Sulfonic acid type water-based polyurethane pressure-sensitive adhesive and preparation method thereof

A water-based polyurethane and pressure-sensitive adhesive technology, which is applied in the field of pressure-sensitive adhesives, can solve the problems of water-based polyurethane pressure-sensitive adhesives with reduced viscosity and no longer bonding, and achieves good initial viscosity, good hydrophilic performance, and good continuous adhesion. combined effect

Inactive Publication Date: 2019-03-01
INST OF NEW MATERIALS & IND TECH WENZHOU UNIV
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing water-based polyurethane pressure-sensitive adhesives have good initial viscosity, but as time goes by, the viscosity of water-based polyurethane pressure-sensitive adhesives will drop significantly, and they can no longer play the role of bonding, which limits their application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A sulfonic acid type water-based polyurethane pressure-sensitive adhesive, comprising the following components by weight:

[0037] 25 parts of isocyanate;

[0038] 50 parts of deionized water;

[0039] 10 parts of polymer glycols;

[0040] 8 parts of small molecular polyols;

[0041] 6 parts of chain extender;

[0042] 2 parts of stabilizer;

[0043] 4 parts of regulator;

[0044] 2 parts of blocking agent;

[0045] The chain extender is 8-aminonaphthalene-1,6-sodium disulfonate, 1,4-bis(butyryloxy)-2-butene and N-tris(hydroxymethyl)methyl-3- The mixture of sodium sulfamate, its mass ratio is 3:1:1.

[0046] The isocyanate is a mixture of isophorone diisocyanate, hexamethylene diisocyanate and trimethylhexamethylene diisocyanate, and its mass ratio is 7:2:1.

[0047] The polymer diol is a mixture of polyoxypropylene diol and polyallyl diglycol carbonate, the mass ratio of which is 1:1, and the number average molecular weight of the polymer diol is 2500-3500.

...

Embodiment 2

[0058] A sulfonic acid type water-based polyurethane pressure-sensitive adhesive, comprising the following parts by weight:

[0059] 20 parts of isocyanate;

[0060] 45 parts of deionized water;

[0061] 8 parts of polymer diol;

[0062] 6 parts of small molecule polyols;

[0063] 5 copies of chain extender;

[0064] 1 part of stabilizer;

[0065] 2 parts of conditioner;

[0066] 1 part of end capping agent;

[0067] The chain extender is sodium 8-aminonaphthalene-1,6-disulfonate, 1,4-bis(butyryloxy)-2-butene and N-tris(hydroxymethyl)methyl-3- The mixture of sodium aminopropanesulfonate, its mass ratio is 3:1:1.

[0068] The isocyanate is a mixture of isophorone diisocyanate, hexamethylene diisocyanate and trimethylhexamethylene diisocyanate, and its mass ratio is 7:2:1.

[0069] The polymer diol is a mixture of azelaic acid-1,2-propylene glycol polyester and polyethylene succinate, and its mass is 2:3, and the number-average molecular weight of the polymer diol is 25...

Embodiment 3

[0080] A sulfonic acid type water-based polyurethane pressure-sensitive adhesive, comprising the following parts by weight:

[0081] 30 parts of isocyanate;

[0082] 70 parts of deionized water;

[0083] 13 parts of polymer diols;

[0084] 9 parts of small molecule polyols;

[0085] 8 parts of chain extender;

[0086] 3 parts of stabilizer;

[0087] 5 parts of conditioner;

[0088] 3 parts of end capping agent;

[0089] The chain extender is sodium 8-aminonaphthalene-1,6-disulfonate, 1,4-bis(butyryloxy)-2-butene and N-tris(hydroxymethyl)methyl-3- The mixture of sodium aminopropanesulfonate, its mass ratio is 3:1:1.

[0090] The isocyanate is a mixture of isophorone diisocyanate, hexamethylene diisocyanate and trimethyl hexamethylene diisocyanate, and its mass ratio is 7:2:1.

[0091] The polymer diol is a mixture of polyallyl diethylene glycol carbonate and polyethylene succinate, and its mass ratio is 2:1, and the number-average molecular weight of the polymer diol is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sulfonic acid type water-based polyurethane pressure-sensitive adhesive and a preparation method thereof. The sulfonic acid type water-based polyurethane pressure-sensitive adhesive takes a polymer composed of isocyanate, polymer diatomic alcohol, small molecular polyhydric alcohol and a chain extender as a main body of the pressure-sensitive adhesive, takes deionized water as a solvent, is free of toluene and other organic solvents, and is nontoxic, pollution-free and environment-friendly; the chain extender, a stabilizer, a regulator and a blocking agent are also added; a mixture of 8-naphthylamine-1,6-disulfonate sodium, 1,4-bis(butyryloxy)-2-butene and sodium N-tris(hydroxymethyl)methyl-3-aminopropane sulfonate is selected as the chain extender; under combinedaction of the three substances, a good chain extending effect is achieved, the length of a polymer is extended, the structure of the polymer is adjusted, and the chain extender has a synergistic effect with the polymer main body; and meanwhile, the prepared pressure-sensitive adhesive has certain temperature tolerance, the finally prepared pressure-sensitive adhesive has high initial viscosity and strong holding power, and the application range of the water-based polyurethane pressure-sensitive adhesive is greatly extended.

Description

technical field [0001] The invention relates to a pressure-sensitive adhesive, in particular to a sulfonic acid type water-based polyurethane pressure-sensitive adhesive and a preparation method thereof. Background technique [0002] Pressure-sensitive adhesive, the abbreviation of pressure-sensitive adhesive, is a type of adhesive that is sensitive to pressure. It is mainly used to prepare pressure-sensitive tapes. Its function is to make the tape have pressure-sensitive adhesive properties. According to the composition of the main resin, pressure-sensitive adhesives can be divided into two types: rubber type and resin type. The rubber type can be divided into natural rubber and synthetic rubber; the resin type mainly includes acrylic, silicone and polyurethane. [0003] Water-based polyurethane (WPU) refers to a stable emulsion formed by dissolving or dispersing polyurethane (PU) in water. It uses polyurethane resin as the base material, uses water instead of organic solv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/04C09J175/08C09J175/06C09J11/06C08G18/75C08G18/73C08G18/44C08G18/48C08G18/32C08G18/42
CPCC08G18/3857C08G18/4018C08G18/4202C08G18/4238C08G18/44C08G18/4825C08G18/722C08G18/73C08G18/755C08G2170/80C09J11/06C09J175/04C09J175/06C09J175/08C08K5/005
Inventor 任宝东晁国库赵启樑赵亚娟袁开博
Owner INST OF NEW MATERIALS & IND TECH WENZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap