A meteorite and glass technology, applied in the field of special coatings, can solve the problems of high cost and complex process, and achieve the effects of good chemical resistance, good permeability, and improved gloss and flexibility.

Active Publication Date: 2021-01-26
YINGDE YAJIA PAINT
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the process is complicated and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method, composition and decorative glass of cast meteorite coating for glass decoration
  • Preparation method, composition and decorative glass of cast meteorite coating for glass decoration
  • Preparation method, composition and decorative glass of cast meteorite coating for glass decoration

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The coating method of pouring meteorite paint for glass decoration, the coating method comprises the following steps:

[0052] A. Cut the flat glass with a glass knife, clean it, put it into the bottom of the box for making the meteorite paint for later use, and cut a slightly harder and wrinkled PET / PVC film that is slightly larger than the glass, and Knead well and wrinkle, set aside;

[0053] B. Prepare agent A and agent B according to the following ratio, agent A: agent B = 2:1, put it in a thick transparent PE film bag, gently squeeze agent A and agent B until they are completely mixed and well controlled The amount of bubbles produced;

[0054] C. When agent A and agent B react to generate heat and increase the consistency, and when there is good fluidity, pour it into the prefabricated box. The bottom of the box is flat glass for making meteorite paint carrier. After casting, cover it with A Step prefabricated PET / PVC crepe film;

[0055] D. After 24 hours, sm...

Embodiment 2

[0072] The coating method of casting meteorite paint for glass decoration, the coating method may further comprise the steps:

[0073] A. Cut the flat glass with a glass cutter, clean it, put it into the bottom of the box for making the cast meteorite paint, and cut it into a slightly harder and wrinkled PET / PVC film that is slightly larger than the glass. , and knead the wrinkles well, set aside;

[0074] B. Prepare agent A and agent B according to the following ratio, agent A: agent B = 1:1, put it in a thick transparent PE film bag, gently squeeze agent A and agent B until they are completely mixed and well controlled The amount of bubbles produced;

[0075] C. When agent A and agent B react to generate heat and increase the consistency, and when there is good fluidity, pour it into the prefabricated box. The bottom of the box is flat glass for making meteorite paint carrier. After casting, cover it with A Step prefabricated PET / PVC crepe film;

[0076] D. After 24 hours...

Embodiment 3

[0093] The coating method of pouring meteorite paint for glass decoration, the coating method comprises the following steps:

[0094] A. Cut the flat glass with a glass cutter, clean it, put it into the bottom of the box for making the cast meteorite paint, and cut it into a slightly harder and wrinkled PET / PVC film that is slightly larger than the glass. , and knead the wrinkles well, set aside;

[0095] B. Prepare agent A and agent B according to the following ratio, agent A: agent B = 1.5:1, put it in a thick transparent PE film bag, gently squeeze agent A and agent B until they are completely mixed and well controlled The amount of bubbles produced;

[0096] C. When agent A and agent B react to generate heat and increase the consistency, and when there is good fluidity, pour it into the prefabricated box. The bottom of the box is flat glass for making meteorite paint carrier. After casting, cover it with A Step prefabricated PET / PVC crepe film;

[0097] D. After 24 hour...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of special coatings, and discloses a method for preparing a cast meteorite coating for glass decoration. The method specifically comprises: mixing agent A containing epoxy resin with epoxy curing agent containing modified alicyclic amines After the agent B is mixed evenly, it is spread on one side of the glass to form a casting layer, and a film that can shield the mixed gas produced by the reaction between agent A and agent B is laid on it, so that the mixed gas forms a layer of different shades on the surface of the casting layer under the pressure of the film. A hollow body, the present invention also discloses a cast meteorite coating paint and decorative glass for glass decoration. The method is simple to operate and low in manufacturing cost. The decorative glass prepared by this method can be seen from the front of the glass in different sizes. , like meteorites falling from the sky, colorful, radiant, dazzling; good decoration.

Description

technical field [0001] The invention relates to the field of special coatings, in particular to a preparation method, composition and decorative glass of a cast meteorite coating for glass decoration. Background technique [0002] CN200810143949.1 discloses a method for making meteorite glass, which is to apply the prepared meteorite glass paint evenly on the surface of the glass, and spread the wrinkled PET film (or PVC film) on the surface of the glass meteorite paint , so that the glass meteorite paint flows with the wrinkles on the PET film, and after natural solidification and drying, spray 2-3 times of glass colored pearlescent paint and colored silver powder paint evenly on the surface of the meteorite paint that has formed wrinkles, (or spray 1 time) Mirror silver reflective paint), baked in an oven set at 60-70°C for 40-60 minutes, and finally sprayed with black or white primer. Due to the different construction technology from the existing glass paint, especially ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D167/00C09D5/28C03C17/30C03C17/34C03C17/38
CPCC03C17/006C03C17/30C03C17/34C03C17/3642C03C17/3649C03C17/3684C03C17/38C03C2217/72C03C2218/114C03C2218/32C09D5/28C09D163/00C08L67/00
Inventor 刘文革何伍南
Owner YINGDE YAJIA PAINT
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com