A preparation method and application of graphene quantum dots and devices or devices containing them

A technology of graphene quantum dots and flake graphite, which is applied in the field of preparation of graphene quantum dots, can solve the problems of adding a large amount of reagents and spending several days, achieve less reagent consumption, shorten reaction time, and reduce operation difficulty and danger sexual effect

Active Publication Date: 2021-01-26
SHENZHEN LOTUT INNOVATION DESIGN CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantage of the hydrothermal method is that the method is based on the raw material GO and its reduction products, which not only requires the oxidation of a large amount of graphite powder to obtain GO, but also requires a series of complex redox reactions, and the reduction The process also typically requires the addition of large quantities of reagents and takes days

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method and application of graphene quantum dots and devices or devices containing them
  • A preparation method and application of graphene quantum dots and devices or devices containing them

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The preparation method provided by the present invention uses flake graphite as raw material to prepare graphene quantum dots. In the prior art, the preparation of graphene quantum dots mostly uses graphene oxide as a raw material (for details, see CN102807209A, etc.), and there are also related projects that use fullerene (for details, see CN104211050A) and coal (for details, see CN103803540A) as raw materials. Prepare to try. However, there are few related studies on the preparation of graphene quantum dots from flake graphite, a layered graphite, as a raw material. Therefore, the proposal of the present invention can not only solve the problems of many reaction steps, long reaction time, and high reagent consumption in the preparation of graphene quantum dots by the traditional hydrothermal method, but also a new attempt and exploration for the preparation of graphene quantum dots. .

[0030] Specifically, the preparation method of the present invention comprises t...

Embodiment 1

[0066] (1) Take 1.2g flake graphite and put it into a 500ml beaker, add 50ml concentrated sulfuric acid, and stir magnetically at room temperature for 30min.

[0067] (2) Place the beaker in a bucket with ice cubes inside, place it on a magnetic stirrer, keep stirring in an ice bath, add 1.5g of sodium nitrate; add potassium permanganate in 5 times, add once every 10 minutes, each time Add 1.2g (control the reaction temperature not to exceed 3°C); keep stirring in an ice bath, and react for 2 hours.

[0068] (3) Take out the beaker, place it in a heat-collecting water bath, and react with stirring for 24 hours under the condition of a water bath at 35°C.

[0069] (4) Keep the ice bath state, add 70ml of distilled water to the beaker (slowly dropwise, keep the temperature of the reactant not exceeding 50°C), after the dilution is completed, place the beaker again in the heat-collecting water bath, under the condition of 85°C water bath , and stirred for 15 minutes.

[0070] (...

Embodiment 2

[0074] (1) Put 2g of graphite flakes into a 500ml beaker, add 50ml of concentrated sulfuric acid, and stir magnetically at room temperature for 30min.

[0075] (2) Place the beaker in a bucket with ice cubes, place it on a magnetic stirrer, keep stirring in an ice bath, add 2g of sodium nitrate, add 1.5g of potassium permanganate in 5 times every 10 minutes; keep stirring in an ice bath , reacted for 2 hours.

[0076] (3) Take out the beaker, place it in a heat-collecting water bath, and react with stirring for 24 hours under the condition of a water bath at 35°C.

[0077] (4) Keeping in the ice bath state, add 70ml of distilled water to the beaker. After the dilution is completed, place the beaker in a heat-collecting water bath again, and stir and react for 15 minutes under the condition of a water bath at 85°C.

[0078] (5) Take out the beaker, add 50ml of distilled water to it again for dilution, and finally add 30% hydrogen peroxide solution dropwise in the beaker until ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method and application of graphene quantum dots and a device or device containing the same. The preparation method of the invention comprises: reacting flake graphite with concentrated sulfuric acid, adding nitrate and potassium permanganate to continue the reaction, diluting the reaction system with water, adding hydrogen peroxide, and the obtained precipitates are graphene quantum dots. Compared with the traditional hydrothermal method, the preparation method of the present invention greatly shortens the required reaction time, and does not require high-temperature reaction, which reduces the operational difficulty and danger of the reaction; at the same time, the preparation method of the present invention requires a small amount of reagents. The processing steps are simple and suitable for large-scale production of graphene quantum dots.

Description

technical field [0001] The invention relates to the field of carbon-based materials, in particular to a preparation method and application of graphene quantum dots and devices or devices containing them. Background technique [0002] As the latest member of the graphene family, zero-dimensional graphene quantum dots (Graphene quantum dots, GQDs) not only have the excellent properties of ordinary graphene materials, but also have stronger quantum confinement effects and Boundary effects, and can exhibit a series of new characteristics. Graphene quantum dots have broader application prospects in the fields of solar photovoltaic devices, biomedicine, light-emitting diodes, and sensors. [0003] GQDs have gradually become the focus of scientists in various fields in recent years, but their development is still in its infancy, and the synthesis process has only begun to be studied in depth in the past two or three years. The synthesis methods of GQDs mainly include hydrothermal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/184C01B32/196
Inventor 张仁辉彭松冷森林
Owner SHENZHEN LOTUT INNOVATION DESIGN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com