A kind of giant dielectric copper calcium titanate composite ceramic material and its preparation method and application
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of calcium copper titanate and composite ceramics, which is applied to circuits, capacitors, electrical components, etc., can solve the problems that need to be further improved and less research, and achieve the effects of simple and controllable preparation process, good repeatability and high yield.
Active Publication Date: 2021-05-28
陕西恩能势材料科技有限公司
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In addition, there are very few studies on the dielectric energy storage behavior of CCTO ceramic materials. The patents applied by Yao Xiaolian and others involve copper cadmium titanate, an oxide similar to copper calcium titanate (Yao Xiaolian, Peng Zhanhui, Yang Zupei, Liang Pengfei. A A high breakdown field strength and energy storage density silicon dioxide doped copper cadmium titanate giant dielectric ceramic material and its preparation method: China, CN107188559A[P].2017.07.20), the invention provides a high breakdown field Strong and energy storage density silicon dioxide doped copper cadmium titanate giant dielectric ceramic material and preparation method, the breakdown field strength of the ceramic material is as high as 895-2352V / cm, and the energy storage density is as high as 0.712-1.77mJ / cm 3 , but the energy storage behavior needs to be further improved from the practical application
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0051] A preparation method of a giant dielectric copper calcium titanate composite ceramic material with high energy storage density is carried out according to the following steps:
[0052] (1) Preparation of copper calcium titanate micron powder (M)
[0053] a. Press CaCu 3 Ti 4 o 12 The stoichiometric ratio of the substances were weighed CaCO 3 7.6g, CuO 18.125g and TiO 2 24.275g;
[0054] b, the CaCO weighed in step a 3 , CuO and TiO 2 After mixing the raw materials, put them into a ball mill jar, then add 60mL of absolute ethanol and agate balls as a ball milling medium, place them in a planetary ball mill for ball milling, and mill at a speed of 500r / min for 12 hours;
[0055] c. Put the mixed solution after ball milling on an evaporating dish, place it in a drying oven, and dry it at 80°C for 10 hours to obtain the CCTO precursor powder;
[0056] d. Fully grind the dried CCTO precursor powder and pass through an 80-mesh sieve, then put it into an alumina cruci...
Embodiment 2
[0070] The difference from Example 1 is that in this example, in step (3), the ratio (N:M) of CCTO nanopowder to CCTO micropowder is 0.5:0.5 and weighs 10g of nanometer and 10g of micron powder After mixing, put it into a ball mill jar, then add 30mL of absolute ethanol and agate balls as a ball milling medium, place it in a planetary ball mill, and mill it at a speed of 550r / min for 12h.
[0071] Other steps are the same as in Example 1 to obtain a CCTO composite ceramic sample.
Embodiment 3
[0073] The difference from Example 1 is that in this example, in step (3), the ratio (N:M) of CCTO nanopowder to micron powder is 0.7:0.3, and 14g of nanometer and 6g of micron powder are weighed and mixed. Put it into a ball mill jar, add 30 mL of absolute ethanol and agate balls as a ball milling medium, place it in a planetary ball mill, and mill it at a speed of 550 r / min for 12 hours.
[0074] Other steps are the same as in Example 1 to obtain a CCTO composite ceramic sample.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
breakdown field strength
aaaaa
aaaaa
energy density
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a giant dielectric copper calcium titanate composite ceramic material, a preparation method and application thereof, and belongs to the technical field of electronic ceramic material preparation. The present invention prepares copper-calcium titanate composite ceramic material by mixing micro-nano powders synthesized by solid-phase method and sol-gel method. The preparation process is simple and controllable, with good repeatability and high yield. Powder and nano-powder composite ratio, adjust the grain size and range of copper calcium titanate composite ceramics, so as to obtain dense high dielectric (5×10 4 ), low loss (0.051), high breakdown field strength (2374V / cm) and high energy storage density (20kJ / m 3 ) copper calcium titanate composite ceramic material, its energy storage density is 12.7 and 12.1 times that of ceramics prepared from single micron and nanometer powders. The copper-calcium titanate composite ceramic material prepared by the invention has strong practicability, can be used as a dielectric material to prepare high-dielectric multilayer ceramic capacitors and dynamic random access memories, and can also be used as a pressure-sensitive ceramic material in fields such as electric power and electronic systems.
Description
technical field [0001] The invention belongs to the technical field of preparation of electronic ceramic materials, and relates to a giant dielectric copper calcium titanate composite ceramic material and a preparation method and application thereof. Background technique [0002] With the increasingly prominent world energy and environmental problems, countries all over the world have attached great importance to the development and application of new energy. Dielectric energy storage technology has broad application prospects in the field of energy storage due to its characteristics of fast dielectric response, device miniaturization, intelligence, integration, and low cost, and has become an indispensable part of the development of new energy storage technology. part. The core of dielectric energy storage technology lies in the research and preparation of dielectric energy storage materials, and the development of an environmentally friendly, comprehensive performance, an...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More