Glaze for achieving silk glazed surface effect on tile surface, preparation method and tile

A ceramic tile and glaze technology, applied in the field of ceramic tile glaze, can solve the problem that the surface of the ceramic tile cannot show silk effect, etc., and achieve the effects of low equipment requirements, simple method and good wear resistance.

Inactive Publication Date: 2019-01-22
GUANGDONG SANSHUI TANDH GLAZE CO LTD
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the deficiencies in the prior art above, the purpose of the present invention is to provide a glaze for ceramic tiles with a silk glaze effect and a preparation method and ceramic tiles, aiming to solve the problem that the surface of ceramic tiles fired with existing glazes cannot exhibit silk effects question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of glaze material with silk glaze effect for ceramic tile surface, wherein, the raw material includes the following components by weight components: including the following components: 5 parts of mineral materials, 12 parts of limestone, 2 parts of dolomite, 4 parts of wollastonite, 5 parts of barium carbonate, 2 parts of calcined talc, 4 parts of feldspar, 4 parts of nepheline, 7 parts of magnesium oxide, 14 parts of barium oxide, 3 parts of aluminum oxide, 30 parts of silicon dioxide, 11 parts of solvent.

[0026] Its raw material components also include 5 parts of sodium dioxide.

[0027] Its raw material components also include 4 parts of potassium oxide.

[0028] Its raw material components also include 6 parts of calcium oxide.

[0029] Its raw material components also include 4 parts of zinc oxide.

[0030] A method for preparing a glaze with a silk glaze effect on the surface of ceramic tiles, which includes the following steps: adding each raw materia...

Embodiment 2

[0034] A kind of glaze material with a silk glaze effect on the surface of tiles, the raw materials include the following components by weight: 3 parts of mineral materials, 15 parts of limestone, 1 part of dolomite, 3 parts of wollastonite, carbonic acid 4 parts of barium, 3 parts of calcined talc, 2 parts of feldspar, 3 parts of nepheline, 5 parts of magnesium oxide, 9 parts of barium oxide, 4 parts of aluminum oxide, 33 parts of silicon dioxide, and 8 parts of solvent.

[0035] Its raw material components also include 3 parts of sodium dioxide.

[0036] Its raw material components also include 2 parts of potassium oxide.

[0037] Its raw material components also include 5 parts of calcium oxide.

[0038] Its raw material components also include 5 parts of zinc oxide.

[0039] Put each raw material into the mixer according to the number of parts, and then add water whose mass is 0.5 times of the total mass of the raw materials for mixing and grinding until the fineness of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glaze for achieving a silk glazed surface effect on a tile surface, a preparation method and the tile. The glaze is prepared from the following raw material components by weight: mineral material, limestone, 1-2 parts of dolomite, wollastonite, barium carbonate, calcined talcum powder, feldspar, nepheline, magnesium oxide, barium oxide, aluminum oxide, silicon dioxide anda solvent. The preparation method of the glaze comprises the following steps: adding the raw materials into a mixer according to the number of parts, adding water with the mass of 0.3 to 0.6 time ofthe total mass of the raw materials, mixing and grinding, until the fineness of glaze slip is 600 to 900 meshes, thus obtaining the glaze. The glaze prepared by the method has a soft, fine and smoothhand feeling and has good wear resistance, and the tile surface can have the silk glazed surface effect after the glaze is applied to the tile.

Description

technical field [0001] The invention relates to the field of ceramic tile glazes, in particular to a glaze with a silk glaze effect on the surface of ceramic tiles, a preparation method and ceramic tiles. Background technique [0002] Traditional ceramic tiles have various glazed decorations, which bring more choices to consumers and designers, and are deeply loved by people. With the improvement of people's living standards, soft and glossy tiles are welcomed by more consumers. As an ancient high-grade textile, silk has been widely used for a long time, but there are few glazed ceramic tiles with silk glaze effect. The existing ceramic tiles with silk effect are mainly produced by adding fritted glaze. This production method makes the firing range narrow and the production cost is relatively high. [0003] Therefore, the prior art still needs to be improved and developed. Contents of the invention [0004] In view of the deficiencies in the prior art above, the purpose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B33/34C04B41/86E04F13/075
CPCC03C8/00C04B33/34C04B41/5022C04B41/86E04F13/0875
Inventor 刘定鲁符以辉杨飞彭清之彭超
Owner GUANGDONG SANSHUI TANDH GLAZE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap