Stockpot

A soup pot and pot body technology, which is applied to special materials for cooking utensils, cooking utensils, household utensils, etc., can solve the problems of low thermal diffusivity and thermal conductivity, large thermal expansion coefficient, and can only be heated by an open fire, and achieves thermal diffusivity. and high thermal conductivity, small thermal expansion coefficient, and the effect of inhibiting high temperature degradation

Inactive Publication Date: 2018-11-30
NINGBO BEEFIT KITCHENWARE
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Pot is an indispensable household appliance in people's daily life. In the prior art, it is generally made of cast iron, but it has the advantages of large weight, small heat resistance range, large thermal expansion coefficient, small thermal diffusivity and thermal conductivity. Disadvantages; there are also pots made of ceramics. Although porcelain pots have high thermal conductivity and small thermal expansion coefficient, their heat-resistant range is small, and they can only be heated with open flames and are easy to break; at the same time, there are so-called pots made of high borosilicate Health pot, although it has a low coefficient of thermal expansion, it is not sensitive to heat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of soup pot, described soup pot is made of graphite composite material pot body, one layer of non-stick layer is coated on the inner surface of pot, wherein the composition and content of described graphite composite material are as follows: glass fiber 2%, talcum powder 8%, aluminum powder 1.2%, titanium powder 0.4%, magnesium oxide 1.2%, silicon nitride 1.2%, calcium carbonate 2.2%, ceramic clay 40%, and the balance is graphite and unavoidable impurities.

[0016] The density of described graphite is 1.76g / cm 3 , the ash content of the graphite material is ≤0.1%, and the thermal expansion coefficient of graphite is 4.8×10 -6 / K, the thermal diffusivity of graphite is 87.5m^ 2 / s, the thermal conductivity of graphite is 130w / m·k.

[0017] The coating of the non-stick layer is composed of the following raw materials in parts by weight: 15 parts of polytetrafluoroethylene resin, 12 parts of acrylic latex, 15 parts of epoxy-based accelerator resin, 3 parts of car...

Embodiment 2

[0019] A soup pot, the pot body is made of graphite composite material, and a layer of non-stick layer is coated on the inner surface of the pot, wherein the composition and content of the graphite composite material are as follows: 1% glass fiber, talcum powder 10%, aluminum powder 0.3%, titanium powder 0.5%, magnesium oxide 0.5%, silicon nitride 2%, calcium carbonate 0.5%, ceramic clay 30%, and the balance is graphite and unavoidable impurities.

[0020] The density of described graphite is 1.72g / cm 3 , the ash content of the graphite material is ≤0.1%, and the thermal expansion coefficient of graphite is 4.8×10 -6 / K, the thermal diffusivity of graphite is 87.5m^ 2 / s, the thermal conductivity of graphite is 130w / m·k.

[0021] The coating of the non-stick layer is composed of the following raw materials in parts by weight: 20 parts of polytetrafluoroethylene resin, 5 parts of acrylic latex, 20 parts of epoxy-type accelerator resin, 0.5 part of carbon nanotube, 5 parts of ...

Embodiment 3

[0023] A kind of soup pot, described soup pot is made of graphite composite material pot body, one layer of non-stick layer is coated on the inner surface of pot, wherein the composition and content of described graphite composite material are as follows: glass fiber 3%, talcum powder 5%, aluminum powder 2%, titanium powder 0.1%, magnesium oxide 2%, silicon nitride 0.5%, calcium carbonate 3%, ceramic clay 35%, and the balance is graphite and unavoidable impurities.

[0024] The density of described graphite is 1.80g / cm 3 , the ash content of the graphite material is ≤0.1%, and the thermal expansion coefficient of graphite is 4.8×10 -6 / K, the thermal diffusivity of graphite is 87.5m^ 2 / s, the thermal conductivity of graphite is 130w / m·k.

[0025] The coating of the non-stick layer is composed of the following raw materials in parts by weight: 10 parts of polytetrafluoroethylene resin, 20 parts of acrylic latex, 10 parts of epoxy accelerator resin, 5 parts of carbon nanotube...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a stockpot, and belongs to the technical field of pots. According to the stockpot, a pot body is prepared by a graphite composite material, and a non-stick layer is coated to an internal surface of the pot. The graphite composite material comprises 1-3% of glass fibre, 5-10% of talcum powder, 0.3-2% of aluminum powder, 0.1-0.5% of titanium powder, 0.5-2% of magnesium oxide, 0.5-2% of silicon nitride, 0.5-3% of calcium carbonate and 30-50% of ceramic clay, the balance being graphite. The stockpot is prepared by the graphite composite material with reasonable compatibility. The prepared stockpot has light weight, a large heat-resisting range, a small thermal expansion coefficient, high thermal diffusivity and thermal conductivity and rapid heat transfer, andis heated uniformly. Furthermore, acrylic acid is added to the coating of the non-stick layer, so that the gap of molten resin particles can be tensioned by the capillary effect generated due to the fact that the surface coating is volatilized away when sintered to form a film, high-temperature degradation of a little PTFE is suppressed, and therefore yellow stain of the surface coating is reduced.

Description

technical field [0001] The invention relates to a soup pot, which belongs to the technical field of pots. Background technique [0002] Pot is an indispensable household appliance in people's daily life. In the prior art, it is generally made of cast iron, but it has the advantages of large weight, small heat resistance range, large thermal expansion coefficient, small thermal diffusivity and thermal conductivity. Disadvantages; there are also pots made of ceramics. Although porcelain pots have high thermal conductivity and small thermal expansion coefficient, their heat-resistant range is small, and they can only be heated with open flames and are easy to break; at the same time, there are so-called pots made of high borosilicate The health pot, although it has a low coefficient of thermal expansion, is not sensitive to heat. Contents of the invention [0003] The object of the present invention is to provide a low-density, high-thermal-conduction soup pot aiming at the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A47J27/00A47J36/02
CPCA47J27/00A47J36/025
Inventor 陈森康
Owner NINGBO BEEFIT KITCHENWARE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap