Polyvinyl chloride (PVC) impregnating solution for copper bar insulation sheaths, and impregnation processing technology of PVC impregnating solution

A processing technology and impregnating liquid technology, which is applied in the field of PVC impregnating liquid for copper bar insulation sheath and its impregnating processing technology, to achieve the effects of cost saving, outstanding high and low temperature resistance, and solving insulation protection problems

Active Publication Date: 2018-12-21
佛山市方普防护技术有限公司 +1
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the defects and deficiencies in the prior art, the present invention aims to provide a PVC impregnating liquid for copper bar insulation sheath and its impregnating process, so as to solve the insulation protection problem of copper bar and prolong the service life of copper bar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyvinyl chloride (PVC) impregnating solution for copper bar insulation sheaths, and impregnation processing technology of PVC impregnating solution
  • Polyvinyl chloride (PVC) impregnating solution for copper bar insulation sheaths, and impregnation processing technology of PVC impregnating solution
  • Polyvinyl chloride (PVC) impregnating solution for copper bar insulation sheaths, and impregnation processing technology of PVC impregnating solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] In this embodiment, the components of the PVC impregnation solution for the insulating sheath of copper bars are composed as follows in parts by mass:

[0025]

[0026] The above raw materials are evenly mixed according to the proportion, and then the PVC impregnating liquid for copper bar insulation sheath can be prepared.

[0027] In the present embodiment, the dipping process of the PVC dipping solution for the insulating sheath of the copper row is as follows:

[0028] 1. Fix the copper bar on the fixture after protective bandaging treatment, start the automatic cycle of the machine, and preheat for 300s at the furnace temperature of 280°C;

[0029] 2. Immerse the preheated copper bar into the PVC dipping solution prepared in this example, so that the dipping solution evenly wraps the copper bar; the copper bar first drops by 30mm at a speed of 350mm / min, and then drops by 35mm at a speed of 100mm / min. The time is 15s; then the copper bar rises by 30mm at a spee...

Embodiment 2

[0033] In this embodiment, the components of the PVC impregnation solution for the insulating sheath of copper bars are composed as follows in parts by mass:

[0034]

[0035]

[0036] The above raw materials are evenly mixed according to the proportion, and then the PVC impregnating liquid for copper bar insulation sheath can be prepared.

[0037] In the present embodiment, the dipping process of the PVC dipping solution for the insulating sheath of the copper row is as follows:

[0038] 1. Fix the copper bar on the fixture after protective bandaging treatment, start the automatic cycle of the machine, and preheat at the furnace temperature of 300 ℃ for 260s;

[0039] 2. Immerse the preheated copper bars in the PVC impregnating solution prepared in this example, so that the dipping solution evenly wraps the copper bars; The time is 10s; then the copper bar rises by 35mm at a speed of 90mm / min, and then rises by 50mm at a speed of 150mm / min;

[0040] 3. Bake the copper...

Embodiment 3

[0043] In this embodiment, the components of the PVC impregnation solution for the insulating sheath of copper bars are composed as follows in parts by mass:

[0044]

[0045] The above raw materials are evenly mixed according to the proportion, and then the PVC impregnating liquid for copper bar insulation sheath can be prepared.

[0046] In the present embodiment, the dipping process of the PVC dipping solution for the insulating sheath of the copper row is as follows:

[0047] 1. Fix the copper bar on the fixture after protective bandaging treatment, start the automatic cycle of the machine, and preheat at the furnace temperature of 420 ℃ for 200s;

[0048] 2. Immerse the preheated copper bars in the PVC impregnating solution prepared in this example, so that the dipping solution evenly wraps the copper bars; The time is 5s; then the copper bar rises by 35mm at a speed of 90mm / min, and then rises by 50mm at a speed of 150mm / min;

[0049] 3. Bake the copper bar treated ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Shore hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyvinyl chloride (PVC) impregnating solution for copper bar insulation sheaths, and an impregnation processing technology of the PVC impregnating solution. The PVC impregnating solution is prepared by mixing PVC resin, a stabilizing agent, a flame retardant, a compound plasticizer, a viscosity reducer and filler; after copper bars are impregnated and cured by using thePVC impregnating solution, the PVC copper bar insulation sheaths can be obtained. The PVC copper bar insulation sheaths are excellent in insulating property, high-temperature-resistant, good in flame-retardant property and long in service life.

Description

technical field [0001] The invention relates to a method for insulating a copper bar, in particular to a PVC dipping liquid for a copper bar insulating sheath and a dipping process thereof. Background technique [0002] Copper bar insulation treatment methods mainly include epoxy resin spraying (dipping powder), heat shrinkable sleeve, encapsulation (injection molding), etc. Epoxy resin spraying (dipping powder) is to place the preheated copper bar in the fluidized bed of epoxy encapsulation material, and apply epoxy encapsulation material to the surface of the copper bar. This kind of insulating sheath is brittle and is mostly used In a static environment, when used on a car, due to shaking, it is easy to cause the envelope to crack and fall off in pieces; the insulation sheath of the heat shrinkable sleeve cannot meet the complex shape of the copper bar, and it is easy to deform and accumulate when the temperature is slightly higher , and poor weather resistance, easy to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/00C08K13/02C08K5/521C08K3/26C08K3/34
CPCC08K3/26C08K3/34C08K5/521C08K13/02C08K2003/265C08L27/06C08L2201/02C08L2201/08C08L2203/20C08L91/00
Inventor 方松喜苏华武黎先梁杨绪锋吴峰
Owner 佛山市方普防护技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com