A kind of ceramic energy storage capacitor and preparation method thereof
A technology of energy storage capacitors and ceramics, applied in the direction of fixed capacitor dielectrics and components of fixed capacitors, etc., can solve the problems of high environmental temperature requirements, small capacity of energy storage capacitors, and difficult heat release, etc., to reduce temperature requirements, reduce Small leakage current change, good thermal conductivity
Active Publication Date: 2022-03-11
GUANGZHOU AURORA TECHNOLOGIES CO LTD
View PDF6 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] The purpose of the present invention is to provide a ceramic energy storage capacitor and its preparation method to solve the problems that the energy storage capacitor prepared by the existing method has small capacity, high requirements on the use environment temperature, complex preparation process and difficult release of heat
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0032] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.
[0033] The purpose of the present invention is to provide a ceramic energy storage capacitor and its preparation method to solve the problems that the energy storage capacitor prepared by the existing method has small capacity, high requirements on the use environment temperature, complex preparation process and difficult heat release.
[0034] In order to make the above objects, features and advantages of the present invention more comprehensible, the present ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a ceramic energy storage capacitor and a preparation method thereof. By coating a layer of extremely thin oxide dielectric film on both sides of the ceramic substrate, the capacitance of the capacitor can be kept basically unchanged when the thickness of the prepared ceramic energy storage capacitor is relatively thin; the oxide used in the present invention The thermal conductivity of the dielectric film is better than that of polymer materials, which can reduce the heat accumulation during the repeated use of energy storage capacitors. At the same time, the oxide dielectric film can adapt to higher temperatures and reduce the temperature requirements for the use environment. In addition, the oxide dielectric film prepared by the method of the present invention is denser and plays a blocking role, which can well solve the problem that the leakage current of the capacitor itself gradually increases during the repeated use of the energy storage capacitor, thereby reducing the energy storage capacity. The leakage current of the energy-capacitor changes during the charge-discharge cycle, and maintains the same peak current during the energy release process.
Description
technical field [0001] The invention relates to the technical field of energy storage capacitors, in particular to a ceramic energy storage capacitor and a preparation method thereof. Background technique [0002] In the preparation process of the existing energy storage capacitor, the energy storage capacitor is mostly coated or coated with a layer of organic polymer material film to improve the withstand voltage and charge-discharge cycle of the energy storage capacitor. This preparation method has the following disadvantages: 1. The dielectric constant of the organic polymer film layer is small. After the energy storage capacitor is coated or coated with the film layer, the capacity is small and the energy storage density is reduced; 2. The organic polymer material film The temperature resistance of the layer is low, and there are strict requirements on the ambient temperature of the energy storage capacitor; 3. It is difficult to prepare electrodes on the energy storage ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): H01G4/002H01G4/08H01G4/10H01G4/12
CPCH01G4/002H01G4/08H01G4/10H01G4/12
Inventor 丁明建杨俊锋刘宇鹏陈炜豪刘福扩庄彤
Owner GUANGZHOU AURORA TECHNOLOGIES CO LTD