A kind of preparation method of alkali-resistant water-based metal exterior wall paint

An exterior wall coating and alkali-resistant technology, which is applied to non-metallic paints, anti-corrosion coatings, coatings, etc., can solve the problems of short service life and poor alkali resistance, and achieve long service life, excellent scrub resistance, low cost effect

Active Publication Date: 2022-05-13
ANHUI SUBANG ENERGY SAVING TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the exterior wall coatings prepared in the prior art can meet the above requirements, they have poor alkali resistance, resulting in a short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of alkali-resistant water-based metal exterior wall paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A preparation method of an alkali-resistant water-based metal exterior wall paint, comprising the following steps:

[0016] (1) In parts by weight, add 18 parts of cerium chloride and 12 parts of yttrium chloride to 190 parts of water, mix and stir evenly, heat it to 75°C, continue to add 36 parts of sodium erucate to it, mix and stir After uniform heat preservation treatment, the alkali-resistant additive is obtained;

[0017] (2) In parts by weight, 58 parts of pure acrylic emulsion, 26 parts of water, 0.1 part of polyglycerol monostearate, 2 parts of tripotassium citrate, 0.8 parts of calcium cyclamate, 8 parts of alkali-resistant Additives, 6 parts of metallic pigment, 0.6 part of wetting and dispersing agent, and 0.2 part of defoaming agent are mixed evenly, and then stirred continuously for 25 minutes to obtain a finished product, wherein the metallic pigment is water-based environmentally friendly copper gold powder.

[0018] Specifically, in the above step (1),...

Embodiment 2

[0022] A preparation method of an alkali-resistant water-based metal exterior wall paint, comprising the following steps:

[0023] (1) In parts by weight, add 20 parts of cerium chloride and 13 parts of yttrium chloride to 195 parts of water, mix and stir evenly, heat it to 80°C, continue to add 40 parts of sodium erucate to it, mix and stir After uniformity and heat preservation treatment, an alkali-resistant additive is obtained;

[0024] (2) In parts by weight, 63 parts of pure acrylic emulsion, 30 parts of water, 0.2 parts of polyglycerol monostearate, 3 parts of tripotassium citrate, 1.0 part of calcium cyclamate, 10 parts of alkali-resistant Additives, 8 parts of metallic pigments, 0.8 parts of wetting and dispersing agent, and 0.3 parts of defoaming agent are mixed evenly, and then stirred continuously for 30 minutes to obtain a finished product, wherein the metallic pigment is water-based environmentally friendly copper gold powder.

[0025] Specifically, in the above...

Embodiment 3

[0029] A preparation method of an alkali-resistant water-based metal exterior wall paint, comprising the following steps:

[0030] (1) In parts by weight, add 23 parts of cerium chloride and 15 parts of yttrium chloride to 200 parts of water, mix and stir evenly, heat it to 85°C, continue to add 42 parts of sodium erucate to it, mix and stir After uniformity and heat preservation treatment, an alkali-resistant additive is obtained;

[0031] (2) In parts by weight, 65 parts of pure acrylic emulsion, 32 parts of water, 0.3 parts of polyglycerol monostearate, 4 parts of tripotassium citrate, 1.2 parts of calcium cyclamate, 13 parts of alkali-resistant Additives, 10 parts of metallic pigment, 0.9 part of wetting and dispersing agent, and 0.5 part of defoamer are uniformly mixed, and then stirred continuously for 35 minutes to obtain a finished product, wherein the metallic pigment is water-based aluminum silver paste.

[0032] Specifically, in the above step (1), the time for hea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of an alkali-resistant water-based metal exterior wall coating, which comprises the following steps: (1) adding cerium chloride and yttrium chloride into water, mixing and stirring evenly, and heating it to 75-85°C Afterwards, continue to add sodium erucate to it, mix and stir evenly, and heat preservation treatment to obtain an alkali-resistant additive; (2) Pure acrylic emulsion, water, polyglycerol monostearate, tripotassium citrate, cyclohexyl Calcium sulfamate, alkali-resistant additives, metallic pigments, wetting and dispersing agents, and defoamers are uniformly mixed, and then stirred continuously to obtain finished products. The preparation method of an alkali-resistant water-based metal exterior wall paint provided by the present invention has wide sources of raw materials and low cost, and the prepared water-based metal exterior wall paint has good construction performance, no obstacles for two coats, water resistance, and scrubbing resistance Excellent performance, especially excellent alkali resistance and long service life.

Description

technical field [0001] The invention belongs to the technical field of exterior wall coatings, and in particular relates to a preparation method of an alkali-resistant water-based metal exterior wall coating. Background technique [0002] Exterior wall paint is used to paint the exterior walls of buildings, so the most important indicator is anti-ultraviolet radiation, which requires long-term exposure without discoloration. Some exterior wall coatings also require water resistance and self-cleaning properties. The paint film should be hard and smooth, and the dirt will fall off as soon as it is washed. Although the exterior wall coatings prepared in the prior art can meet the above requirements, they have poor alkali resistance, resulting in a short service life. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the present invention provides a preparation method of an alkali-resistant water-based metal exterior wall paint. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/04C09D5/08C09D5/38
CPCC09D133/04C09D5/08C09D5/38C08K2003/221C08K2003/0831C08K2003/085C08K2003/0812C08L71/02C08K3/16C08K3/22C08K5/098C08K3/08C08K13/02
Inventor 王永国
Owner ANHUI SUBANG ENERGY SAVING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap