Preparation method for double-sided light aluminum foil

An aluminum foil, double-sided technology, applied in the field of preparation of double-sided glossy aluminum foil, can solve the problems of difficulty in producing stable and qualified products in batches, difficulty in threading at the entrance of rolling, and poor surface quality, etc., to achieve product thickness reduction Thinning is easy, the speed of the pressing process is reduced, and the effect of reducing quality fluctuations

Inactive Publication Date: 2019-05-17
HANGZHOU FIVE STAR ALUMINUM
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is very difficult to produce by sheet rolling, and it is difficult to produce stable and qualified products in batches.
[0007] 2. When the original process produces single-sheet finished products, there are problems such as difficulty in threading at the rolling entrance, high rate of product breakage, poor surface quality, and low yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for double-sided light aluminum foil
  • Preparation method for double-sided light aluminum foil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention will be described in further detail below.

[0029] The following is a preparation method of a double-sided glossy aluminum foil according to an embodiment of the present invention.

[0030] The method of the present invention comprises:

[0031] (1) Casting and rolling: put 1N00 aluminum alloy materials and aluminum ingots into the melting furnace for melting, after standing still in the furnace, filter the molten liquid with a 50ppi filter, which can effectively absorb and intercept metal and non-metallic substances in the molten liquid Metal magazine, to ensure the filtering effect, to ensure that the hydrogen content is ≤0.10mL / (100 g), and then the cast-rolled plate is obtained after multiple casting and rolling by the casting-rolling machine, and the thickness difference of the same plate of the cast-rolled plate is ≤0.05mm;

[0032] (2) Cold rolling: the cast-rolled sheet is cooled to room temperature, cold-pressed for many times by a cold ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for a double-sided light aluminum foil. The preparation method comprises the following steps that (1) cast-rolling is performed, wherein an aluminum alloymaterial and an aluminum ingot are put into a melting furnace for melting, after standing is performed through a standing furnace, a molten liquid is filtered, and a cast-rolled plate is obtained after multiple times of cast-rolling is performed by a cast-rolling machine; (2) cold rolling is performed, wherein the cast-rolled plate is cooled to room temperature, multiple times of cold pressing isperformed by a cold press, and then multiple times of annealing treatment is performed to obtain an aluminum foil stock; (3) an aluminum foil working procedure is performed, wherein the aluminum foilstock undergoes five passes of rolling working procedures to obtain a finished aluminum foil, the first pass of the rolling working procedure to the third time of the rolling working procedure are rough rolling, the thickness of the obtained aluminum foil is 0.03 mm, the fourth pass of the rolling working procedure is intermediate rolling, the thickness of the obtained aluminum foil is 0.014 mm, the fifth pass of rolling working procedure is finish rolling, and the aluminum foil with the thickness of 0.009 mm is obtained. According to the method, the distribution of reduction pass of an aluminum foil rolling working procedure is adjusted again, the pass reduction rate of the third pass is properly improved, the pass reduction rate of the fifth pass, namely, the pass reduction rate of the final pass is reduced, so that the reduction process speed is reduced, and the thickness of the product is reduced easier.

Description

technical field [0001] The invention relates to the field of aluminum foil processing for lithium batteries, in particular to a preparation method of double-sided glossy aluminum foil. Background technique [0002] my country has now become the world's largest aluminum foil production country, with an annual output of more than 1,000kt of aluminum foil products, and the technology of aluminum foil production is becoming more and more mature. Aluminum foil products have been widely used in food packaging, pharmaceutical packaging, air conditioners, electronics and other industries, and the development prospects are very broad. [0003] At present, the aluminum foil products we produce are divided into two types: double-sided light and single-sided light according to the surface state. Double-sided aluminum foil, the finished product pass is single-sheet rolling, that is, the entrance and exit are single-sheet aluminum foil. The product produced by this process has both upper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21C37/02
Inventor 关世彤袁静慧
Owner HANGZHOU FIVE STAR ALUMINUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products