Composite plant fiber for processing mattress
A plant fiber, mattress technology, applied in the direction of plant fiber, improved hand-feeling fiber, fiber processing, etc., can solve the problems of poor combined textile performance, single function of plant fiber, and stay in the most basic utilization, so as to improve sustainable development. Development and environmental protection, fiber softness, and improved development and utilization effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] A composite plant fiber for mattress processing, which is made of the following components in parts by weight: 45 parts of moso bamboo, 25 parts of coconut shell, 15 parts of loofah, 10 parts of broom grass, 5 parts of activated carbon residue, and 0.5 part of sulfur; The preparation method comprises the following steps:
[0017] (1) Crush and cut moso bamboo, coconut shell, loofah, and broom grass to a length of 1-2 cm, put it into the cooking equipment, add a sodium hydroxide solution with a mass concentration of 1.5% to immerse the material, and the ratio of solid to liquid is 1 :3.5, set the cooking temperature to be 150°C, and the cooking time to be 2.0 hours;
[0018] (2) Take out the cooked material, wash it with clean water to remove the residual lye, use a roller compactor to process the boiled and softened material, comb it, wash it and air dry it to obtain a bunch of crude fiber, mix the crude fiber with activated carbon slag Send it into a fiber opener to b...
Embodiment 2
[0024] A composite plant fiber for mattress processing, which is made of the following components in parts by weight: 46 parts of moso bamboo, 30 parts of coconut shell, 18 parts of loofah, 12 parts of broom grass, 6 parts of activated carbon residue, and 0.6 part of sulfur; The preparation method comprises the following steps:
[0025] (1) Crush and cut moso bamboo, coconut shell, loofah, and broom grass to a length of 1-2 cm, put it into the cooking equipment, add a sodium hydroxide solution with a mass concentration of 1.6% to immerse the material, and the ratio of solid to liquid is 1 : 3.8, set the cooking temperature to be 155°C, and the cooking time to be 2.2 hours;
[0026] (2) Take out the cooked material, wash it with clean water to remove the residual lye, use a roller compactor to process the boiled and softened material, comb it, wash it and air dry it to obtain a bunch of crude fiber, mix the crude fiber with activated carbon slag Send it into a fiber opener to ...
Embodiment 3
[0032] A composite plant fiber for mattress processing, which is made of the following components in parts by weight: 48 parts of moso bamboo, 35 parts of coconut shell, 20 parts of loofah, 15 parts of broom grass, 8 parts of activated carbon residue, and 0.7 part of sulfur; The preparation method comprises the following steps:
[0033] (1) Crush and cut moso bamboo, coconut shell, loofah, and broom grass to a length of 1-2 cm, put it into the cooking equipment, add a sodium hydroxide solution with a mass concentration of 1.8% to immerse the material, and the ratio of solid to liquid is 1 :4.0, set the cooking temperature to 160°C, and the cooking time to 2.5 hours;
[0034] (2) Take out the cooked material, wash it with clean water to remove the residual lye, use a roller compactor to process the boiled and softened material, comb it, wash it and air dry it to obtain a bunch of crude fiber, mix the crude fiber with activated carbon slag Send it into a fiber opener to dispers...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |