of rolling in each pass is 20-30%; after every two rollings, the intermediate annealing temperature is 520 degrees, and the temperat...

Embodiment 3

[0024] A 958 alloy for die-casting red silver jewelry and its processing technology. In terms of weight percentage, the composition of the alloy is C:0.2wt.%, B:0.5wt.%, Ba:1.3wt.%, Ti:0.5wt.%, Mo:0.9wt.%, Sb:0.4wt.%. , Ag: 95.0.0wt.%, the balance is copper. The above-mentioned 958 alloy for red silver jewellery, which is used for die-casting, and its processing technology include the following steps: adding the above proportioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; Minutes, stir evenly by high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1200 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. Roll the obtained ingot at room temperature, and the amount of rolling in each pass is 20-30%; after every two rollings, the intermediate annealing temperature is 520 degrees, and the temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a 958 alloy for die casting and red silver jewelry and a processing technology thereof. The alloy comprises, by weight, 0.2-0.3% of C, 0.5-0.6% of B, 1.2-1.4% of Ba, 0.4-0.8% of Ti, 0.8-1.2 % of Mo, 0.3-0.5% of Sb, 95-96% of Ag, and the balance copper. A new material with red appearance is provided for the 958 silver alloy for the jewelry in China, and the material has an excellent die casting characteristic. The implementation and industrialization of the material can effectively promote the demands of product updating and industry upgrading in the jewelry industry ofChina, and rich economic gains and social benefits are obtained when the industry problems are solved.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a silver alloy. Background technique [0002] Silver has a white luster and is located between gold and copper on the periodic table. Although it is chemically less inert among noble metals, it is far more stable than copper and aluminum, and will not oxidize even when heated in air. The earliest uses of silver were decorations and currency, and later as tableware. With the development of industry, other uses have gradually been developed, such as: electrical contactors, brazing alloys, catalysts and photographic materials. China is a multi-ethnic country, and there has always been a large market for ethnic minority silver jewelry. With the improvement of people's living standards, silver jewelry and silverware will enter the general family more and faster. [0003] Because silver is cheap compared to gold, its soft texture can be processed into various jewelry accessories, ta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C5/06C22C5/08C22C1/02C22F1/14C22F1/02C23C8/12
CPCC22C5/06C22C1/02C22C5/08C22F1/02C22F1/14C23C8/12
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com