Preparation method of ABS antibacterial plastic board

A technology of antibacterial plastics and plates, applied in the field of new material preparation, to achieve good market prospects

Inactive Publication Date: 2019-06-04
慈溪市万诚纺织品有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no research report on the modification of ABS sheets with nanomaterials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The content of the technical solution will be described in detail below through specific embodiments.

[0012] A preparation method of ABS antibacterial plastic plate, it comprises the following steps:

[0013] (1) Select 25 kg of glass fiber, 1 kg of nano-TiO2 and 2 kg of additives into a mixing device and stir for 30 to 40 minutes. The additive is a silane coupling agent, and the stirring time is generally 30 minutes;

[0014] (2) Add 100 kg of general-purpose ABS resin to the mixture obtained in step (1), stir for 20 to 40 minutes, and the stirring time is 30 minutes;

[0015] (3) The mixed material obtained in step (2) is sent into the board production line by a screw feeder, and the obtained mixed material is made into an ABS antibacterial plastic board through the board production line.

[0016] In the present invention, nano-TiO2 is added to realize the antibacterial function of the ABS board, glass fiber is added to enhance the strength of the ABS board, and a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of an ABS antibacterial plastic board. The method includes the steps of: (1) selecting 25kg of glass fiber, 1kg of nano-TiO2 and 2kg of an additive, putting the substances into a mixer, and conducting stirring for 30-40min; (2) adding 100kg of general grade ABS resin into the mixture obtained in step (1), and performing stirring for 20-40min; and (3) sending the mixture obtained step (2) into a board production line by a screw feeder, and making the obtained mixture into an ABS antibacterial plastic board by the board production line. The inventionhas the beneficial effects that: antibacterial functionalization of the ABS board is realized by adding nano-TiO2 into general grade ABS resin, glass fiber is added to reinforce the strength of the ABS board, a new method for preparation and production of boards special for ABS is opened up, has important application value in reversing the current situation of production of boards special for ABSwith resin special for ABS, and has good market prospects.

Description

technical field [0001] The invention belongs to the technical field of new material preparation, and in particular relates to a preparation method of an ABS antibacterial plastic board. Background technique [0002] ABS resin is an important general-purpose synthetic resin, which has the advantages of high impact resistance, good heat resistance and low temperature resistance, chemical corrosion resistance, high surface hardness, easy molding and processing, etc. It is widely used in electronic appliances, auto parts, furniture, bathroom and industrial parts. Although China is the largest producer of ABS resin in the world, most of them are general-purpose ABS resins. ABS special resins such as flame-retardant, transparent, high-gloss, matte, weather-resistant, antibacterial, and conductive mainly rely on imports, and the production costs are relatively high. ABS sheet is the basic material of ABS resin products. At present, the preparation method of ABS plastic sheet is m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08K7/14C08K3/22
Inventor 陈君辉
Owner 慈溪市万诚纺织品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com