Manufacturing method of al-mg-si alloy plate

A manufacturing method and alloy plate technology, applied in metal rolling and other directions, can solve the problems of low strength, poor thermal conductivity and electrical conductivity, etc., and achieve the effect of high processability

Active Publication Date: 2022-03-01
堺アルミ株式会社
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although pure aluminum alloys such as JIS1100, 1050, and 1070 have excellent thermal conductivity, they have low strength
The thermal conductivity and electrical conductivity of Al-Mg alloys (5000 series alloys) such as JIS5052 used as high-strength materials are significantly worse than pure aluminum alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of al-mg-si alloy plate
  • Manufacturing method of al-mg-si alloy plate
  • Manufacturing method of al-mg-si alloy plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0102] Examples and comparative examples of the present invention are shown below.

no. 1 Embodiment

[0104] This embodiment is an embodiment related to the invention according to claims 1-10.

[0105] Aluminum alloy cast slabs having different chemical compositions shown in Table 1 were obtained by the DC casting method.

Embodiment 1

[0107] The aluminum alloy casting slab of chemical composition number 1 in Table 1 was subjected to face cutting. Next, the face-cut alloy slab was homogenized at 560° C. for 5 hours in a heating furnace, and then heated before hot rolling at 540° C. for 4 hours at different temperatures in the same furnace. The slab heated at 540° C. before hot rolling was taken out from the heating furnace, and rough hot rolling was started. After the thickness of the alloy sheet in the rough hot rolling becomes 25 mm, the final pass of the rough hot rolling is carried out at an average cooling rate of 80° C. / min from the alloy sheet temperature 461° C. immediately before the start of the pass. An alloy plate having a rolling finish temperature of 243° C. and a thickness of 12 mm. In addition, in the final pass of rough hot rolling, forced cooling is performed, the alloy sheet is moved while rolling, and water is sprayed onto the alloy sheet from the top and bottom of the rolled alloy sheet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
surface temperatureaaaaaaaaaa
surface temperatureaaaaaaaaaa
Login to View More

Abstract

Provided is a method of manufacturing an Al-Mg-Si-based alloy sheet having high electrical conductivity, good workability, and high strength. In the method for producing an alloy sheet in which hot rolling and cold rolling are sequentially performed on an Al-Mg-Si alloy ingot, the surface temperature of the Al-Mg-Si alloy sheet immediately after hot rolling is set to 230° C. or lower, Heat treatment is performed at a temperature of not less than 200°C and less than 400°C after completion of hot rolling and before completion of cold rolling.

Description

technical field [0001] The present invention relates to a method for manufacturing an Al-Mg-Si alloy sheet, and more particularly to a method for manufacturing an Al-Mg-Si alloy sheet excellent in thermal conductivity, electrical conductivity, strength, and workability. Background technique [0002] Built into the chassis, metal base printed circuit board, and inner cover of products such as thin TVs, thin displays for personal computers, notebook computers, tablet personal computers, car navigation systems, portable navigation systems, smartphones, mobile phones, etc. Or, among materials for components to which a heating element is mounted, excellent thermal conductivity, strength, and workability for rapid heat dissipation are required. [0003] Although pure aluminum alloys such as JIS1100, 1050, and 1070 have excellent thermal conductivity, they have low strength. Al—Mg alloys (5000-series alloys) such as JIS 5052 used as high-strength materials are remarkably inferior ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/05B21B1/22B21B3/00C22C21/02C22C21/06C22F1/00
CPCB21B1/22B21B3/00C22C21/02C22C21/06C22F1/00C22F1/05
Inventor 西森秀树笼重真二谷口和章山之井智明
Owner 堺アルミ株式会社
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com