Medical hydrocolloid dressing and preparation method thereof
A hydrocolloid, medical technology, applied in the field of biomedical engineering, can solve the problems of ineffective hemostasis and pain relief, unproven safety, and poor wound healing ability, so as to promote the growth of wound granulation tissue, promote orderly growth, and promote healing Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0037] This embodiment provides a medical hydrocolloid dressing, the main components of which include: by mass percentage, 52% of medical adhesive, 20% of sodium carboxymethylcellulose, 10% of bioactive glass, 1% of beeswax, and 8% of olive oil %, microcapsule wall material 9%.
[0038] The medical adhesive is medical polyisobutylene hot melt adhesive, and the microcapsule wall material is hyaluronic acid salt. Both the bioactive glass and the sodium carboxymethyl cellulose have a size of 150 mesh to 300 mesh. The medical polyisobutylene hot-melt adhesive, hyaluronic acid salt, bioactive glass and sodium carboxymethylcellulose are all commercially available.
[0039] The present embodiment also provides the preparation method of above-mentioned medical hydrocolloid dressing, and the steps are as follows:
[0040] Step 1, heating and melting the adhesive at 130°C;
[0041]Step 2, preparation of microcapsules: Soak the microcapsule wall material in water and heat to 70° C. an...
Embodiment 2
[0046] The present embodiment provides a medical hydrocolloid dressing, the main components include: by mass percentage, medical adhesive 51%, sodium carboxymethylcellulose 20%, bioactive glass 5%, beeswax 2%, olive oil 10% %, microcapsule wall material 12%.
[0047] The medical adhesive is medical polyisobutylene hot melt adhesive, and the microcapsule wall material is alginate. Both the bioactive glass and the sodium carboxymethyl cellulose have a size of 150 mesh to 300 mesh.
[0048] The present embodiment also provides the preparation method of above-mentioned medical hydrocolloid dressing, and the steps are as follows:
[0049] Step 1, heating and melting the adhesive at 140°C;
[0050] Step 2, preparation of microcapsules: Soak the microcapsule wall material in water and heat to 68° C. and stir for 30 minutes at a constant temperature to obtain a wall material solution. The mass ratio of the wall material in the wall material solution is 15%; beeswax, olive oil And s...
Embodiment 3
[0055] This embodiment provides a medical hydrocolloid dressing, the main components include: by mass percentage, medical adhesive 53%, sodium carboxymethylcellulose 25%, bioactive glass 10%, beeswax 1%, olive oil 5% %, microcapsule wall material 6%.
[0056] The medical adhesive is medical polyisobutylene hot melt adhesive, and the microcapsule wall material is hyaluronic acid salt. Both the bioactive glass and the sodium carboxymethyl cellulose have a size of 150 mesh to 300 mesh.
[0057] The present embodiment also provides the preparation method of above-mentioned medical hydrocolloid dressing, and the steps are as follows:
[0058] Step 1, heating and melting the adhesive at 145°C;
[0059] Step 2, preparation of microcapsules: Soak the microcapsule wall material in water and heat to 73° C. and stir for 30 minutes at a constant temperature to obtain a wall material solution. The mass ratio of the wall material in the wall material solution is 25%; beeswax, olive oil A...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com