A kind of self-cleaning heat-insulation paint for building exterior wall, roof and preparation method

A heat-insulating coating and self-cleaning technology, applied in the direction of coating, etc., can solve the problems that affect the aesthetics of buildings and city appearance, adverse effects, coatings are easily contaminated with dust, oil, etc., and achieve good self-cleaning effect Effect

Active Publication Date: 2021-05-11
中山多涂乐建材有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the viscousness of the heat-insulation coating that makes is very big, and coating is easy to contaminate dust, oil stain etc., affects building aesthetics and city appearance, and the adhesion of organic pollutant may cause adverse effect to coating property, affects Coating functionality and durability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of self-cleaning heat-insulation paint for building exterior wall, roof and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Stir and heat the ethylene-vinyl acetate copolymer emulsion to 67°C, add ammonium persulfate aqueous solution, sodium bicarbonate aqueous solution, and sodium dodecylsulfonate under nitrogen protection, heat up to 83°C, and then add dropwise Perfluoroalkyl ethyl acrylate and acrylic acid were copolymerized for 4 hours under stirring to obtain a composite emulsion; the solid content of the ethylene-vinyl acetate copolymer emulsion was 56%, and the mass ratio of ethylene to vinyl acetate was 15:85 The mass concentration of ammonium persulfate aqueous solution is 7%; The mass concentration of sodium bicarbonate aqueous solution is 4%; Perfluoroalkyl ethyl acrylate is perfluorooctyl ethyl acrylate; The parts by weight of each raw material are, ethylene- Vinyl acetate copolymer emulsion 61.4 parts by weight, ammonium persulfate aqueous solution 2.5 parts by weight, sodium bicarbonate aqueous solution 1.4 parts by weight, sodium dodecylsulfonate 0.7 parts by weight, perflu...

Embodiment 2

[0028] (1) Stir and heat the ethylene-vinyl acetate copolymer emulsion to 66°C, add ammonium persulfate aqueous solution, sodium bicarbonate aqueous solution, and sodium dodecylsulfonate under nitrogen protection, raise the temperature to 81°C, and then add dropwise Perfluoroalkyl ethyl acrylate and acrylic acid, copolymerization reaction 4.5h under stirring state, make composite emulsion; The solid content of ethylene-vinyl acetate copolymer emulsion is 52%, and the mass ratio of ethylene and vinyl acetate is 15: 85; the mass concentration of ammonium persulfate aqueous solution is 6%; the mass concentration of sodium bicarbonate aqueous solution is 3.5%; perfluoroalkyl ethyl acrylate is perfluorohexyl ethyl acrylate; the parts by weight of each raw material are, ethylene- Vinyl acetate copolymer emulsion 63.9 parts by weight, ammonium persulfate aqueous solution 2.3 parts by weight, sodium bicarbonate aqueous solution 1.2 parts by weight, sodium dodecylsulfonate 0.6 parts by ...

Embodiment 3

[0033] (1) Stir and heat the ethylene-vinyl acetate copolymer emulsion to 69°C, add ammonium persulfate aqueous solution, sodium bicarbonate aqueous solution, and sodium dodecylsulfonate under nitrogen protection, raise the temperature to 84°C, and then add dropwise Perfluoroalkyl ethyl acrylate and acrylic acid, copolymerization reaction 3.5h under stirring state, make composite emulsion; The solid content of ethylene-vinyl acetate copolymer emulsion is 58%, and the mass ratio of ethylene and vinyl acetate is 15: 85; the mass concentration of ammonium persulfate aqueous solution is 7%; the mass concentration of sodium bicarbonate aqueous solution is 4.5%; perfluoroalkyl ethyl acrylate is perfluorobutyl ethyl acrylate; the parts by weight of each raw material are, ethylene - 58.7 parts by weight of vinyl acetate copolymer emulsion, 2.7 parts by weight of ammonium persulfate aqueous solution, 1.7 parts by weight of sodium bicarbonate aqueous solution, 0.9 parts by weight of sodi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water contact angleaaaaaaaaaa
Login to View More

Abstract

The invention provides a self-cleaning heat-insulating coating for building exterior walls and roofs and a preparation method. In this method, ethylene-vinyl acetate copolymer emulsion is used as the polymerization seed, and perfluoroalkyl ethyl acrylate and acrylic acid are grafted and copolymerized to obtain a composite emulsion, and then micronized with heptadecafluorodecyltrimethoxysilane and nano thermal insulation fillers for surface modification, and finally composite emulsion, fluorine-modified micro-fillers, fluorine-modified nano-fillers, pigments, wetting and dispersing agents, polyvinyl formal glue, ammonia water, cross-linking agents, defoamers, ultraviolet absorbers The self-cleaning heat-insulating coating for exterior walls and roofs of buildings can be obtained by mixing uniformly with the agent and appropriate amount of water. Compared with the traditional method, the coating made of the heat-insulating coating of the present invention has a higher contact angle to water and oil, and the water drop or oil drop cannot automatically expand on the coating surface and maintain a spherical shape, and it is easy to roll off the surface And take away other adhered pollutants, thus showing a good self-cleaning effect.

Description

technical field [0001] The invention belongs to the technical field of functional coatings, and provides a self-cleaning heat-insulating coating for exterior walls and roofs of buildings and a preparation method. Background technique [0002] Generally, architectural coatings have decorative, protective, and habitability-improving functions. Acrylic paint is a one-component water-emulsion waterproof paint made of pure acrylic polymer emulsion as the base material and other additives. It has good aging resistance, elongation, elasticity, adhesion and film-forming properties, and the overall waterproof effect Good, it can be used in non-long-term flooding environments such as roofs, walls, bathrooms, and basements. It is especially suitable for roof waterproofing projects with light-weight thin shell structures, and can also be used as exterior wall decorative coatings. The performance of ethylene-vinyl acetate (EVA) waterproof coatings is similar to that of acrylic coatings,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D151/00C09D129/14C09D7/62C08F263/04C08F220/24C08F220/06
Inventor 张玉英
Owner 中山多涂乐建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com