Heat transfer carbon ribbon and preparation method thereof

A technology of thermal transfer printing and thermal transfer layer, which is applied in temperature recording method, ink, household utensils, etc. It can solve the problems of harming human health, polluting the environment, and fire hazards in production, transportation and storage, and achieves increased adhesion. , Improve the effect of transfer printing effect

Inactive Publication Date: 2019-10-25
湖南鼎一致远科技发展股份有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The carbon ribbons currently used in the thermal transfer printing industry will release a large amount of toxic organic substances during the preparation process. These substances not only pollute the environment, damage human health, but also pose fire hazards during production, transportation and storage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0018] The preparation method of thermal transfer ribbon comprises the following steps:

[0019] ①Coat the ink layer on one side of the base tape, the coating amount is 1.5~3.5g / m 2 , drying, and enter the next process;

[0020] ② Coat the top coat on the surface of the ink layer, the coating amount is 0.5~0.9g / m 2 , drying, and enter the next process;

[0021] ③ Coat the back coat on the other side of the above-mentioned base tape coated with the ink layer and the top coat, and dry to obtain the carbon tape.

Embodiment 1

[0023] The base tape used in the present invention is a PET film, each layer is coated according to the following steps, and finally a thermal transfer carbon tape is obtained.

[0024] 1) ink layer

[0025] After mixing the raw materials in the following weight ratios, use a coater to coat one side of the above-mentioned base tape at room temperature, and the coating amount is 1.5g / m 2 , drying after coating to form an ink layer, and entering the next process;

[0026] Ink layer composition:

[0027] 15 parts by weight of water-based acrylic resin;

[0028] 6 parts by weight of hydroxyethyl cellulose;

[0029] 10 parts by weight of hyperdispersant;

[0030] 8 parts by weight of leveling agent;

[0031] 10 parts by weight of defoamer;

[0032] 8 parts by weight of carbon black;

[0033] 56 parts by weight of deionized water.

[0034] 2) Top coat

[0035] After mixing the raw materials in the following weight ratios, use a coater to coat the surface of the above-mentio...

Embodiment 2

[0042] The base tape used in the present invention is a PET film, each layer is coated according to the following steps, and finally a thermal transfer carbon tape is obtained.

[0043] 1) ink layer

[0044] After mixing the raw materials in the following weight ratios, use a coater to coat one side of the above-mentioned base tape at room temperature, and the coating amount is 3.5g / m 2 , drying after coating to form an ink layer, and entering the next process;

[0045] Ink layer composition:

[0046] 10 parts by weight of water-based acrylic resin;

[0047] 3 parts by weight of hydroxyethyl cellulose;

[0048] 3 parts by weight of hyperdispersant;

[0049] 5 parts by weight of leveling agent;

[0050] 8 parts by weight of defoamer;

[0051] 6 parts by weight of carbon black;

[0052] 35 parts by weight of deionized water.

[0053] 2) Top coat

[0054] After mixing the raw materials in the following weight ratios, use a coating machine to coat the surface of the ink l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a heat transfer printing carbon ribbon. The heat transfer printing carbon ribbon is composed of a base ribbon, a back coating and a heat transfer layer, wherein the back coatingand the heat transfer layer are coated on the two sides of the base ribbon respectively; the heat transfer layer is divided into two parts, and an ink layer and a surface coating are sequentially arranged on the surface of one side of the base ribbon from inside to outside. The preparation method of the heat transfer printing carbon ribbon comprises the following steps of coating one side of thebase ribbon with the ink layer, wherein the coating amount is 1.5-3.5 g / m<2>, and drying; coating the surface coating on the surface of the ink layer, wherein the coating amount is 0.5-0.9 g / m<2>, anddrying; and coating the back coating on the other surface of the base ribbon coated with the ink layer and the surface coating, and drying to obtain the carbon ribbon. According to the heat transferprinting carbon ribbon and the preparation method thereof, the adhesiveness between the printing ink and a printing material is improved, so that the transfer printing effect is improved, the raw materials adopted in the carbon ribbon formula meet the low-carbon and environmental-friendly concept, and the expansion of the carbon ribbon using field is facilitated.

Description

technical field [0001] The invention relates to the technical field of heat transfer consumables, in particular to a heat transfer carbon ribbon and a preparation method thereof. Background technique [0002] Thermal transfer printing is the process of using heat and pressure to transfer ink from ribbon media to paper or film, transferring the ink to the label as it passes through the printer's printhead and platen. [0003] Thermal transfer printing technology is to use a special carbon ribbon to transfer the toner coating on the carbon ribbon to paper or other types of materials through the working principle similar to the print head of a fax machine. The coating material on the belt can be selected according to the needs to produce strong adhesion, coupled with the selection of printing media, it can ensure that the printed handwriting will not be affected by the outside world. And this heating process, how to heat, can be handed over to the computer to control. At prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B41M5/40C09D11/107C09D11/03
CPCB41M5/40C09D11/03C09D11/107
Inventor 尹玉霞唐国初
Owner 湖南鼎一致远科技发展股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products