A kind of polyphenylene sulfide resin synthesis process

Abstract

The invention discloses a polyphenylene sulfide resin synthesis process, and the purpose is to obtain a resin synthesis method with good particle shape, high product yield, high solvent recovery rate and reduced corrosion degree of a polymerization reaction device. Sodium hydrosulfide, sodium hydroxide, and p-dichlorobenzene of water are used as raw materials, and N-methylpyrrolidone is used as a solvent, and a condensation polymerization reaction occurs in the synthesis system. After the low-temperature and high-temperature polycondensation is completed, acetate, NMP and aqueous solution are then subjected to high temperature insulation, cooling, and filtration. After the filter cake is purified by NMP solvent, it is repeatedly washed with deionized water, filtered, and the filter cake is dried to obtain polyphenylene sulfide resin. Synthesis of the present invention The polyphenylene sulfide resin is widely used in aerospace, electronic machinery, petrochemical, food, light industry, thermal power generation, cement industry, steel manufacturing, environmental protection, textile industry and other fields.

Description

technical field [0001] The invention relates to the field of synthesis of resin materials, in particular to a synthesis process of polyphenylene sulfide resin. Background technique [0002] Linear high-molecular-weight polyphenylene sulfide (PPS) is widely used in aerospace, electronic machinery, petrochemical, food, light industry and other industrial technology fields due to its good chemical and physical properties. attention. US Patent No. 4910294, European Patent No. EP0256757, and U.S. Patent No. 4794164 all describe the process of synthesizing PPS in two steps, but they do not involve the method of adding materials. Domestic industrial synthesis process about PPS, only see the synthesis process and process condition control method announced by Chinese patent CN971073570, in the process of its polymerization reaction, almost all adopt a one-time feeding method, this method must reduce the temperature in the kettle to When the temperature is below 160°C, open the kett...

AI Technical Summary

Problems solved by technology

[0005] In Chinese patent application 201610033529.2, a co-solvent using sodium acetate as a synthetic polyphenylene sulfide resin is introduced. After the polyphenylene sulfide resin is synthesized, it is affected by the shape of the sodium acetate crystal, making the polyphenylene sulfide resin relatively difficult to form. more difficult

[0006] In Chinese patent application 201410087155.3, an industrial synthesis process of polyphenylene sulfide resin without adding any additives is introduced, in which sodium hydrosulfide, sodium hydroxide and p-dichlorobenzene are used as raw materials, and N-methyl- 2-Pyrrolidone is used as a solvent, and polyphenylene sulfide resin is synthesized by polycondensation without adding any synthetic additives. Due to the influence of the amount of solvent in the polymerization reaction system, the synthesized polyphenylene sulfide resin particles are very irregular, and at the same time The presence of polyphenylene sulfide resin particles is very small, which is not conducive to later purification and washing