Double pore distribution alumina carrier and preparation method thereof, and hydrodemetallization catalyst

A technology of alumina support and double pores, which is applied in metal/metal oxide/metal hydroxide catalysts, catalyst activation/preparation, physical/chemical process catalysts, etc. It can solve the problem of large pore size and the time that reaction molecules stay in the channel short, lower carrier utilization, etc., to achieve high metal capacity, facilitate mass transfer and diffusion, and improve permeability

Active Publication Date: 2019-05-07
CHINA PETROLEUM & CHEM CORP +1
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the alumina support prepared by this technology has a double pore distribution, the pore size of the large pores is relatively large, resulting in a short time for the reaction molecules to stay in the pores, which reduces the utilization rate of the support.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double pore distribution alumina carrier and preparation method thereof, and hydrodemetallization catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Weigh 500 grams of pseudoboehmite A1 (produced by Wenzhou Jingjing Alumina Co., Ltd., with a weight content of 70% on a dry basis) and roast at 450°C for 6 hours to prepare alumina.

[0036] Weigh 50 grams of the above-mentioned alumina and place it in 250 grams of ammonium bicarbonate aqueous solution with a mass concentration of 12%, transfer the mixed material into an autoclave, seal it, heat it at 140°C for 6 hours, and then dry the carrier at 110°C for 6 hours. The aluminum oxide was submerged in a 25% polyethylene glycol-6000 (molecular weight: 6000) solution for 1.5 hours, and then the carrier was dried at 120°C for 6 hours to obtain rod-shaped alumina clusters.

[0037] Weigh 120 grams of pseudo-boehmite A1 (manufactured by Wenzhou Jingjing Alumina Co., Ltd., with a dry weight content of 70%), 30 grams of the above-mentioned rod-shaped alumina clusters, and 1.5 grams of scallop powder, and mix the above-mentioned materials evenly. Add an appropriate amount of aq...

Embodiment 2

[0039] Same as Example 1, except that the calcination temperature of pseudo-boehmite is 550°C. The consumption of ammonium bicarbonate solution is 200 grams, and the mass concentration of solution is 15%. The heat treatment temperature was 160° C., and the treatment time was 4 hours. The polyethylene glycol-6000 solution was changed to polyethylene glycol-2000 (that is, the molecular weight is 2000) solution, and the mass concentration was 30%. The amount of rod-shaped alumina clusters added was 24 grams, and the dual-porous alumina carrier A2 of the present invention was obtained. The properties of the carrier are shown in Table 1.

Embodiment 3

[0041] Same as Example 1, except that the roasting temperature of pseudo-boehmite is 500°C. The consumption of ammonium bicarbonate solution is 400 grams, and the mass concentration of solution is 8%. The heat treatment temperature was 130° C., and the treatment time was 7 hours. The polyethylene glycol-6000 solution was changed to polyethylene glycol-12000 (that is, the molecular weight is 12000) solution, and the mass concentration was 20%. The amount of rod-shaped alumina clusters added was 42 grams, and the dual-porous alumina carrier A3 of the present invention was obtained. The properties of the carrier are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a double pore distribution alumina carrier and a preparation method thereof, and a hydrodemetallization catalyst, wherein the double pore distribution alumina carrier containsa rod-like alumina cluster, and the rod-like alumina cluster is formed by disorderly staggered rod-like alumina. The preparation method of the double pore distribution alumina carrier comprises: calcining pseudo-boehmite A to obtain alumina; immersing the alumina in an ammonium bicarbonate aqueous solution, carrying out sealing heat treatment, drying, soaking with a polyethylene glycol solution, and drying the soaked material to obtain a rod-like alumina cluster; and carrying out mixing kneading molding on pseudo-boehmite B and the rod-like alumina cluster, drying the molded material, and calcining to obtain the double pore distribution alumina carrier. According to the present invention, the prepared double pore distribution alumina carrier has high pore volume and unique double pore distribution; and the hydrodemetallization catalyst prepared from the double pore distribution alumina carrier has advantages of ensured activity and good stability.

Description

technical field [0001] The present invention relates to an alumina carrier, a catalyst containing the carrier and a preparation method thereof, in particular to a double-porous alumina carrier, a hydrodemetallization catalyst and a preparation method thereof, the catalyst is particularly suitable for preparing residual oil in the hydrogen treatment process. Background technique [0002] With the intensification of crude oil deterioration and heaviness, the efficient conversion of heavy oil and the improvement of the yield of light oil products have become an important trend in the development of refining technology. The fixed bed hydrogenation technology of residual oil is an effective means to realize the efficient conversion of heavy oil. Adopting this technical route can effectively remove impurities such as metals, sulfur, nitrogen and residual carbon in residual oil, provide high-quality feed for catalytic cracking, and meet stricter environmental protection regulation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J21/04B01J35/10B01J37/08B01J37/10B01J37/02B01J23/888B01J23/882B01J23/883C10G45/08
Inventor 隋宝宽季洪海彭冲吕振辉关月明佟佳
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com