Method for producing al-mg-si alloy plate

A manufacturing method and alloy plate technology, applied in the direction of metal rolling, etc., can solve the problems of poor thermal conductivity and electrical conductivity, low strength, etc., and achieve the effects of improving electrical conductivity, increasing strength, and improving quenching effect.

Inactive Publication Date: 2018-10-23
SHOWA DENKO KK
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although pure aluminum alloys such as JIS1100, 1050, and 1070 have excellent thermal conductivity, they have low strength
The thermal conductivity and electrical conductivity of Al-Mg alloys (5000 series alloys) such as JIS5052 used as high-strength materials are significantly worse than pure aluminum alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing al-mg-si alloy plate
  • Method for producing al-mg-si alloy plate
  • Method for producing al-mg-si alloy plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0092] Examples and comparative examples of the present invention are shown below.

no. 1 Embodiment

[0094] This embodiment is an embodiment related to the inventions of claims 1-8.

[0095] Aluminum alloy cast slabs having different chemical compositions shown in Table 1 were obtained by the DC casting method.

Embodiment 1

[0097] The aluminum alloy casting slab of chemical composition number 1 in Table 1 was subjected to face cutting. Next, the face-cut alloy slab was homogenized at 560° C. for 6 hours in a heating furnace, and then heated before hot rolling at 540° C. for 4 hours in the same furnace while changing the temperature. The slab heated at 540° C. before hot rolling was taken out from the heating furnace, and rough hot rolling was started. After the thickness of the alloy sheet in the rough hot rolling becomes 25 mm, the final pass of the rough hot rolling is carried out at an average cooling rate of 80° C. / min from the alloy sheet temperature 461° C. immediately before the start of the pass. An alloy plate having a rolling finish temperature of 243° C. and a thickness of 12 mm. In addition, in the final pass of the rough hot rolling, forced cooling is performed, and the alloy sheet is moved while rolling, and the parts of the rolled alloy sheet are water-cooled by spraying water to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

Provided is a method for producing an Al-Mg-Si alloy plate that exhibits high conductivity and high strength. Thus, a method for producing an alloy plate by sequentially hot rolling and cold rolling an Al-Mg-Si alloy ingot, wherein the surface temperature of the Al-Mg-Si alloy plate immediately following completion of the hot rolling is 230DEG C or less.

Description

technical field [0001] The present invention relates to a method for manufacturing an Al-Mg-Si alloy sheet, and more particularly to a method for manufacturing an Al-Mg-Si alloy sheet excellent in thermal conductivity, electrical conductivity, and strength. Background technique [0002] Built into the chassis, metal base printed circuit board, and inner cover of products such as thin TVs, thin displays for personal computers, notebook computers, tablet personal computers, car navigation systems, portable navigation systems, smartphones, mobile phones, etc. Or, among materials of members to which a heating element is mounted, excellent thermal conductivity and strength for rapid heat dissipation are required. [0003] Although pure aluminum alloys such as JIS1100, 1050, and 1070 have excellent thermal conductivity, they have low strength. Al—Mg alloys (5000-series alloys) such as JIS 5052 used as high-strength materials are remarkably inferior in thermal conductivity and ele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22F1/05B21B3/00C22C21/02C22C21/06C22F1/00
Inventor 西森秀树笼重真二谷口和章山之井智明
Owner SHOWA DENKO KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com