Method for controlling the center defect of ultra-wide slab

A technology of center defect and control method, applied in the field of continuous casting billet processing, can solve the problems of inconsistent end point of billet solidification, easy formation of center segregation, safety accidents, etc., to promote the movement of inclusions and bubbles, improve center segregation, and increase rigidity Effect

Inactive Publication Date: 2019-04-16
NANJING IRON & STEEL CO LTD
View PDF12 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] During the casting process of ultra-wide slabs, due to the wide section of the casting machine, it is difficult to uniformly cool the slabs in the secondary cooling zone, resulting in inconsistent solidification end points of the slabs, poor effect of light reduction process, and easy formation of center segregation, center looseness, and shrinkage cavities internal defects such as V-shaped segregation, etc., thereby reducing the ductility, hydrogen-induced crack resistance and welding performance of the steel, or causing safety accidents due to internal quality problems of the steel.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0016] Embodiment: A method for controlling defects in the center of an ultra-wide slab, including a continuous casting machine, the continuous casting machine includes eight cooling sections located behind the crystallizer, including the following steps:

[0017] In the second cooling section, there is an electromagnetic stirring device for generating spiral rotating force to stir molten steel. The electromagnetic stirring device includes a first electromagnetic stirring roller set and a second stirring electromagnetic roller set. The spiral rotating force is controlled by the first electromagnetic stirring roller set and the second stirring electromagnetic roller set. The magnetic field of the electromagnetic roller group is generated, wherein the first stirring electromagnetic roller group is located in the second section of the second cooling section, the second stirring electromagnetic roller group is located in the third section of the second cooling section, and the first...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for controlling the center defect of an ultra-wide slab, and relates to the technical field of continuous casting blank processing. A continuous casting machine is involved, and comprises eight cooling sections positioned behind a crystallizer, and the method comprises the following steps that an electromagnetic stirring device used for generating spiral rotating force and stirring molten steel is arranged at a second cooling section, the electromagnetic stirring device comprises a first electromagnetic stirring roller set and a second stirring electromagneticroller set, the first stirring electromagnetic roller set is located at the second section of the second cooling section, the second stirring electromagnetic roller set is located at the third sectionof the second cooling section. According to the method, the electric magnetic force can be used for driving a steel liquid perpendicular to columnar crystal to flow so as to enable the temperature ofthe solidified front edge to be uniform, impurities and bubbles in the solidified front edge can be promoted to move, most importantly, columnar dendritic crystal is broken or bent, the solute accumulates in the solidified front edge is uniformly distributed in a solution body, after the dendritic crystal fragments enter the solution body to form a new crystallization core, the quantity of isometric crystal is increased, so that the quality of the continuous casting blank can be improved.

Description

technical field [0001] The invention relates to the technical field of continuous casting slab processing, in particular to a method for controlling defects in the center of an ultra-wide slab. Background technique [0002] During the casting process of ultra-wide slabs, due to the wide section of the casting machine, it is difficult to uniformly cool the slabs in the secondary cooling zone, resulting in inconsistent solidification end points of the slabs, poor effect of light reduction process, and easy formation of center segregation, center looseness, and shrinkage cavities and V-shaped segregation and other internal defects, thereby reducing the ductility, hydrogen-induced crack resistance and welding performance of the steel, or causing safety accidents due to internal quality problems of the steel. Contents of the invention [0003] The technical problem to be solved by the present invention is that in the casting process of super-wide slabs, due to the wide section ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/115B22D11/22
CPCB22D11/115B22D11/225
Inventor 常运合
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products