Preparation method of high-wear-resistance plastic piece

A kind of plastic parts, high wear-resistant technology, applied in the field of plastics, can solve the problems of easy to be worn, scratched, increased weight, affecting performance, etc., to achieve not easy to scratch, improve wear resistance, improve performance and service life Effect

Inactive Publication Date: 2018-11-20
桐乡市富鸿塑业股份有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, the wear resistance of plastic is limited, so metal parts are used on the cover plate at the bottom of the vacuum cleaner to increase its wear resistance, but at the same time it also increases its weight, which affects the use performance
However, if plastic is used, it is easy to be worn, scratched, etc. during repeated use, which seriously affects the service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] The preparation method of a high-wear-resistant plastic part described in this example, ingredients, and the following components in parts by mass are prepared: 20 parts of ABS, 15 parts of polyamide, 13 parts of polycarbonate, 8 parts of silica lime, polyvinyl chloride 12 parts of resin, 2 parts of rubber oil, 1 part of 1,3-dimethylol-5,5-dimethylhydantoin, 2 parts of octyl stearate; Mix thoroughly and evenly, and transport to the extruder, where the temperatures of the first zone, second zone, third zone, fourth zone and fifth zone of the extruder are 80°C, 90°C, 95°C, 95°C, 100°C, 110°C respectively , extruded into granules through an extruder, then heat up the granules to 180°C to melt, pour into a mold of corresponding shape, keep the temperature at 170°C, pressure 2MPa, keep for 0.3min, then quickly cool to room temperature, and take it out of the mold .

Embodiment 2

[0011] The preparation method of a high wear-resistant plastic part described in this example, the ingredients, the preparation of the following components in parts by mass: 30 parts of ABS, 18 parts of polyamide, 16 parts of polycarbonate, 10 parts of silica lime, polyvinyl chloride 45 parts of resin, 6 parts of rubber oil, 5 parts of 1,3-dimethylol-5,5-dimethylhydantoin, 4 parts of octyl stearate; Mix thoroughly and evenly, and transport to the extruder, where the temperatures of the first zone, second zone, third zone, fourth zone and fifth zone of the extruder are 80°C, 90°C, 95°C, 95°C, 100°C, 110°C respectively , extruded into granules through an extruder, then heat up the granules to 180°C to melt, pour into a mold of corresponding shape, keep the temperature at 170°C, pressure 2MPa, keep for 0.3min, then quickly cool to room temperature, and take it out of the mold .

Embodiment 3

[0013] The preparation method of a high wear-resistant plastic part described in this example, the ingredients, the preparation of the following components in parts by mass: 25 parts of ABS, 16 parts of polyamide, 14 parts of polycarbonate, 9 parts of silica lime, polyvinyl chloride 33 parts of resin, 5 parts of rubber oil, 3 parts of 1,3-dimethylol-5,5-dimethylhydantoin, 3 parts of octyl stearate; Mix thoroughly and evenly, and transport to the extruder, where the temperatures of the first zone, second zone, third zone, fourth zone and fifth zone of the extruder are 80°C, 90°C, 95°C, 95°C, 100°C, 110°C respectively , extruded into granules through an extruder, then heat up the granules to 180°C to melt, pour into a mold of corresponding shape, keep the temperature at 170°C, pressure 2MPa, keep for 0.3min, then quickly cool to room temperature, and take it out of the mold .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of plastic, in particular to a preparation method of a high-wear-resistance plastic piece. The preparation method comprises the following steps: preparingthe following components in parts by mass: 20 to 30 parts of ABS, 15 to 18 parts of polyamide, 13 to 16 parts of polycarbonate, 6 to 10 parts of silicon lime, 12 to 45 parts of polyvinyl chloride resin, 2 to 6 parts of rubber oil, 1 to 5 parts of 1,3-dihydroxy methyl-5,5-dimethyl glycolylurea and 2 to 4 parts of ethylhexyl stearate; forming: mixing the prepared components in a mixer completely anduniformly, conveying to an extruding machine, extruding particles by using the extruding machine, heating the particles to 180 DEG C to melt, injecting into a mode with the corresponding shape, maintaining the temperature to be 170 DEG C and the pressure to be 2 MPa for 0.3 minute, rapidly cooling to normal temperature and taking out of the mold. According to the preparation method of the high-wear-resistance plastic piece and through reasonable formula design and process design, the wear resistance of the plastic can be improved, so that the high-wear-resistance plastic piece is suitable forbeing used on a cover plate at the bottom of a dust remover, is not liable to scratch and wear in the repeated moving friction process, improves the use property and prolongs the service life.

Description

technical field [0001] The invention relates to the technical field of plastics, in particular to a method for preparing high wear-resistant plastic parts. Background technique [0002] In the prior art, the wear resistance of plastic is limited, so metal parts are used on the cover plate at the bottom of the vacuum cleaner to increase its wear resistance, but at the same time its weight is also increased, which affects the use performance. However, if plastic is used, it is easy to be worn, scratched, etc. during repeated use, which seriously affects the service life. Contents of the invention [0003] The object of the present invention is to provide a method for preparing a high wear-resistant plastic part with high wear resistance and light weight in order to solve the above-mentioned technical deficiencies. [0004] In order to achieve the above-mentioned purpose, the preparation method of a kind of highly wear-resistant plastic part designed by the present invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L77/00C08L69/00C08L27/06C08L91/00C08K3/34C08K5/101
CPCC08L55/02C08L2205/035C08L77/00C08L69/00C08L27/06C08L91/00C08K3/34C08K5/101
Inventor 姚富林
Owner 桐乡市富鸿塑业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap