A covering agent for preventing tundish melt damage and its application

A covering agent and tundish technology, which is applied in the application field of continuous casting auxiliary materials, can solve the problems of inability to prevent tundish coating erosion and insufficient adsorption capacity, and achieve the goal of reducing abnormal casting, solving the problem of melting loss, and stabilizing continuous casting Effect

Active Publication Date: 2022-02-22
BAOSHAN IRON & STEEL CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

One of the main problems is the insufficient adsorption capacity and most critically, the inability to prevent the erosion of the tundish coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A covering agent for preventing tundish melt damage and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The covering agent for preventing tundish melt damage is produced according to the technical plan and the important components of the ingredients in the technical description.

[0037] 1. Prepare the premelt. According to 58% CaO, 22% Al 2 o 3 , 10% MgO, 8% SiO 2 And 2% C to carry out the proportioning of composition. Among them, CaO and Al 2 o 3 Wollastonite can be used as an incoming material source.

[0038] 2. Prepare magnesia. Using magnesite, the sintering temperature is controlled at 700-950 degrees, and the main component of MgO with a purity of more than 95% is prepared, which is used as the adsorbate of the premelted material in the tundish. The mixing mass ratio of premelt and magnesia is 5:1.

[0039] 3. Mechanically mix the premelted material prepared above with magnesia to form a tundish covering agent for preventing erosion of the tundish.

[0040] Before use, the depth of melting damage in the tundish can reach 20mm-30mm. After the implementatio...

Embodiment 2

[0042] 1. Prepare the premelt. According to 55% CaO, 24% Al 2 o 3 , 11% MgO, and 7.5% SiO 2 , 2.5% C for the proportioning of ingredients. Among them, CaO and Al2O3 can use wollastonite as the source of incoming materials.

[0043] 2. Prepare magnesia. Using magnesite, the sintering temperature is controlled at 700-950 degrees, and the main component of MgO with a purity of more than 95% is prepared, which is used as the adsorbate of the premelted material in the tundish. The mixing mass ratio of premelt and magnesia is 6:1.

[0044] 3. Mechanically mix the premelted material prepared above with magnesia to form a tundish covering agent for preventing erosion of the tundish.

[0045]Before use, the depth of the tundish melting loss can reach 20mm-30mm, and after the implementation, the depth is basically within 2mm, basically solving the problem of melting loss.

Embodiment 3

[0047] 1. Prepare the premelt. According to 52.5% CaO, 23% Al 2 o 3 , 11% MgO, and 10% SiO 2 , 3.5% C for the ratio of ingredients. Among them, CaO and Al2O3 can use wollastonite as the source of incoming materials.

[0048] 2. Prepare magnesia. Using magnesite, the sintering temperature is controlled at 700-950 degrees, and the main component of MgO with a purity of more than 95% is prepared, which is used as the adsorbate of the premelted material in the tundish. The mixing mass ratio of premelt and magnesia is 3:1.

[0049] 3. Mechanically mix the premelted material prepared above with magnesia to form a tundish covering agent for preventing erosion of the tundish.

[0050] Before use, the depth of the tundish melting loss can reach 20mm-30mm, and after the implementation, the depth is basically within 2mm, basically solving the problem of melting loss.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a covering agent for preventing tundish melt damage, including premelt material and adsorbate; the premelt material is composed of the following components by weight percentage: CaO: 50-65%, Al 2 o 3 : 20‑31%, MgO: 10%‑18%, SiO 2 : 7.5-12.5%, C: 2.5%-3%; the melting point is 1300-1450°C; the mass ratio of the premelt and the adsorbate is 5-6:1-2. The covering agent for preventing tundish melt damage of the present invention can be widely used in the production process of continuous steel casting, and has the characteristics of reducing the abnormality of pouring and stabilizing continuous casting. It can effectively prevent the melting loss of the tundish coating. Before adopting the technical solution of the present invention, the depth of the tundish melting loss can reach 20mm-30mm, and after the implementation, the depth is basically within 2mm, which basically solves the problem of melting loss.

Description

technical field [0001] The invention relates to the application field of continuous casting auxiliary materials in continuous casting steel machines, in particular to the covering agent used in the continuous casting steel pouring process. Background technique [0002] In the continuous casting process, the role of the covering agent is to prevent oxidation and to absorb the inclusions of molten steel. The main component of the adsorption is CAO to complete. [0003] Publication (announcement) number: CN103111592A, tundish covering agent, covering agent comprises 40%-50% CaO, 25%-35% Al2O3, 1%-8% MgO, less than 5% SiO2, 1%-10% of CaF2, 1%-5% of Na2O and the balance of unavoidable impurities. In this patent, the MgO content is too low, and the erosion of the tundish coating is prone to occur. Moreover, there is a low-melting-point substance such as CaF2, which is more prone to melting loss of the coating. [0004] Publication (announcement) No. CN103372636A, a double-laye...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/111
CPCB22D11/111
Inventor 赵显久吴杰姜立新唐惠中
Owner BAOSHAN IRON & STEEL CO LTD