A technology of composite materials and gutta-percha, which is applied in dentistry, dental preparations, dental prostheses, etc., can solve the problems that the precision of finished products needs to be improved, and achieve excellent antibacterial effects, high precision, and increased compatibility.

Active Publication Date: 2019-06-07
SOUTH CHINA AGRI UNIV
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This patented composition described for use in treating teeth diseases involves combining two materials: guttape tip (a type called Gutta Peri) made from algae and an anti bacteric ingredient like nystatin A into one mixture. These compositions have better strength but also improve their ability to fight off plaque buildup on them compared to pure glue solutions alone. Additionally, they provide precise control over how much each component gets mixed together during application, resulting in improved results when applied topically onto hard tissue surfaces such as root cusps.

Problems solved by technology

This patented technical problem addressed in this patent relates to improving dentistry's ability to treat roots effectively while reducing failures caused by root clogging during medical procedures like endodontic therapy. Current methods involve injectable compositions containing liquid photopolyester resists and other chemical substances, making them challenged because they cannot completely mix well together without losing important properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gutta-percha tip composite and DLP printing application thereof
  • Gutta-percha tip composite and DLP printing application thereof
  • Gutta-percha tip composite and DLP printing application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A gutta-percha tip composite material based on DLP printing is prepared from the following components in parts by weight of modified nano-barium sulfate, modified nano-silver and photosensitive resin:

[0029] Modified nano barium sulfate: 10 parts,

[0030] Modified nano silver: 10 parts,

[0031] Photosensitive resin: 80 parts;

[0032] The specific steps are: add modified nano-barium sulfate and modified nano-silver to the photosensitive resin in batches according to the proportion, and under the condition of heating (45°C) and avoiding light, stir each time evenly, and stir for 6 hours, and finally obtain a DLP-based gutta-percha tip composites.

[0033] The preparation method of modified nano-barium sulfate and modified nano-silver powder is the same: first dissolve titanate coupling agent UP-801 in an appropriate amount of 40°C absolute ethanol to make the concentration reach 2wt%, and then add an appropriate amount of nano-barium sulfate Or nano-silver, so tha...

Embodiment 2

[0037] A gutta-percha tip composite material based on DLP printing is prepared from the following components in parts by weight of modified nano-barium sulfate, modified nano-silver and photosensitive resin:

[0038] Modified nano zirconia: 15 parts,

[0039] Modified nano silver: 15 parts,

[0040] Photosensitive resin: 70 parts;

[0041] The specific steps are: add modified nano-barium sulfate and modified nano-silver to the photosensitive resin in batches according to the proportion, and under the condition of heating (45°C) and avoiding light, stir each time evenly, and stir for 5 hours to finally obtain a DLP-based gutta-percha tip composites.

[0042] The preparation method of modified nano-zirconia and modified nano-silver powder is the same: first dissolve stearic acid in an appropriate amount of 40°C absolute ethanol to make the concentration reach 1.5wt%, add nano-zirconia or nano-silver, and make it with The mass-to-volume ratio between the surface modifier solut...

Embodiment 3

[0046] A gutta-percha tip composite material based on DLP printing is prepared from the following components in parts by weight of modified nano-barium sulfate, modified nano-silver and photosensitive resin:

[0047] Modified nano barium sulfate: 10 parts,

[0048] Modified nano silver: 20 parts,

[0049] Photosensitive resin: 70 parts;

[0050] The specific steps are: add the obtained modified nano-barium sulfate and modified nano-silver to the photosensitive resin in batches according to the proportion, and under the condition of heating (45°C) and avoiding light, stir evenly each time, stir for 4 hours, and finally get A gutta-percha tip composite based on DLP printing.

[0051] The preparation method of modified nano-barium sulfate and modified nano-silver powder is the same: first dissolve titanate coupling agent UP-801 in an appropriate amount of 40°C absolute ethanol to make the concentration reach 2.5wt%, then add nano-barium sulfate Or nano-silver, so that the mass...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical fields of manufacturing and applying of a DLP strengthened material and stomatology, and particularly relates to a gutta-percha tip composite. The gutta-percha tip composite comprises the following components in parts by weight of 5-20 parts of a modified developer, 5-20 parts of a modified antibacterial agent and 60-80 parts of photosensitive resin, whereinthe modified developer and the modified antibacterial agent are obtained through surface modification with a surface modifier. The gutta-percha tip composite is suitable for DLP printing, has favorable characteristics of favorable mechanical properties, favorable antibacterial effects and favorable biocompatibility, is high in production and processing precision, and can realize smooth printing. The gutta-percha tip composite can be widely applied to the biomedical science field, particularly the stomatology field. The root canal treatment accuracy can be improved, and a new way is provided for reduction of the failure rate of root canal treatment.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner SOUTH CHINA AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap