Anti-corrosion, anti-sticking, high temperature resistant oil casing connector and preparation method thereof

A connector and high-temperature-resistant technology, which is applied in the direction of casing, drill pipe, earthwork drilling, etc., can solve the problems of only one maintenance, harsh working environment, thread failure, etc., achieve uniform and dense distribution, improve mining efficiency, and extend The effect of service life

Active Publication Date: 2021-06-22
山西中能企服环保科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, as the oilfield enters the middle and later stages of exploitation, the downhole working environment is getting worse. The well fluid contains various corrosive components such as carbon dioxide and hydrogen sulfide. Corrosion damage is becoming more and more serious, which often leads to corrosion and perforation of oil casing couplings, resulting in oil leakage. In severe cases, thread failure occurs and breaks off, resulting in serious well shutdown accidents. At the same time, the oil casing coupling will also stick to the oil casing, resulting in the failure to remove and replace the oil casing coupling normally and quickly, increasing the work intensity of the operator and reducing the work efficiency
[0004] Aiming at the sticking situation, oilfields currently generally use lubricating paste and anti-sticking agents on the thread of the oil casing coupling. Although it has a certain effect, it increases the labor intensity of the operator, and the effect is only limited. It can be maintained once, and it needs to be repeated for the next maintenance
In addition, lubricating paste, anti-sticking agent and other materials will fail in high temperature environment for a long time, which cannot meet the high temperature resistance working conditions of the increasing number of ultra-deep wells and heavy oil hot wells in oil fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The present invention also provides a method for preparing an anti-corrosion, anti-sticking, and high-temperature-resistant oil casing connector, which includes the following steps:

[0027] (1) Prepare the connector base: use materials that meet the standards of the petroleum industry to process into a hollow cylindrical body, and make a hole in the body along the axial direction. The through hole has a certain taper, and then process the internal thread on the inner wall of the through hole to obtain the connection. The base body of the device, the specification of the internal thread conforms to the petroleum industry standard, and the taper of the through hole is 12°;

[0028] (2) Pretreatment of the connector base: wash the connector base with hot water and cold water to remove grease and impurities on the surface of the base;

[0029] (3) electroplating: electroplating a tungsten-based amorphous alloy coating on the surface of the pretreated connector base;

[00...

Embodiment 1

[0037] Prepare the connector base: select the P110 oil casing material that meets the industry standard, process it into a hollow cylindrical body, and make a hole in the axial direction in the body. The through hole has a certain taper, and the taper of the through hole is 12°C. Then process the internal thread on the inner wall of the through hole to obtain the connector base. The length and diameter of the connector should be compatible with the size of the oil casing; the equipment selected for the through hole and the processing of the internal thread only needs to meet the requirements for preparing the connector base that meets industry standards. can;

[0038] Pretreatment: Use sandpaper to remove the rust on the surface of the connector substrate prepared above, and then soak it in boiling water for 0.5h. After soaking, soak it in cold water for 0.5h, take it out and wash it with deionized water for 2 hours. Second, remove the grease and attached impurities on the sur...

Embodiment 2

[0047] Prepare the connector base: select the P110 oil casing material that meets the industry standard, process it into a hollow cylindrical body, and make a hole in the axial direction in the body. The through hole has a certain taper, and the taper of the through hole is 12°C. Then process the internal thread on the inner wall of the through hole to obtain the connector base. The length and diameter of the connector should be compatible with the size of the oil casing; the equipment selected for the through hole and the processing of the internal thread only needs to meet the requirements for preparing the connector base that meets industry standards. can;

[0048] Pretreatment: Use sandpaper to remove the rust on the surface of the connector substrate prepared above, and then soak it in boiling water for 0.5h. After soaking, soak it in cold water for 0.5h, take it out and wash it with deionized water for 2 hours. Second, remove the grease and attached impurities on the sur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides an anti-corrosion, anti-sticking, high-temperature-resistant oil casing connector, which includes a connector base and a tungsten-based amorphous alloy coating, the amorphous alloy coating itself has high activity, and Ni-P amorphous in the coating State structure passivation film, evenly distributed and dense, can prevent further internal corrosion; in addition, the oil casing connector described in this application can replace the ordinary oil casing connector and the conventional process of painting anti-seize agent, etc., through Electroplating amorphous alloy on the substrate saves the steps of brushing lubricants and anti-sticking agents, effectively reduces the labor intensity, improves the efficiency of oil extraction, and avoids lubricants and anti-sticking agents under high temperature. The defect of failure prolongs the service life of the oil casing.

Description

technical field [0001] The invention relates to a connector, in particular to an anti-corrosion, anti-sticking, high-temperature resistant oil casing connector for oil field development. Background technique [0002] In the process of oil field development, pumping wells are the most important way of oil production at home and abroad, and the oil casing is the main equipment. Generally, the oil casing is connected by the thread of the oil casing collar, and the oil casing is kept The sealing state of the tube space. [0003] However, as the oilfield enters the middle and later stages of exploitation, the working environment in the well is getting worse and worse. The well fluid contains various corrosive components such as carbon dioxide and hydrogen sulfide. Corrosion damage is becoming more and more serious, which often leads to corrosion and perforation of oil casing couplings, resulting in oil leakage. In severe cases, thread failure occurs and breaks off, resulting in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E21B17/08C22C45/10C25D3/56C25D5/50B23P15/00
CPCB23P15/00C22C45/10C25D3/56C25D5/50E21B17/08
Inventor 吴振宁葛效珍
Owner 山西中能企服环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products