Automobile metal support surface treatment technology

A metal bracket and surface treatment technology, applied in the direction of metal material coating process, coating, solid diffusion coating, etc., can solve the problems of poor wear resistance, poor high temperature resistance and poor corrosion resistance of metal brackets, and improve support The effect of improving wear resistance and improving service life

Inactive Publication Date: 2019-05-21
华彦汽车零部件(江苏)有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to save costs and improve the precision of the brackets, manufacturers of metal brackets for automobiles have adopted stamping technology to prepare metal brackets. However, the metal brackets after stamping have poor wear resistance, poor fatigue resistance, poor corrosion resistance, and high temperature resistance. poor performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A kind of automobile metal bracket surface treatment process, described steps are as follows:

[0014] (1) Degreasing: place the metal bracket at an ambient temperature of 50-70°C, use a degreasing and degreasing agent to wash the oil and grease on the surface of the metal bracket, and rinse the metal bracket with water after cleaning;

[0015] (2) Grinding: use sandpaper and chemical polishing agent to polish the metal bracket, rinse the polished metal bracket and dry it for later use;

[0016] (3) Nitriding treatment: put the metal bracket into the furnace and heat it at 130-150°C, keep it warm for 1 hour, feed anhydrous nitrogen, then heat to 510-530°C, and keep it for 4-8 hours;

[0017] (4) Galvanizing treatment: take out the metal bracket and place it for cooling, then place the metal bracket in the electroplating solution for galvanizing;

[0018] (5) Cleaning and drying: the metal bracket will be cleaned and prevented from drying at 50-60°C.

[0019] In this e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an automobile metal support surface treatment technology. Surface treatment is carried out on a metal support, and includes the technologies of oil removal, polishing, nitriding treatment, galvanization treatment and cleaning and drying. With the automobile metal support surface treatment technology, the characteristics of wear resistance, fatigue resistance, corrosion resistance and high temperature resistance of the metal support are improved, the corrosion resistance is further improved through galvanization, and the service life of the metal support is prolonged.

Description

technical field [0001] The invention belongs to metal surface treatment technology, in particular to a surface treatment process of an automobile metal bracket. Background technique [0002] In order to save costs and improve the precision of the brackets, manufacturers of metal brackets for automobiles have adopted stamping technology to prepare metal brackets. However, the metal brackets after stamping have poor wear resistance, poor fatigue resistance, poor corrosion resistance, and high temperature resistance. Poor performance. Contents of the invention [0003] Purpose of the invention: the purpose of the invention is to provide a surface treatment process for automobile metal brackets to solve the above-mentioned problems in order to solve the deficiencies in the prior art. [0004] Technical solution: a kind of automobile metal bracket surface treatment process according to the present invention, the steps are as follows: [0005] (1) Degreasing: place the metal b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C8/24C23C8/02C25D3/22C23F17/00
Inventor 郑宏卫
Owner 华彦汽车零部件(江苏)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products